A preparation method of large-scale reaction sintered silicon carbide ceramic plate

A technology for sintering silicon carbide and silicon carbide ceramics, which is applied in the field of preparation of large-size reactive silicon carbide ceramic plates, can solve the problems of press size limitation, large production investment, and silicon carbide ceramic plates not being mass-produced. Effect of cracking and damage reduction

Active Publication Date: 2022-04-26
SHAANXI UDC MATERIALS TECH CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, large-scale (3500*500*10~30mm) silicon carbide ceramic plates (including hollow plates) have not been mass-produced and encountered many difficulties
[0003] 1. Selection of molding method: 1) Dry pressing molding has relatively limited size of the press, especially its high pressure requirements, so its production investment is too large, the pass rate is low, and because of its molding method, it cannot be manufactured. Silicon hollow sheet
2) Grouting molding: the uniformity is difficult to guarantee, and the density of the same section varies greatly during the drying process
3) Extrusion molding: It has no limitation on the size in the length direction, but it will cause a large number of tiny cracks due to excessive length shrinkage during the shrinkage process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of large-scale reaction sintered silicon carbide ceramic plate
  • A preparation method of large-scale reaction sintered silicon carbide ceramic plate
  • A preparation method of large-scale reaction sintered silicon carbide ceramic plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] The present invention will be described in detail below in conjunction with the accompanying drawings and specific embodiments. The large size in the present invention is 3100*500*10mm in length×width×height.

[0030] 1) Ingredients, according to the ratio of parts by mass, weigh 60-85 parts of silicon carbide, 5-10 parts of graphite powder, 2-5 parts of carbon black and 2-4 parts of additives, stir well and add 5-15 parts Continue to stir for more than 4 hours with a portion of water, and then stale for 24-72 hours to obtain mud.

[0031] Wherein, the auxiliary agent is PAM (polyacrylamide), PVA (polyvinyl alcohol), PVP (polyvinylpyrrolidone) or CMC (carboxymethylcellulose).

[0032] 2) Extrude the mud with an extruder after smelting, and set a duckbill die 6 at the outlet of the extruder, see figure 1 In Figures (a), (b) and (c), the duckbill die 6 includes a cylinder with two openings, one end of the cylinder is rectangular, and the other end is circular, and the d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

A method for preparing a large-size reaction-sintered silicon carbide ceramic plate. According to the ratio of parts by mass, 60-85 parts of silicon carbide, 5-10 parts of graphite powder, 2-5 parts of carbon black and 2-4 parts of Auxiliary, after stirring evenly, add 5-15 parts of water to continue stirring evenly, and then stale to obtain mud material; after the mud material is smelted, it is extruded by an extruder to obtain a green billet; after drying, it is sintered to obtain silicon carbide ceramics sheet. Adopting the standing furnace charging method can effectively reduce a large number of cracks, and overcome the shrinkage cracks in the prior art during drying. The invention can prepare large-scale silicon carbide ceramic plates in large batches, and overcomes the problems in the processes of forming, drying and sintering in the prior art while ensuring the flatness thereof.

Description

technical field [0001] The invention belongs to the technical field of silicon carbide ceramic materials, and relates to a method for preparing a large-size reactive silicon carbide ceramic plate. Background technique [0002] With the continuous expansion of the application of silicon carbide ceramics, there are more and more requirements for the quality and size of silicon carbide ceramics. Among them, large-scale (3500*500*10-30mm) silicon carbide ceramic plates (including hollow plates) have not been mass-produced and have encountered many difficulties. [0003] 1. Selection of molding method: 1) Dry pressing molding has relatively limited size of the press, especially its high pressure requirements, so its production investment is too large, the pass rate is low, and because of its molding method, it cannot be manufactured. Silicon hollow sheet. 2) Grouting molding: the uniformity is difficult to guarantee, and the density of the same section varies greatly during the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/565C04B35/622C04B35/626
CPCC04B35/565C04B35/622C04B35/62605C04B2235/425C04B2235/424C04B2235/6562C04B2235/6567
Inventor 王东邱冰山陈兵刘飞王兴龙赵金
Owner SHAANXI UDC MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products