A silicon molecular sieve and molecular sieve technology, applied in the field of molecular sieves, can solve the problems of limited application and poor catalytic performance, and achieve the effect of good catalytic effect and modulation selectivity.

Active Publication Date: 2021-05-18
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although the prior art can prepare vanadium-silicon molecular sieves, its catalytic performance is poor, which limits its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified vanadium silicon molecular sieve, its preparation method and application, and sulfide oxidation method
  • Modified vanadium silicon molecular sieve, its preparation method and application, and sulfide oxidation method
  • Modified vanadium silicon molecular sieve, its preparation method and application, and sulfide oxidation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0030] According to a preferred embodiment of the present invention, B=i×nV, wherein, 0960 / I 800 The ratio B is positively correlated.

[0031] According to the molecular sieve of the present invention, preferably the molecular sieve satisfies T w / T k =D, 0.2w is the pore volume of the molecular sieve, T k is the total pore volume of the molecular sieve.

[0032] According to the molecular sieve of the present invention, preferably, the molar ratio of silicon element: vanadium element is 100: (0.1-10), more preferably silicon element: the molar ratio of vanadium element is 100: (0.2-5), further preferably silicon element: The molar ratio of the vanadium element is 100:(0.5-4), most preferably 100:(1-4).

[0033] According to the modified vanadium-silicon molecular sieve of the present invention, preferably, the surface silicon-vanadium ratio of the molecular sieve is not lower than the bulk silicon-vanadium ratio, and the silicon-vanadium ratio refers to the molar ratio of...

Embodiment 1

[0102] This example illustrates the methods and products provided by the invention.

[0103]At normal temperature (20°C, the rest of the comparative examples are the same as the examples) and normal pressure (0.1MPa, the rest of the comparative examples are the same as the examples), first mix the vanadium silicon molecular sieve with 1mol / L aqueous hydrochloric acid for beating, and then mix the mixed slurry in Mix and stir at 80°C for 12 hours; after solid-liquid separation, mix the solid, vanadium source ammonium metavanadate, organosilicon source tetraethyl orthosilicate and sodium hydroxide aqueous solution (pH 12), and treat tetraethyl orthosilicate After hydrolysis (the hydrolysis rate of the organic silicon source is 40%), the mixture is transferred to a stainless steel sealed reactor, and treated at 170° C. for 12 hours, wherein the vanadium silicon molecular sieve: vanadium source: organic silicon source: acid: alkali: the molar ratio of water is 100:0.5:2:10:5:250, ...

Embodiment 2

[0105] This example illustrates the methods and products provided by the invention.

[0106] At normal temperature and pressure, first mix the vanadium silicon molecular sieve with 5mol / L hydrochloric acid solution for beating, then mix and stir the mixed slurry at 60°C for 1 hour; The source methyl orthosilicate is mixed with tetrapropylammonium hydroxide aqueous solution (pH is 10), and after the methyl orthosilicate is hydrolyzed (organosilicon source hydrolysis rate is 50%), the mixture is transferred to a stainless steel sealed reaction kettle, and the Treat at ℃ for 12 hours, wherein, vanadium silicon molecular sieve: vanadium source: organosilicon source: acid: alkali: water molar ratio is 100:1:1:15:15:200, vanadium silicon molecular sieve and organosilicon source are SiO 2 In terms of acid, H + In terms of base, in N. Then the product was recovered according to the method of Example 1 to obtain the modified vanadium silicon molecular sieve S-2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The present invention involves the field of molecular screens, and a modified 钒 silicon molecular sieve and its preparation methods and applications, as well as sulfation oxidation methods, this molecular sieve includes: 钒 elements, silicon elements, and oxygen elements, which meets X to meet X 1‑1.8 / X 0.4‑0.9 = C, 0.3 <c <0.9, x 0.4‑0.9 It is the proportion of micro -hole diameter in the range of molecular sieves in the range of 0.4筛0.9nm. 1‑1.8 It is the proportion of micro -hole diameter in the range of a molecular sieve in the range of micropores in the range of 181.8nm.This method includes: mixing silicon molecules with acid solution to obtain a mixture A, the first thermal treatment, and the first solid; mix the first solid, the source, the sources of the alkali, and the waterHot treatment.The modified sirrillary sieve provided by the present invention has a special materialized characteristic structure and is used to oxidize the sulfur ether oxidation, which is conducive to the selectivity of the target product.

Description

technical field [0001] The invention relates to the field of molecular sieves, in particular to a modified vanadium-silicon molecular sieve, a preparation method of the modified vanadium-silicon molecular sieve, an application of the modified vanadium-silicon molecular sieve in sulfide oxidation reaction and a sulfide oxidation method. Background technique [0002] Vanadium-silicon molecular sieve is a molecular sieve whose skeleton is composed of silicon, vanadium and oxygen. Vanadium-silicon molecular sieves have broad application prospects in petroleum refining and petrochemical industry. [0003] CN1500729A discloses a kind of preparation method of vanadium silicon molecular sieve, vanadium silicon molecular sieve has following general formula: (SiO 4 )n·(VO 4 )m, n / m is 30-200, it uses ammonium vanadate as the vanadium source, silica sol as the silicon source, tetraethylammonium hydroxide or tetrapropylammonium hydroxide as the template, wherein each of the molecular ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B39/08B82Y30/00B82Y40/00B01J29/04C07C315/02C07C317/04
CPCB01J29/04B82Y30/00B82Y40/00C01B39/08C01P2006/14C01P2006/17C07C315/02C07C317/04
Inventor 史春风林民朱斌
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com