Production method of heat-sealing self-adhesive medical dialyzing paper

A production method and self-adhesive technology, applied in pulp beating method, pulp beating/refining method, paper and other directions, can solve the problems of low production efficiency, high production cost, low bonding strength on the surface of base paper, etc., and achieve production speed. Fast, low energy consumption, door width effect

Active Publication Date: 2020-03-31
安徽华邦古楼新材料有限公司
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies in the prior art, the technical problem to be solved by the present invention is to overcome the low bonding strength of the base paper produced by the prior art, and the high production cost and low production efficiency of the dialysis paper obtained by recoating the base paper surface. Defect, provide a kind of production method of heat-sealing self-adhesive medical dialysis paper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A kind of production method of heat-sealing self-adhesive type medical dialysis paper comprises the following steps:

[0035] Slurry disintegration: the silver star softwood pulp and star hardwood pulp with a ratio of 1:0.75 are mixed with sodium bicarbonate with a per ton pulp dosage of 3kg and a per ton pulp dosage of 2kg sodium carboxymethyl cellulose. Disintegrate in a disintegrator for 15 minutes, and finally add water to make a slurry with a concentration of 4.5%.

[0036] Beating: the process The slurry is made through a beating system with a knockout degree of 28 0 SR, a slurry with a wet weight of 6.5 g and a concentration of 4.2%.

[0037] Blending: the process Dilute the slurry with a concentration of 4.2% to a concentration of 3.5%, and mix it with additives evenly. The auxiliary agents include 1.8% of tapioca starch enhancer, 4.0% of wet strength agent, 1.8% of AKD sizing agent and 0.2% of peeling agent in the absolute dry slurry gelatinized at ...

Embodiment 2

[0045] A kind of production method of heat-sealing self-adhesive type medical dialysis paper comprises the following steps:

[0046] Slurry disintegration: silver star softwood pulp and star hardwood pulp with a ratio of 1:0.65 are mixed with sodium bicarbonate with an amount of 2.5 kg per ton of pulp and carboxymethyl cellulose with an amount of 1.5 kg per ton of pulp Disintegrate in a sodium hydrodisintegrator for 15 minutes, and finally add water to make a slurry with a concentration of 4.5%.

[0047] Beating: the process The slurry is made through a beating system with a knockout degree of 26 0 SR, a slurry with a wet weight of 7.0 g and a concentration of 4.0%.

[0048] Blending: the process Dilute the slurry with a concentration of 4.0% to a concentration of 3.5%, and mix it evenly with additives. The additives include 1.5% tapioca starch enhancer, 3.5% wet strength agent, 1.5% AKD sizing agent and 0.2% stripping agent.

[0049] Internet forming: the prepa...

Embodiment 3

[0056] A kind of production method of heat-sealing self-adhesive type medical dialysis paper comprises the following steps:

[0057] Slurry disintegration: silver star softwood pulp and star hardwood pulp with a ratio of 1:0.55 are mixed with sodium bicarbonate with an amount of 2 kg per ton of pulp and sodium carboxymethyl cellulose with an amount of 1.2 kg per ton of pulp Disintegrate into a hydraulic disintegrator for 15 minutes, and finally add water to make a slurry with a concentration of 4.5%.

[0058] Beating: the process The slurry is made through a beating system with a knockout degree of 25 0 SR, a slurry with a wet weight of 7.8 g and a concentration of 4.0%.

[0059] Blending: the process Dilute the slurry with a concentration of 4.0% to a concentration of 3.5%, and mix it evenly with additives, which include 1.2% tapioca starch enhancer, 2.8% wet strength agent, 1.2% AKD sizing agent and 0.15% stripping agent.

[0060] Internet forming: the prepare...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production method of heat-sealing self-adhesive medical dialyzing paper. The production method comprises the following steps: pulping a pulp; pulping; preparing materials; forming on a net; squeezing and dehydrating; drying and surface sizing; drying, transferring and coating; calendaring and coiling; rewinding and packaging to obtain a finished product. According to themedical dialyzing paper prepared by the method, the indexes of air permeability and bonding strength can meet the use requirements of the medical industry, the production of base paper and an adhesivelayer is completed in a papermaking machine in one time, the medical dialyzing paper is directly used for manufacturing medical packaging paper plastic bags, the equipment, labor and transportation cost can be saved, and the efficiency is greatly improved.

Description

technical field [0001] The invention relates to a production method of heat-sealing self-adhesive medical dialysis paper, which belongs to the field of medical paper manufacturing. Background technique [0002] It has been more than 10 years since sterilization packaging was introduced to China, and disposable medical devices have replaced traditional glass medical devices. Many types of sterilization packaging have also appeared on the market, one of which is widely used is a paper-plastic bag package made of high-density polyethylene on one side and dialysis paper on the other: that is, the surface of the dialysis paper is gravure printed, Coating thermoplastic resin, or directly heat-sealing or glue-sealing with film materials such as high-density polyethylene, to make a paper-plastic packaging bag with dialysis function. Paper-plastic bags are favored by the medical industry and manufacturers because of their good antibacterial effect, long storage time, and convenient ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21F11/02D21B1/34D21D1/02D21D1/30D21H21/20D21H21/16D21F3/00D21F5/02D21F5/18D21H23/22D21G1/00
CPCD21F11/02D21B1/345D21D1/02D21D1/30D21H21/20D21H21/16D21F3/00D21F5/02D21F5/18D21H23/22D21G1/00
Inventor 胡江涛许国强潘卫忠江景日程雪丽雷振
Owner 安徽华邦古楼新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap