Preparation method of alcohol resisting type polyarylether electrolyte film material

An electrolyte membrane material, polyarylether technology, applied in fuel cell parts, circuits, electrical components, etc., can solve problems such as poor alcohol resistance, achieve excellent film formation, simple synthesis method, and promote proton conduction Effect

Inactive Publication Date: 2018-08-31
CHANGZHOU DAAO NEW MATERIAL TECH CO LTD
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Technical problem to be solved by the present invention: Aiming at the problem of poor alcohol resistance of existing electrolyte membrane materials, a method for preparing an alcohol-resistance type polyarylether electrolyte membrane material is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of alcohol resisting type polyarylether electrolyte film material

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0017] Take the collagen and put it in a pulverizer to pulverize it, collect the pulverized material and mix it with deionized material with stirring at a mass ratio of 1:10, and adjust the pH to 8.0 with a mass fraction of 1% ammonia solution to obtain a modified solution and press 50U / g, add neutral protease to the modified solution, then hydrolyze at 35°C for 3h, filter and collect the filtrate to obtain hydrolyzed collagen solution; weigh 45 parts of hydrolyzed collagen solution, 10 parts of polyvinyl alcohol, 3 parts of glutaraldehyde, 1 part of 1% hydrochloric acid and 55 parts of 120# solvent oil were placed in a three-necked flask, heated in a water bath at 75°C for 3 hours, allowed to stand and cooled to room temperature, filtered and collected the filtrate , after washing 3 times with acetone, the modified cross-linked particles were obtained; in parts by weight, 45 parts of dimethyl sulfoxide, 10 parts of epichlorohydrin, 3 parts of 1% sodium hydroxide solution and 1...

example 2

[0019]Take the collagen and put it in a pulverizer to pulverize it, collect the pulverized material and mix it with deionized material with stirring at a mass ratio of 1:10, and adjust the pH to 8.0 with a mass fraction of 1% ammonia solution to obtain a modified solution and press 50U / g, add neutral protease to the modified liquid, then hydrolyze at 36°C for 4h, filter and collect the filtrate to obtain hydrolyzed collagen liquid; weigh 47 parts of hydrolyzed collagen liquid, 12 parts of polyvinyl alcohol, 4 parts of glutaraldehyde, 2 parts of 1% hydrochloric acid and 57 parts of 120# solvent oil were placed in a three-necked flask, heated in a water bath at 77°C for 4 hours, left to cool to room temperature, filtered and collected the filtrate , after washing with acetone for 4 times, the modified cross-linked particles were obtained; in parts by weight, 47 parts of dimethyl sulfoxide, 12 parts of epichlorohydrin, 4 parts of 1% sodium hydroxide solution and 12 parts of mass f...

example 3

[0021] Take the collagen and put it in a pulverizer to pulverize it, collect the pulverized material and mix it with deionized material with stirring at a mass ratio of 1:10, and adjust the pH to 8.0 with a mass fraction of 1% ammonia solution to obtain a modified solution and press 50U / g, add neutral protease to the modified solution, then hydrolyze at 37°C for 5h, filter and collect the filtrate to obtain hydrolyzed collagen solution; weigh 50 parts of hydrolyzed collagen solution, 15 parts of polyvinyl alcohol, 5 parts of glutaraldehyde, 2 parts of 1% hydrochloric acid and 65 parts of 120# solvent oil were placed in a three-necked flask, heated in a water bath at 80°C for 5 hours, left to cool to room temperature, filtered and collected the filtrate , after washing 5 times with acetone, the modified cross-linked particles were obtained; in parts by weight, 50 parts of dimethyl sulfoxide, 15 parts of epichlorohydrin, 5 parts of 1% sodium hydroxide solution and 15 parts of mas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of an alcohol resisting type polyarylether electrolyte film material, and belongs to the technical field of an electrolytic film material. Collagen and polyvinyl alcohol are mixed to be subjected to hydrolysis to form amino acid to be grafted to the surface of a polyvinyl alcohol material; by virtue of amino modification of polyvinyl alcohol and sulfonic acid group modification processing, a macromolecule crosslinking agent with the sulfonic acid group is introduced; next, through thermal treatment, the sulfonic acid group and amino are subjected to a cross-linking reaction to prepare an amino-containing sulfonated polyarylether ketone sulfone/sulfonated polyvinyl alcohol crosslinking film; sulfonated polyvinyl alcohol has high alcohol resisting performance, and meanwhile, the sulfonic acid group and amino can exist in an acid alkali pair form by virtue of an acid alkali effect therebetween, so that proton transmission sites are provided for protons and proton conduction is promoted; and in addition, by virtue of the formed crosslinking network structure, permeation of methyl alcohol can be suppressed effectively, and the prepared electrolyte film material can be excellent in compact structure.

Description

technical field [0001] The invention relates to a method for preparing an alcohol-resisting polyarylether electrolyte membrane material, and belongs to the technical field of electrolytic membrane materials. Background technique [0002] For fuel cells that use polymer membranes as electrolytes to transmit ions and isolate fuels and oxidants, the core component is the polymer electrolyte membrane. Polymer electrolyte membrane materials can be roughly divided into two categories: proton exchange membrane, PEM) and anion exchange membrane. The important role of this membrane is reflected in the fact that its comprehensive performance directly affects the various efficiency and performance indicators of the fuel cell. As the core component of the fuel cell, it plays a very important role. It not only has excellent ability to block fuel and oxidant, but also has good ion conductivity, so that the fuel cell can work normally. Then the polymer electrolyte membrane material with ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M8/02H01M2/16H01M50/409
CPCH01M8/02H01M50/409Y02E60/50Y02E60/10
Inventor 董发勇蒋益
Owner CHANGZHOU DAAO NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap