A kind of super-concentrated high-solid nano-yellow paste and its preparation method and application

A beige, ultra-concentrated technology, used in additive processing and other directions, can solve the problems of insufficient color paste accuracy, unfavorable fine mold printing and molding, hidden dangers to the health of production operators, etc., to improve the appearance and the safety of operators. Lifting, not easy precipitation effect

Active Publication Date: 2021-12-07
上海彩生色料化学股份有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The color paste used in this light-curing resin is UV color paste, and the precision of this color paste is not high enough, which is not conducive to the printing and molding of fine molds, and the photosensitive color paste needs a photoinitiator, and the production environment requires shielding from sunlight-like wavelengths of light , there are hidden dangers to the health of production operators

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of super-concentrated high-solid nano-yellow paste and its preparation method and application
  • A kind of super-concentrated high-solid nano-yellow paste and its preparation method and application
  • A kind of super-concentrated high-solid nano-yellow paste and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A super-concentrated high-solid nano-yellow slurry, the specific composition of the yellow slurry is shown in Table 1. The super-concentrated high-solid nano-yellow paste is prepared by the following preparation method: the inorganic and organic composite yellow pigments, anti-aging additives, anti-sedimentation additives, dispersants and liquid oil are formulated according to the weight percentage of Example 1 in Table 1. Specific weighing, adding to the container one by one, using a high-speed disperser for mixing and dispersing, the rotating speed is 1500r / min, and the mixing time is 60min. And ball mill dispersion, in which the high-speed shear dispersion cycle is 3 times, and the particle size of the mixture is detected. When the particle size is less than 900nm, the super-concentrated high-solid nano-yellow slurry can be obtained.

[0023] The prepared nano-yellow paste was subjected to a performance test, and the test results are shown in Table 2.

Embodiment 2

[0025] A super-concentrated high-solid nano-yellow slurry, the specific composition of the yellow slurry is shown in Table 1. The super-concentrated high-solid nano-yellow paste is prepared by the following preparation method: the inorganic and organic composite yellow pigments, anti-aging additives, anti-sedimentation additives, dispersants and liquid oil are formulated according to the weight percentage of Example 2 in Table 1. Specific weighing, adding to the container one by one, using a high-speed disperser for mixing and dispersing, the rotating speed is 1400r / min, and the mixing time is 50min. And ball mill dispersion, in which the high-speed shear dispersion cycle is 6 times, and the particle size of the mixture is detected. When the particle size is less than 900nm, the ultra-concentrated high-solid nano-yellow slurry can be obtained.

Embodiment 3

[0027] A super-concentrated high-solid nano-yellow slurry, the specific composition of the yellow slurry is shown in Table 1. The super-concentrated high-solid nano-yellow paste is prepared by the following preparation method: the inorganic and organic composite yellow pigments, anti-aging additives, anti-sedimentation additives, dispersants and liquid oil are formulated according to the weight percentage of Example 2 in Table 1. Specific weighing, adding to the container one by one, using a high-speed disperser for mixing and dispersing, the rotating speed is 1600r / min, and the mixing time is 55min. And ball mill dispersion, in which the high-speed shear dispersion cycle is 5 times, and the particle size of the mixture is detected. When the particle size is less than 900nm, the super-concentrated high-solid nano-yellow slurry can be obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a super-concentrated high-solid nano-yellow paste and its preparation method and application. The yellow paste contains the following components in weight percentage: 40-50% of inorganic and organic mixed yellow pigments, 30-40% of liquid oil, 10-20% dispersant, 0.5-1% anti-aging additive, 0.5-1% anti-sedimentation additive. Compared with the existing technology, the nano-yellow paste has an average particle size of 1 micron and good compatibility with light-curable resins. It can be used for 3D printing of LCD\SLA\DLP, and is used to make high-strength, high-temperature-resistant , waterproof and other industrial materials to ensure that the printed finished product has high color brilliance, is not easy to precipitate, is not affected by light and printing temperature, and has high precision, which is conducive to the development of 3D colored materials. Sunlight production is in line with the economic development trend of energy conservation and environmental protection. It is also beneficial to the company's needs for safety and health protection of production operators.

Description

technical field [0001] The invention relates to the technical field of new material coloring, in particular to a super-concentrated high-solid nano-yellow paste and its preparation method and application. Background technique [0002] 3D printing technology, also known as rapid prototyping technology, referred to as R P or R P M technology (Rapid Prototyping Manufacturing), is a rapid design and prototyping technology developed in the late 1980s. Stereolithography is currently the most precise rapid prototyping technology. It has the advantages of high production efficiency and high material utilization, and can quickly and accurately manufacture complex-shaped objects. Its working principle is: a laser beam with a certain wavelength and intensity scans the light-curing resin point by point according to the shape of each layered section of the model. A solidified thin section, after scanning one layer, the workbench moves a layer-thick distance, so that each layer is scanne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L33/04C08L33/08C08K13/04C08K3/22C08K5/521C08K7/26C08K5/00B33Y70/10
CPCB33Y70/00C08K2003/2241C08L33/04C08L2205/02C08L33/08C08K13/04C08K3/22C08K5/521C08K7/26C08K5/0041
Inventor 虞幸芝
Owner 上海彩生色料化学股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com