Inorganic anticorrosive paint and preparation method thereof

An anti-corrosion coating, inorganic technology, applied in the direction of anti-corrosion coatings, fire-proof coatings, coatings, etc., can solve the problems of inability to effectively reduce the temperature of phosphate coatings, poor curing effect and low activity curing agent, and affect the overall performance of coatings, etc., to achieve Avoid the effects of being unable to form a film, no VOC release, and good high temperature resistance

Active Publication Date: 2020-04-17
烟台海誉新材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there are the following problems in the popularization and application of phosphate coating materials. The addition of basic metal oxide curing agents can effectively reduce the curing temperature of the coating, but the use of low-activity curing agents with relatively poor curing effects cannot effectively reduce the temperature of phosphate coatings. temperature, while the strong curing agent is easy to cause the curing reaction to be too fast, which affects the overall performance of the coating after curing and cannot form a film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inorganic anticorrosive paint and preparation method thereof
  • Inorganic anticorrosive paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1 A kind of inorganic anticorrosion coating

[0031] Its preparation raw materials include by weight:

[0032] Aluminum dihydrogen phosphate adhesive: 80 parts;

[0033] Curing agent: 10 parts;

[0034] Auxiliary: 4 parts;

[0035] Filling: 4 parts;

[0036] Distilled water: 80 parts.

[0037] The aluminum dihydrogen phosphate adhesive is an aqueous solution of aluminum dihydrogen phosphate with a mass content of 25%.

[0038] The curing agent is a mixture of zinc oxide, magnesium oxide and nickel oxide, and the mass ratio of the zinc oxide, magnesium oxide and nickel oxide is 1:3:5.

[0039] The auxiliary agent is a mixture of borax and polydimethylsiloxane, and the mass ratio of borax to polydimethylsiloxane is 1:5.

[0040] The filler is a mixture of calcium aluminate, magnesium sulfate and nano molybdenum disulfide, and the mass ratio of calcium aluminate, magnesium sulfate and nano molybdenum disulfide is 10:6:1.

[0041] The average particle diam...

Embodiment 2

[0045] Embodiment 2 A kind of inorganic anticorrosion coating

[0046] Its preparation raw materials include by weight:

[0047] Aluminum dihydrogen phosphate adhesive: 90 parts;

[0048] Curing agent: 15 parts;

[0049] Auxiliary: 1 part;

[0050] Filling: 8 parts;

[0051] Distilled water: 90 parts.

[0052] The aluminum dihydrogen phosphate adhesive is an aqueous solution of aluminum dihydrogen phosphate with a mass content of 25%.

[0053] The curing agent is a mixture of zinc oxide, magnesium oxide and nickel oxide, and the mass ratio of zinc oxide, magnesium oxide and nickel oxide is 1:1:5.

[0054] The auxiliary agent is a mixture of borax and polydimethylsiloxane, and the mass ratio of borax to polydimethylsiloxane is 1:2.

[0055] The filler is a mixture of calcium aluminate, magnesium sulfate and nano molybdenum disulfide, and the mass ratio of calcium aluminate, magnesium sulfate and nano molybdenum disulfide is 10:6:3.

[0056] The average particle diameter ...

Embodiment 3

[0061] Embodiment 3 A kind of inorganic anticorrosion coating

[0062] Its preparation raw materials include by weight:

[0063] Aluminum dihydrogen phosphate adhesive: 85 parts;

[0064] Curing agent: 12 parts;

[0065] Auxiliary: 2 parts;

[0066] Filling: 6 parts;

[0067] Distilled water: 85 parts.

[0068] The aluminum dihydrogen phosphate adhesive is an aqueous solution of aluminum dihydrogen phosphate with a mass content of 25%.

[0069] The curing agent is a mixture of zinc oxide, magnesium oxide and nickel oxide, and the mass ratio of zinc oxide, magnesium oxide and nickel oxide is 1:2:5.

[0070] The auxiliary agent is a mixture of borax and polydimethylsiloxane, and the mass ratio of borax to polydimethylsiloxane is 1:4.

[0071]The filler is a mixture of calcium aluminate, magnesium sulfate and nano molybdenum disulfide, and the mass ratio of calcium aluminate, magnesium sulfate and nano molybdenum disulfide is 10:6:2.

[0072] The average particle diameter ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an inorganic anticorrosive paint. The inorganic anticorrosive paint is prepared from the following raw materials in parts by weight: 80-90 parts of an aluminum dihydrogen phosphate adhesive, 10 to 15 parts of a curing agent, 1-4 parts of an auxiliary agent, 1-4 parts of a filler and 80 to 90 parts of distilled water, wherein the curing agent is a mixture of zinc oxide, magnesium oxide and nickel oxide, the auxiliary agent is a mixture of borax and polydimethylsiloxane, and the filler is a mixture of calcium aluminate, magnesium sulfate and nanometer molybdenum disulfide. The inorganic anticorrosive paint provided by the invention can realize self-curing at room temperature, does not release VOC, and has good corrosion resistance, heat resistance and water resistance.

Description

technical field [0001] The invention relates to the technical field of anti-corrosion coatings, in particular to an inorganic anti-corrosion coating and a preparation method thereof. Background technique [0002] Metal materials such as iron and steel are widely used in various fields of national economic construction, but their poor corrosion resistance also limits their application. Among them, anti-corrosion coating has become one of the most commonly used and effective methods to prevent corrosion of metal materials such as steel. Anti-corrosion coating materials refer to materials that can be cured to form a tough protective film coated on the surface of metal materials such as steel. However, most of the polluting raw materials contained in organic coatings will be lost to the surrounding environment during production and application, causing certain harm to the human body and the environment. At the same time, the limited high temperature resistance of organic coatin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/08C09D7/61C09D7/65
CPCC09D1/00C09D5/08C09D5/18C09D7/61C09D7/65
Inventor 王志政
Owner 烟台海誉新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka