Antibacterial and antistatic additive for PE and preparation method thereof

An additive, antibacterial and antistatic technology, which is applied in the field of antibacterial and antistatic additives for PE and its preparation, can solve the problems of being easily affected by ambient temperature and humidity, and the antistatic effect is not durable, and achieves excellent compatibility and long-term antistatic effect. The effect of electrostatic properties and easy operation of the reaction

Active Publication Date: 2022-02-25
泉州绿陆新材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing new antistatic agents in the domestic market are mainly surfactants, the antistatic effect is not durable, and they are easily affected by ambient temperature and humidity, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial and antistatic additive for PE and preparation method thereof
  • Antibacterial and antistatic additive for PE and preparation method thereof
  • Antibacterial and antistatic additive for PE and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Step (1) Dissolve 1mol of amino-dodecaethylene glycol-carboxylic acid (A) and 1mol of maleic anhydride (B) in tetrahydrofuran, heat to reflux for 30h, filter, wash, and dry to obtain amic acid; 1mol Dissolve amic acid in benzene, add 1.2mol anhydrous zinc chloride, heat to 80°C, add dropwise benzene dissolved in 1.8mol hexamethyldisilazane, after the dropwise addition, heat to reflux for 8 hours, filter, and the filtrate Concentrate to get oil. Use 10% hydrochloric acid to adjust the pH to 1, solids precipitate out, add ethyl acetate to dissolve, separate the liquids, extract the aqueous phase with ethyl acetate for 3 times, combine the organic phases, and wash with anhydrous Na 2 SO 4 Drying. Filtration, concentration, to get intermediate product I (IR: 1649cm -1 : the presence of -C=O of the amide bond; 1720cm -1 :-C=O generation; 3505cm -1 : -OH exists; 1601 cm -1 、810cm -1 :-C=C-exists).

[0038] Step (2) Dissolve the mixture of 1.2mol I, 1.2mol dicyclohexylc...

specific Embodiment 2-6

[0040] Specific embodiment 2-6, other are with specific embodiment 1, difference is following table:

[0041]

[0042]

[0043] The antibacterial and antistatic additive obtained in specific example 1 is used as the basic material of the application example, added to PE pellets, and blown into a film to obtain an antibacterial and antistatic PE film.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of plastic processing aids. The invention relates to a novel antibacterial and antistatic additive for PE and a preparation method thereof. The method uses amino-dodecapolyethylene glycol-carboxylic acid (A), maleic anhydride (B), guanidine (C) and polyethylene as The raw materials are subjected to multi-step amidation reaction, blending, extrusion and blow molding to obtain the target product, a new type of antibacterial and antistatic additive. The utility of plastics provides antibacterial and antistatic groups from the structure, reduces the amount of plasticizers from the formulation, reduces static electricity accumulation, improves flame retardancy, prolongs its service life, and enriches its application fields, especially suitable for food packaging films.

Description

technical field [0001] The invention relates to an antibacterial and antistatic additive for PE and a preparation method thereof. The invention belongs to the field of plastic processing aids. Background technique [0002] Due to its abundant raw material resources, moderate price, and superior product comprehensive performance, polyethylene (PE) has been widely used, especially in the packaging field. Since the polyethylene material has a non-polar molecular structure, the molecular chain composed of its covalent bonds can neither be ionized nor transfer free electrons. Once charged due to the gain and loss of electrons due to friction, it is difficult to eliminate. The static electricity generated by the PE material during the processing brings a lot of inconvenience to the further processing of the packaging film material, affects the operational performance of the product, and the printing effect is affected by the electrostatic interference when the film is used for p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K5/31C08J3/22C08J5/18C08L23/06C07D207/452
CPCC08K5/31C08J3/226C08J5/18C07D207/452C08K2201/017C08J2423/06C08J2323/06
Inventor 华月圆
Owner 泉州绿陆新材料科技有限公司