A kind of high-strength aluminum alloy material and preparation method thereof

An aluminum alloy material, high-strength technology, applied in the field of aluminum alloy preparation, can solve problems such as affecting the yield strength, brittleness and plasticity of aluminum alloys, no specific solutions are proposed, and extrusion production efficiency is reduced, and achieves a small aggregation tendency. , improve strength and toughness, improve the effect of shape

Active Publication Date: 2021-02-19
佛山市三水凤铝铝业有限公司 +1
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

6XXX alloys have good formability and weldability, and are widely used because of their good corrosion resistance and surface treatment capabilities. However, the extrusion speed of this type of alloy is very slow when extruding thin-walled profiles, which will cause extrusion The production efficiency is significantly reduced. In addition, the refinement and deterioration of the structure in the process of preparing aluminum alloys, the degree of refinement of the grains in the structure will directly affect the yield strength, brittleness, and plasticity of the aluminum alloy. Therefore,
[0003] For example, the patent No. CN106414782A discloses a new type of 6xxx aluminum alloy with an improved combination of properties; another example is U.S. Patent No. 7,182,825, U.S. Patent Application Publication No. 2014 / 0000768 and U.S. Patent Application Publication No. 2014 Continuous casting of 6XXX alloys is described in / 036998, but these prepared 6XXX alloys do not have more detailed treatment for α-Al embryos, eutectic silicon clusters, and iron-rich phases
[0004] In summary, in the field of preparing aluminum alloys, there are still many practical problems that need to be dealt with in practical applications, and no specific solutions have been proposed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-strength aluminum alloy material and preparation method thereof
  • A kind of high-strength aluminum alloy material and preparation method thereof
  • A kind of high-strength aluminum alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A high-strength aluminum alloy material, the aluminum alloy material includes the following elements by mass percentage: Si0.7wt%, Fe≤0.50wt%, Cu 0.05wt%, Mn≤0.5wt%, Mg 1.2wt%, Cr≤ 0.05wt%, Zn≤0.2wt%, Ti≤0.1wt%, the balance is Al and other unavoidable impurities; wherein, the Mn element is added in the form of Al-Mn master alloy, and the Cr element is added in the form of Al-Cr The master alloy is added, and the Al-Mn master alloy and the Al-Cr master alloy work together to refine the α-Al embryo, the eutectic silicon cluster and the iron-rich phase.

[0035] In addition, the preparation method of the high-strength aluminum alloy material includes the following steps:

[0036] a. adopt endogenous method to prepare Al-Mn master alloy and Al-Cr master alloy respectively; In the present embodiment, the method for described endogenous method to prepare Al-Mn master alloy is the Mn powder that is 1:3 according to weight Put the aluminum powder into a ball mill for ball mill...

Embodiment 2

[0044] A method for preparing a high-strength aluminum alloy material, comprising the steps of:

[0045] a. adopt endogenous method to prepare Al-Mn master alloy and Al-Cr master alloy respectively; In the present embodiment, the method for described endogenous method to prepare Al-Mn master alloy is the Mn powder that is 1:3 according to weight Put the aluminum powder into a ball mill for ball milling, and mix the materials for 8 hours at a speed of 75r / min. Wrap the evenly mixed Mn powder and aluminum powder with aluminum foil, put them into the mold, and apply unidirectional axial The pressure is 100 MPa, and the pressure is maintained for 5 minutes, then heated to 1000 ° C, cooled to room temperature to obtain an Al-Mn master alloy, and the average particle size of the Mn powder and aluminum powder after ball milling is 45 μm; the inner The method of preparing Al-Cr master alloy by raw method is to put Cr powder and aluminum powder in a ball mill with a weight ratio of 1:5...

Embodiment 3

[0054] A method for preparing a high-strength aluminum alloy material, comprising the steps of:

[0055] a. adopt endogenous method to prepare Al-Mn master alloy and Al-Cr master alloy respectively; In the present embodiment, the method for described endogenous method to prepare Al-Mn master alloy is the Mn powder that is 1:3 according to weight And the aluminum powder is put into a ball mill for ball milling. Under the condition of the rotating speed of 60r / min, the mixture is mixed for 5 hours, and the evenly mixed Mn powder and aluminum powder are wrapped with aluminum foil, put into the mold, and the unidirectional axial The pressure is 65 MPa, and the pressure is maintained for 3 minutes, then heated to 960 ° C, cooled to room temperature to obtain an Al-Mn master alloy, and the average particle size of the Mn powder and aluminum powder after ball milling is 35 μm; the inner The method for preparing the Al-Cr master alloy by the raw method is to put Cr powder and aluminum...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a high-strength aluminum alloy material and a preparing method thereof. An Al-Mn intermediate alloy and an Al-Cr intermediate alloy jointly act on refined alpha-Al crystal blanks, eutectic silicon clusters and an iron-rich phase, and the problem that an iron phase is rough and in a strip shape in an aluminum alloy, too many eutectic silicon clusters exist, the total crystalgrains rough, and aluminum alloy performance is poor can be solved. On the other hand, the forming temperature of the iron-rich phase can be improved, the solidifying sequence of the iron-rich phase can be changed, the forming temperature of the iron-rich phase is increased to be slightly higher than an alpha-Al matrix from the temperature betweeny alpha-Al and eutectic silicon, a large amount ofAl(MnFe)Si four-element high-temperature mass points can be formed to serve as heterogeneous nucleation cores of the alpha-Al, two intermediate alloys jointly act, components of eutectic points can bereduced, heat stability is higher, and minimum aggregation tendency is achieved. In addition, an aluminum alloy prepared by the method can meet the aluminum alloy lightweight and high strength needsof a vehicle manufacturer.

Description

technical field [0001] The invention relates to the field of aluminum alloy preparation, in particular to a high-strength aluminum alloy material and a preparation method thereof. Background technique [0002] In the automotive field, vehicle designers and manufacturers are constantly striving to improve overall fuel efficiency, and one of the most direct ways to improve fuel efficiency is to reduce the vehicle's structural weight. According to statistics, if the weight of the car is reduced by 35%, the fuel can be saved by more than 30%, the engine output power can be increased by more than 30%, and the carbon dioxide emission can be reduced at the same time, which can save energy and reduce environmental pollution. If the weight of the car is reduced by 25%, the time to accelerate the car to 100KM / hour can be reduced from 10 seconds to 8 seconds; the use of aluminum wheels can reduce the vibration and allow the use of a lighter rebound buffer; Aluminum is to reduce the we...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/02C22C21/08C22C1/03C22F1/043C22F1/047C22F1/05B22F9/04
CPCB22F9/04B22F2009/041B22F2009/043C22C1/026C22C1/03C22C21/02C22C21/08C22F1/043C22F1/047C22F1/05
Inventor 黄志其陈慧胡权许栩达
Owner 佛山市三水凤铝铝业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products