Preparation method of super-hydrophobic coating

A super-hydrophobic coating, ionized water technology, applied in the coating, the device for coating liquid on the surface, the pretreatment surface, etc. Cracks or fractures, etc., to achieve the effect of increasing hydrophobicity, stable coating quality, and reducing the amount of side erosion

Active Publication Date: 2019-11-12
QINGDAO TECHNOLOGICAL UNIVERSITY
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the final analysis, the etching process is an operation that damages the surface of the substrate, especially for thin-layer aluminum alloy substrates, the mechanical properties will be greatly affected during the etching process, and even lead to cracks or breakage of the substrate. The rate is low, and the micro-nano morphology of the surface of the copper sheet is simple in the existing etching method, so that the hydrophobic effect of the prepared hydrophobic coating is poor, and the wear resistance and bending resistance are poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of super-hydrophobic coating
  • Preparation method of super-hydrophobic coating
  • Preparation method of super-hydrophobic coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A kind of preparation method of superhydrophobic coating of the present embodiment, described method comprises the steps:

[0041] (1) Substrate pretreatment: select a circular copper sheet with a diameter of 1 cm and a thickness of 0.2 mm, and polish and derust the surface of the copper sheet sequentially through 400 mesh, 600 mesh, 1000 mesh, 1500 mesh, and 2000 mesh sandpaper, and then Use acetone, ethanol, and deionized water to ultrasonically clean surface oil stains and other impurities, and dry them for later use;

[0042](2) Copper sheet etching: first copper sheet is immersed in the mixed solution of sodium chloride and hydrochloric acid 4h, and the mixed solution of sodium chloride and hydrochloric acid is the sodium chloride aqueous solution that concentration is 1mol / L and mass fraction is 10% hydrochloric acid The solutions are mixed in equal volumes, cleaned with deionized water, dried, and then immersed in the mixed solution of hydrogen peroxide and hydro...

Embodiment 2

[0045] A kind of preparation method of superhydrophobic coating of the present embodiment, described method comprises the steps:

[0046] (1) Substrate pretreatment: select a circular copper sheet with a diameter of 1 cm and a thickness of 0.2 mm, and polish and derust the surface of the copper sheet sequentially through 400 mesh, 600 mesh, 1000 mesh, 1500 mesh, and 2000 mesh sandpaper, and then Use acetone, ethanol, and deionized water to ultrasonically clean surface oil stains and other impurities, and dry them for later use;

[0047] (2) Copper sheet etching: earlier copper sheet is immersed in the mixed solution of sodium chloride and hydrochloric acid 6h, and the mixed solution of sodium chloride and hydrochloric acid is the sodium chloride aqueous solution that concentration is 1.5mol / L and mass fraction is 15% Hydrochloric acid solution is mixed in equal volumes, cleaned with deionized water, dried, and then immersed in a mixed solution of hydrogen peroxide and hydrochl...

Embodiment 3

[0050] A kind of preparation method of superhydrophobic coating of the present embodiment, described method comprises the steps:

[0051] (1) Substrate pretreatment: select a circular copper sheet with a diameter of 1 cm and a thickness of 0.2 mm, and polish and derust the surface of the copper sheet sequentially through 400 mesh, 600 mesh, 1000 mesh, 1500 mesh, and 2000 mesh sandpaper, and then Use acetone, ethanol, and deionized water to ultrasonically clean surface oil stains and other impurities, and dry them for later use;

[0052] (2) Copper sheet etching: first copper sheet is immersed in the mixed solution of sodium chloride and hydrochloric acid 8h, and the mixed solution of sodium chloride and hydrochloric acid is the sodium chloride aqueous solution that concentration is 2mol / L and mass fraction is 20% hydrochloric acid The solution is mixed in equal volumes, dried, and then immersed in the mixed solution of hydrogen peroxide and hydrochloric acid for 10 hours. The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a super-hydrophobic coating. According to the etching method, three different steeping liquors are correspondingly used for steeping for some time, inthis way, the etching rate is increased by using the different steeping liquors for steeping, the etching rate is increased by adopting the specific steeping liquor proportion, the side etching amountand bulges are reduced by increasing the etching rate, the micro-nano shape formed on the surface of a copper sheet is more complicated, and the hydrophobicity, the friction resistance and the fracture resistance of the super-hydrophobic coating are improved. Fluoroalkyl silane and silane with the boiling points being similar are selected to be better deposited on the surface of matrix copper etched well, so that the coating has the very low surface energy, the quality of the coating is relatively stable, the good hydrophobic effect is reached, the corrosion resistance and cleanness of the copper are better, and the service life is longer.

Description

technical field [0001] The invention belongs to the technical field of superhydrophobic materials, and in particular relates to a preparation method of a superhydrophobic coating. Background technique [0002] Because of its thermal conductivity, electrical conductivity, corrosion resistance and processing properties, copper has important applications in various industries such as electric power, marine and military industries. For example, most of the condensers in the power industry, the heat exchange devices of low-pressure heating and oil coolers, and the hollow wires of water-cooled generators are made of copper alloy materials; in the marine military industry, in the water piping systems of military warships such as aircraft carriers Most of them are some copper materials; civil medical equipment, industrial utensils, telecommunications industry parts, etc. have copper applications. However, the application of copper has been limited due to the serious corrosion probl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B05D1/00B05D3/02B05D5/00C23F1/18
CPCB05D1/60B05D3/0254B05D5/00C23F1/18
Inventor 郭思瑶罗惠华陈际洲乔晓立张素磊谭哲
Owner QINGDAO TECHNOLOGICAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap