Production process of aluminum alloy medium plate

A production process and technology of aluminum alloy, applied in the field of metal processing, can solve the problems affecting the surface performance and service life of aluminum alloy sheets, and achieve the effect of improving surface performance and service life

Inactive Publication Date: 2019-11-05
任万坤
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After testing, the residual stress on the surface of the aluminum alloy plate after the first heat treatment process is -147Mpa ± 10Mpa, and the residual stress on the surface of the aluminum alloy plate after the latter heat treatment process is -84Mpa ± 10Mpa. Effectively reduce the surface residual stress left by aluminum alloy during mechanical processing, which greatly affects the surface properties and service life of aluminum alloy sheets, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A production process of aluminum alloy plate, comprising the steps of:

[0024] a. Put metal materials and auxiliary materials into the heating device to melt and temper, and the furnace temperature is 1300-1600K;

[0025] b. Pour the molten metal obtained in step a into the mold, and obtain a plate-shaped metal part blank after solidification;

[0026] c. cutting the metal part blank obtained in step b into regular plate metal parts;

[0027] d. Carry out surface milling to the shape metal part that c step gains, obtain the flat plate metal part of surface;

[0028] e. Put the plate metal part obtained in step d into a heating device, heat it above the recrystallization temperature, and perform hot rolling.

[0029] Wherein, the first quenching medium in the heat treatment is water, and when the water temperature reaches 70-80° C., PDA quenching liquid is added, and the solubility of the PDA quenching liquid is 2%-20%.

[0030] Among them, the second quenching in he...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of metal processing, in particular to a production process of an aluminum alloy medium plate. The production process comprises the following steps that a, a metal material and an auxiliary material are put into a heating device for melting and hardening and tempering, and the furnace temperature is 1300-1600K; b, molten metal obtained in the step a is poured intoa casting mold, and solidifying is conducted to obtain a plate-shaped metal part blank; c, the metal part blank obtained in the step b is cut into a regular plate-shaped metal part; d, the metal partobtained in the step c is milled to obtain a plate-shaped metal part with a flat surface; and e, the plate-shaped metal part obtained in the step d is put into a heating device, heating is conductedto the recrystallization temperature or above, and hot rolling is conducted.

Description

technical field [0001] The invention relates to the field of metal processing, in particular to a production process of an aluminum alloy medium-thick plate. Background technique [0002] At present, there are two main heat treatment processes for aluminum alloy plates: one is quenching + leveling + aging, and the other is quenching + leveling + cold rolling 10% + multiple leveling + aging. After testing, the residual stress on the surface of the aluminum alloy plate after the first heat treatment process is -147Mpa ± 10Mpa, and the residual stress on the surface of the aluminum alloy plate after the latter heat treatment process is -84Mpa ± 10Mpa. Effectively reduce the surface residual stress left by the aluminum alloy during machining, which greatly affects the surface properties and service life of the aluminum alloy sheet. Contents of the invention [0003] The purpose of the present invention is to overcome the shortcomings of the above-mentioned prior art, and prov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22F1/04B21C37/02C22C1/02
CPCB21C37/02C22C1/026C22F1/002C22F1/04
Inventor 任万坤
Owner 任万坤
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap