White-cooper alloy with light-weight characteristics used for Tibetan area buddha casting and process of white-cooper alloy

A Bai Lima, lightweight technology, applied in the field of alloys, can solve problems such as lack of progress, achieve the effect of facilitating transportation and layout, reducing usage, and maintaining low density

Inactive Publication Date: 2019-11-22
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The development and industrialization of Lima alloy with advanced performance is an unavoidable problem in the religious field of Tibet. For a long time, many domestic research institutions and enterprises have made multi-faceted attempts, but unfortunately, no substantial progress has been made so far. Progress

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A Bailima alloy for casting Buddha statues in Tibetan areas with lightweight characteristics and its technology. In terms of weight percentage, the composition of the alloy is Li: 1.5wt.%, Mg: 8.0wt.%, Sc: 0.2wt.%, Bi: 5.0wt.%, Ni: 5.0wt.%, Al: 20.0wt.% , Au: 2.0wt.%, Ag: 8.0wt.%, and the balance is copper. The above-mentioned Bailima alloy and its process for casting Buddha statues in Tibetan areas with lightweight features include the following steps: adding the raw materials in the above ratio into an induction furnace under an argon environment, and using a graphite crucible; melting at 1200 The temperature is kept at 1200°C for 10 minutes, and it is evenly stirred by high-frequency induction furnace electromagnetically; after stirring evenly, it is kept at 1200°C for 1 minute and cast out of the furnace; the alloy casting adopts a steel mold with a diameter of 20-30mm, and the temperature is cooled by water cooling. The obtained ingot is heated to 850-950 degrees ...

Embodiment 2

[0023] A Bailima alloy for casting Buddha statues in Tibetan areas with lightweight characteristics and its technology. In terms of weight percentage, the composition of the alloy is Li: 3.0wt.%, Mg: 12.0wt.%, Sc: 0.4wt.%, Bi: 6.0wt.%, Ni: 8.0wt.%, Al: 28.0wt.% , Au: 3.0wt.%, Ag: 10.0wt.%, and the balance is copper. The above-mentioned Bailima alloy and its process for casting Buddha statues in Tibetan areas with lightweight features include the following steps: adding the raw materials in the above ratio into an induction furnace under an argon environment, and using a graphite crucible; melting at 1200 The temperature is kept at 1200°C for 10 minutes, and it is evenly stirred by high-frequency induction furnace electromagnetically; after stirring evenly, it is kept at 1200°C for 1 minute and cast out of the furnace; the alloy casting adopts a steel mold with a diameter of 20-30mm, and the temperature is cooled by water cooling. The obtained ingot is heated to 850-950 degree...

Embodiment 3

[0026] A Bailima alloy for casting Buddha statues in Tibetan areas with lightweight characteristics and its technology. In terms of weight percentage, the composition of the alloy is Li: 1.8wt.%, Mg: 9.0wt.%, Sc: 0.3wt.%, Bi: 5.2wt.%, Ni: 5.4wt.%, Al: 24.0wt.% , Au: 2.5wt.%, Ag: 9.0wt.%, and the balance is copper. The above-mentioned Bailima alloy and its process for casting Buddha statues in Tibetan areas with lightweight features include the following steps: adding the raw materials in the above ratio into an induction furnace under an argon environment, and using a graphite crucible; melting at 1200 The temperature is kept at 1200°C for 10 minutes, and it is evenly stirred by high-frequency induction furnace electromagnetically; after stirring evenly, it is kept at 1200°C for 1 minute and cast out of the furnace; the alloy casting adopts a steel mold with a diameter of 20-30mm, and the temperature is cooled by water cooling. The obtained ingot is heated to 850-950 degrees ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a white-cooper alloy with light-weight characteristics used for Tibetan area buddha casting and a process of the white-cooper alloy. The alloy comprises the following components of, in percentage by weight, 1.5 wt.%-3.0 wt.% of Li, 8.0 wt.%-12.0 wt.% of Mg, 0.2 wt.%-0.4 wt.% of Sc, 5.0 wt.%-6.0 wt.% of Bi, 5.0 wt.%-8.0 wt.% of Ni, 20.0 wt.%-28.0 wt.% of Al, 2.0 wt.%-3.0 wt.% of Au, 8.0 wt.%-10.0 wt.% of Ag and the balance copper. The material provides a light-weight solution for the white-cooper alloy used for Tibetan area buddha casting, and the appearance of the obtained product has a white impression. The implementation and industrialization of the material can effectively promote the updating and industry upgrading requirements of new materials in the religiousdecoration industry in China.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a copper alloy. Background technique [0002] Tibetan Buddhism was formed in the 10th century AD, and the existence of bronze Buddha statues in Tibetan religious activities can be traced back to the era when Buddhism was first introduced in the Tubo Dynasty. In the history of Tibetan Buddhism that has lasted for more than a thousand years, countless Buddha statues have been enshrined in monasteries and families as carriers of faith. As a form of artistic expression, bronze Buddha statues occupy a prominent position in the religious culture of Tibetan Buddhism and represent the highest achievements of Tibetan art and traditional skills. These cultural treasures embody the superb casting skills and splendid culture in ancient my country. [0003] There are two traditional copper Buddha casting methods in Tibet: lost wax casting and sand mold casting. The dimensions of the bronze ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C30/02C22C9/01C22C1/02C22F1/02C22F1/08
CPCC22C1/02C22C9/01C22C30/02C22F1/02C22F1/08
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap