A kind of anti-xenon lamp test polarizer and preparation method thereof

A technology for polarizers and manufacturing methods, applied in weather resistance/light resistance/corrosion resistance, optics, measuring devices, etc., can solve problems such as yellowing, achieve the effect of avoiding yellowing and improving xenon lamp test performance

Active Publication Date: 2021-07-13
佛山纬达光电材料股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, traditional polarizers, especially iodine-based polarizers, are prone to yellowing problems in the xenon lamp test

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-xenon lamp test polarizer and preparation method thereof
  • A kind of anti-xenon lamp test polarizer and preparation method thereof
  • A kind of anti-xenon lamp test polarizer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] like figure 1 As shown, a xenon lamp test polarizer includes a protective film 1, a polarizing original plate 2, a pressure-sensitive adhesive layer 3 and a release film 4 bonded together from top to bottom, and the dye-based polarizing original plate 2 consists of The first layer of cellulose triacetate film layer 2-1, the dye-based polarizer 2-2 and the second layer of cellulose triacetate film layer 2-3 bonded together from top to bottom in sequence.

[0035] Wherein, the first cellulose triacetate film layer 2-1 adopts a cellulose triacetate film layer with anti-ultraviolet performance, and the anti-ultraviolet performance means that the transmittance of the full light spectrum at 380nm is 0-5 %.

[0036] The dye-based polarizer 2-2 is formed by swelling, dipping, stretching, color correction and drying of polyvinyl alcohol film, and the dipping liquid is a dichroic dye liquid. The dye-based polarizer 2-2 is bonded with the upper and lower layers of cellulose tria...

Embodiment 2

[0057] A xenon lamp test polarizer, the structure of which is basically the same as that of Example 1, the difference lies in: the hue bs value of the dye-based polarizer original plate 2 is 3.

Embodiment 3

[0059] A xenon lamp test polarizer, the structure of which is basically the same as that of Example 1, the difference lies in: the hue bs value of the dye-based polarizer original plate 2 is -5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
phaseaaaaaaaaaa
Login to View More

Abstract

The invention discloses a xenon lamp resistant test polarizer, which comprises a protective film, a polarizing original plate, a pressure-sensitive adhesive layer and a release film bonded together. An anti-ultraviolet film layer, a dye-based polarizer and a cellulose triacetate film layer, the hue value of the dye-based polarizer plate is between -5 and 5. The invention can effectively improve the xenon lamp test performance of the polarizer, and avoid the yellowing phenomenon after the xenon lamp test. The invention also provides a preparation method of the xenon lamp resistance test polarizer.

Description

technical field [0001] The invention relates to the technical field of polarizer preparation, in particular to a xenon lamp resistance test polarizer and a preparation method thereof. Background technique [0002] Polarizers are an essential part of liquid crystal displays. Common polarizers include iodine-based polarizers and dye-based polarizers. Among them, the iodine-based polarizer has poor heat resistance and moisture resistance, which cannot meet the application of the new generation of liquid crystal display technology in various occasions, especially the use of outdoor instruments and the automotive industry; while the dye-based polarizer has excellent moisture resistance. Good performance and heat resistance, which can well meet the needs of new trends. [0003] When dye-based polarizers are used in displays and instruments that need to work outdoors for a long time, such as instrument displays, rearview mirror displays, sunroofs, and heat insulation films in the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G02B1/04
CPCG01N17/004G02B5/305G02B1/14
Inventor 周文贤
Owner 佛山纬达光电材料股份有限公司