Easy-to-clean coating and preparation method and application thereof

An easy-to-clean and paint technology, applied in the field of paint, can solve the problems of easy to absorb oil stains, easy to scratch, easy to crack and aging, etc.

Inactive Publication Date: 2020-04-21
HEFEI HUALING CO LTD +2
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the refrigerator liner, end cover and fruit and vegetable boxes are mostly made of acrylonitrile-butadiene-styrene copolymer ABS, impact-resistant polystyrene HIPS or general-purpose polystyrene GPPS, which have a large surface energy and are easy to absorb oil stains It is difficult to clean; in addition, this kind of material also has problems such as low hardness, easy to scratch, and easy to crack and age when it is in contact with food oil for a long time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Easy-to-clean coating and preparation method and application thereof
  • Easy-to-clean coating and preparation method and application thereof
  • Easy-to-clean coating and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0081] Leveling and defoaming agents can improve the preparation efficiency and leveling performance of coatings.

[0082] In some embodiments, the water contact angle of the easy-to-clean paint is not less than 90°; preferably, the water contact angle of the easy-to-clean paint is not less than 99°; more preferably, the water contact angle of the easy-to-clean paint Not less than 100°.

[0083] In some embodiments, the oil contact angle of the easy-to-clean paint is not less than 40°; preferably, the oil contact angle of the easy-to-clean paint is not less than 45°; more preferably, the oil contact angle of the easy-to-clean paint Not less than 49°.

[0084] Another aspect of the present invention provides a method for preparing the above-mentioned easy-to-clean coating, comprising the steps of:

[0085] 1) Add fluorosilicon modified acrylic resin to the solvent and mix evenly, then add polyurethane acrylate to obtain a mixed solution;

[0086] 2) Add dispersant and solven...

Embodiment 1

[0098] Composition: 25.7 parts by weight of fluorosilicon modified acrylic resin, 15.4 parts by weight of polyurethane acrylate, 1.3 parts by weight of dispersant, 51.5 parts by weight of solvent, 1 part by weight of curing agent, 0.5 parts by weight of leveling agent and 0.8 parts by weight of defoamer.

[0099] Among them, the functionality of fluorosilicon modified acrylic resin is 3, the solid content is 73wt%, and the viscosity at 25°C is 700cps; the functionality of polyurethane acrylate is 10, the solid content is 100wt%, and the viscosity at 60°C is 1500cps; The dispersant is trimethylolpropane triacrylate; the curing agent is 1-hydroxyl-cyclohexyl phenyl ketone; the leveling agent is a polyether modified silicone polymer; the solvent is 38.6 parts by weight of propylene glycol methyl ether and butyl acetate 12.9 parts by weight of ester.

[0100] preparation:

[0101]First weigh 25.7 parts by weight of fluorosilicone modified acrylic resin in 38.6 parts by weight of ...

Embodiment 2

[0103] Composition: 25.7 parts by weight of fluorosilicon modified acrylic resin, 15.4 parts by weight of polyurethane acrylate, 1.3 parts by weight of dispersant, 51.5 parts by weight of solvent, 1 part by weight of curing agent, 0.5 parts by weight of leveling agent, 0.8 parts by weight of defoaming agent and 1.5 parts by weight of nano silicon dioxide.

[0104] Among them, the functionality of fluorosilicon modified acrylic resin is 3, the solid content is 73wt%, and the viscosity at 25°C is 700cps; the functionality of polyurethane acrylate is 10, the solid content is 100wt%, and the viscosity at 60°C is 1500cps; The dispersant is trimethylolpropane triacrylate; the curing agent is 1-hydroxyl-cyclohexyl phenyl ketone; the leveling agent is a polyether modified silicone polymer; the solvent is 38.6 parts by weight of propylene glycol methyl ether and butyl acetate 12.9 parts by weight of the ester; the particle size of the nano silicon dioxide is 50nm.

[0105] preparation...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Water contact angleaaaaaaaaaa
Water contact angleaaaaaaaaaa
Water contact angleaaaaaaaaaa
Login to view more

Abstract

The invention relates to an easy-to-clean coating and a preparation method and application thereof. The easy-to-clean coating comprises the following components in parts by weight: 20 to 30 parts of fluorosilicone modified acrylic resin, 10 to 20 parts of urethane acrylate, 0.5 to 7 parts of a dispersing agent, 23 to 60 parts of a solvent and 0.7 to 1.5 parts of a curing agent. The preparation method comprises the following steps: 1) adding the fluorosilicone modified acrylic resin into the solvent, carrying out uniform mixing, and adding the urethane acrylate to obtain a mixed solution; 2) sequentially adding the dispersing agent and the solvent into the mixed solution and carrying out uniform mixing; and 3) finally, adding the curing agent until the curing agent is completely dissolved to obtain the easy-to-clean coating. The easy-to-clean coating disclosed by the invention has the advantages of good adhesive force, high wear resistance, good toughness, aging resistance and the like,and is low in cost and excellent in comprehensive performance.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an easy-to-clean coating and a preparation method and application thereof. Background technique [0002] With the rapid development of science and technology, the application and research of engineering plastics are becoming more and more extensive. Compared with other materials, its performance in all aspects has reached a higher standard, and it has been widely used in household appliances. However, due to the working environment of different household appliances, there are also some special functional requirements for engineering plastics. For example, the refrigerator liner, end cover and fruit and vegetable boxes are mostly made of acrylonitrile-butadiene-styrene copolymer ABS, impact-resistant polystyrene HIPS or general-purpose polystyrene GPPS, which have a large surface energy and are easy to absorb oil stains It is difficult to clean; in addition, this kind of material also ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/04C09D175/14C09D7/42C09D7/61C08J7/04C08J7/046
CPCC08J2433/04C08J2475/14C08K2201/011C08L2201/10C08L2205/03C09D133/04C09D175/14C09D7/42C09D7/61C08L75/14C08L83/12C08K3/36C08L33/04
Inventor 雷健
Owner HEFEI HUALING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap