Composite high-performance polycarboxylic acid water reducing agent and preparation method and application thereof

A technology of water reducing agent and polycarboxylic acid, applied in the field of concrete, can solve the problems of large hydration heat release, large fluidity loss, poor pumpability, etc., to alleviate the hydration concentration, reduce the peak heat release rate, improve The effect of pumping performance

Active Publication Date: 2019-10-25
GUANGZHOU INSTITUTE OF BUILDING SCIENCE CO LTD
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Based on this, it is necessary to provide a composite high-performance polycarboxylate water reducer for barite concrete, which can improve the fluidity of barite concrete,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite high-performance polycarboxylic acid water reducing agent and preparation method and application thereof
  • Composite high-performance polycarboxylic acid water reducing agent and preparation method and application thereof
  • Composite high-performance polycarboxylic acid water reducing agent and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0042] Example 1

[0043] A composite high-performance polycarboxylic acid water-reducing agent, which is prepared by including the following parts by weight of raw materials:

[0044]

[0045] Among them, the water-reducing polycarboxylic acid water-reducing agent mother liquor is prepared by the following method: 320 parts of methallyl polyoxyethylene ether are dissolved in water as substrate solution I; 40 parts of acrylic acid are dissolved in water to obtain a solution A; Dissolve 2.0 parts of mercaptopropionic acid and 0.8 parts of vitamin C in water to obtain solution B; add hydrogen peroxide to the substrate solution I at 25°C, stir for 10 minutes, and add solution A and solution B dropwise at the same time. The addition process lasts for 2h, after the dripping is completed, keep it for 1~2h, add alkali to adjust the pH to 6~7, it is obtained; the solid content of the mother liquor of the water-reducing polycarboxylic acid water-reducing agent is 37.5wt%, and the solid cont...

Example Embodiment

[0052] Example 2

[0053] A composite high-performance polycarboxylic acid water-reducing agent, which is prepared by including the following parts by weight of raw materials:

[0054]

[0055] Among them, the preparation methods of the mother liquor of the water-reducing polycarboxylic acid water-reducing agent, the viscosity-reducing polycarboxylic acid water-reducing agent mother liquor, the slow-release polycarboxylic acid water-reducing agent mother liquor, and the heat of hydration inhibitor are prepared in accordance with the corresponding raw materials in Example 1. The preparation method is the same.

[0056] The above-mentioned composite high-performance polycarboxylic acid water reducing agent for barite concrete is prepared by the following method:

[0057] Add the mother liquor of the water-reducing polycarboxylic acid water-reducing agent, the viscosity-reducing polycarboxylic acid water-reducing agent mother liquor and the slow-release polycarboxylic acid water-reducing...

Example Embodiment

[0059] Example 3

[0060] A composite high-performance polycarboxylic acid water-reducing agent, which is prepared by including the following parts by weight of raw materials:

[0061]

[0062] Among them, the preparation methods of the mother liquor of the water-reducing polycarboxylic acid water-reducing agent, the viscosity-reducing polycarboxylic acid water-reducing agent mother liquor, the slow-release polycarboxylic acid water-reducing agent mother liquor, and the heat of hydration inhibitor are prepared in accordance with the corresponding raw materials in Example 1. The preparation method is the same.

[0063] The above-mentioned composite high-performance polycarboxylic acid water reducing agent for barite concrete is prepared by the following method:

[0064] Add the mother liquor of the water-reducing polycarboxylic acid water-reducing agent, the viscosity-reducing polycarboxylic acid water-reducing agent mother liquor and the slow-release polycarboxylic acid water-reducing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Solid contentaaaaaaaaaa
Login to view more

Abstract

The invention provides a composite high-performance polycarboxylic acid water reducing agent and a preparation method and application thereof, and relates to the technical field of concrete. The composite high-performance polycarboxylic water reducing agent is prepared from the following raw materials in parts by weight: 15-20 parts of a water-reduced polycarboxylic acid water reducing agent mother liquor, 10-15 parts of a viscosity reduction polycarboxylic acid water reducing agent mother liquor, 20-30 parts of a slow-release polycarboxylic acid water reducing agent mother liquor, 10-15 partsof a hydration heat inhibitor, 2-5 parts of a retarder, 0-0.1 part of a consistency regulator, 0-0.06 part of an air entraining agent and 0-0.05 part of a defoamer. The composite high-performance polycarboxylic acid water reducing agent is applied to barite concrete, the fluidity, pumping performance and stability of the barite concrete can be effectively improved, the heat release rate of hydration is slowed down, and the wall is prevented from cracking.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to a composite high-performance polycarboxylate water reducer and its preparation method and application. Background technique [0002] In places such as scientific research institutes, medical units, and nuclear power plants, equipment such as particle liners and cyclotrons are equipped. These equipments will generate harmful rays and neutron flows during operation. Therefore, when building structures in these places, it is necessary to Concrete with anti-radiation properties is used. Barite has a high density and can effectively absorb radiation and neutron flow, avoiding the harm of radiation to the human body to a certain extent. Barite concrete is widely used in such places. [0003] The existing barite concrete is prone to some problems during use, such as: [0004] Barite concrete has high water absorption and high brittleness. During the mixing process, the barite aggrega...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B24/42C04B24/34C04B24/32C04B28/02C04B103/30
CPCC04B28/02C04B40/0039C04B2103/302C04B2201/20C04B2201/50C04B24/42C04B24/20C04B24/383C04B22/0013C04B24/32C04B24/04C04B24/16C04B24/06C04B22/068C04B24/283C04B24/045C04B24/38C04B24/34C04B24/10C04B24/00C04B14/368
Inventor 张金龙陈小龙钟开红孙申美邵强吴英哲
Owner GUANGZHOU INSTITUTE OF BUILDING SCIENCE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap