UV-CTP photosensitive adhesive and preparation and testing method thereof

A UV-CTP, photosensitive adhesive technology, applied in the photosensitive adhesive field, can solve the problems of insufficient alkali resistance and solvent resistance, damage to the photosensitive film layer, etc., and achieve excellent alcohol resistance, high printing resistance, and wide developing latitude. Effect

Inactive Publication Date: 2019-12-03
河北金锐美科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing UV-CTP photosensitive adhesive has insufficient anti-alkali and anti-solvent ability, resulting in damage to the photosensitive film layer that constitutes the pattern and dots

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0065] The second aspect of the present invention provides a preparation method of UV-CTP photosensitive glue, which includes the following steps: adding the above components into the solvent in sequence according to the formula, stirring for 10-20 hours, and filtering after complete dissolution to obtain the photosensitive glue.

[0066] In the present invention, the solvent can be selected from one of methyl ethyl ketone, butyrolactone, ethylene glycol ethyl ether, ethylene glycol monoethyl ether, ethylene glycol monomethyl ether, butyl acetate, dioxane, tetrahydrofuran, butanone one or more combinations.

[0067] Preferably, the solvent is a mixed solvent of butyrolactone, ethylene glycol ether, butanone, and dioxane.

[0068] As more preferably, the volume ratio of butyrolactone, ethylene glycol ethyl ether and butanone in the mixed solvent is (0-10%):(20%-90%):(0-60%).

[0069] As most preferably, the volume ratio of butyrolactone, ethylene glycol ethyl ether and butanon...

Embodiment 1

[0093] Embodiment 1 provides a kind of UV-CTP photosensitive adhesive, by mass fraction, at least includes the following components, coloring dye 2%, photosensitizer 20%, film-forming resin 45%, alcohol-resistant resin 25%, solvent resistance 3% , Monofunctional anhydride 5%.

[0094] The colored dye is crystal violet; the sensitizer is 2,1,4-diazonaphthoquinone sulfonate, purchased from Shanghai Dajin Photosensitive Material Co., Ltd., the model is NAC-4; the film-forming resin is plastic Phenolic resin, purchased from Benxi Ruishida Chemical Co., Ltd., model is BX-30; the capacitance resistance agent is triphenyl phosphate; the monofunctional anhydride is tetrahydrophthalic anhydride.

[0095] The alcohol-resistant resin, in parts by mass, includes the following components: 30 parts of (meth)acrylate, 25 parts of acrylonitrile, 10 parts of styrene, 50 parts of acrylamide, N-[4-(sulfonamide)benzene base] 80 parts of acrylamide; the preparation method of the alcohol-resistant...

Embodiment 2

[0101] Embodiment 2 provides a kind of UV-CTP photosensitive adhesive, in terms of mass fraction, at least includes the following components, coloring dye 0.5%, photosensitizer 30%, film-forming resin 50%, alcohol-resistant resin 16%, solvent resistance 1.5% , Monofunctional anhydride 2%.

[0102] The preparation method and testing method of the UV-CTP photosensitive glue are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Sensitivityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of photosensitive adhesives, and in particular relates to a UV-CTP photosensitive adhesive and a preparation method thereof. The UV-CTP photosensitive adhesive comprises, by mass, at least 0.1 to 4% of coloring dye, 5 to 40% of photosensitizer, 30 to 60% of film-forming resin, 5 to 40% of alcohol-resistant resin, 0.1 to 5% of anti-solvent, and 1 to 8% of monofunctional acid anhydride. The photosensitive adhesive has the advantages of excellent alcohol resistance and high print resistance, and can reach 200,000 prints. At the same time, the photosensitive adhesive prepared by the invention has large latitude, is suitable for 1: 2 to 1: 7 dilution of the Huaguang PD-type positive picture PS version developing solution, and can be used for both strong development and weak development. At present, many photosensitive adhesives on the market can only adapt to strong development or only weak development, and the development latitude is very limited.

Description

technical field [0001] The invention relates to the technical field of photosensitive glue, in particular to a UV-CTP photosensitive glue and a preparation and testing method thereof. [0002] technical background [0003] The digitalization of printing plate making is the general trend of the printing plate making industry at present, thus giving birth to a large number of new technologies of computer-to-plate making. UV-CTP system technology is one of them. Computer to Plate (CTP for short) refers to the process of directly outputting graphics and text to the printing plate through the computer, mainly refers to the off-line direct plate making process. CTP technology converts digital pages directly into printing plates, eliminating the need for traditional prepress procedures and corresponding equipment such as laser phototypesetting photosensitive film or electronic color separation film imposition, printing, and PS plate washing. It not only simplifies the production p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G03F7/004G03F7/016G01N21/84
CPCG01N21/84G03F7/004G03F7/0163G03F7/0166
Inventor 郑卫平陈有才刘凯王丽娟
Owner 河北金锐美科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap