A kind of water system high-voltage window antifreeze electrolyte and its application

A voltage window, electrolyte technology, applied in the direction of hybrid capacitor electrolytes, circuits, electrical components, etc., can solve the problems of electrochemical energy storage devices not working, restricting the application of high-concentration electrolytes, hindering ion transport, etc., to achieve excellent electrochemical performance. performance, viscosity reduction, effect of high ionic conductivity

Active Publication Date: 2021-11-09
LANZHOU INST OF CHEM PHYSICS CHINESE ACAD OF SCI
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, under low temperature conditions, the solubility of the solute will decrease, resulting in salting out of the high-concentration electrolyte, and the precipitated inorganic salt will adhere to the electrode material and the separator, hindering the transmission of ions, and causing the electrochemical energy storage device to fail to work, which is serious. Limits the application of high-concentration electrolytes in low-temperature environments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water system high-voltage window antifreeze electrolyte and its application
  • A kind of water system high-voltage window antifreeze electrolyte and its application
  • A kind of water system high-voltage window antifreeze electrolyte and its application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043] The preparation method provided by the invention is simple and convenient to operate and easy for large-scale production.

[0044] The present invention provides the application of the water system high-voltage window antifreeze electrolyte in the supercapacitor or battery described in the above scheme. The present invention has no special requirements on the positive electrode, negative electrode and diaphragm of the supercapacitor or battery; the present invention has no special requirements on the assembly method of the supercapacitor or battery, and the assembly method known to those skilled in the art can be used.

[0045] In a specific embodiment of the present invention, activated carbon is used as the positive electrode and the negative electrode respectively, and glass fiber is used as the diaphragm to assemble a button supercapacitor; activated carbon is used as the positive electrode, and sodium titanium phosphate is used as the negative electrode to assemble ...

Embodiment 1

[0049] NaClO 4 - Preparation of acetonitrile electrolyte:

[0050] 1.7mol NaClO 4 Add to 6mol water, stir and mix to obtain NaClO with a mass molar concentration of 15.74mol / kg 4 aqueous solution; then 2 mol of acetonitrile was added to NaClO 4 In the aqueous solution, stirring and mixing to obtain NaClO with a mass molar concentration of 8.94mol / kg 4 base electrolyte.

[0051] To the NaClO that embodiment 1 obtains 4 Electrochemical performance tests were performed on the base electrolyte, as follows:

[0052] (1) the NaClO that test embodiment 1 obtains 4 The voltage window of the base electrolyte: with the stainless steel column as the working electrode and the counter electrode, Ag / AgCl as the reference electrode to form a three-electrode system, the electrolyte of Example 1 is tested for the voltage window, and the test results are as follows figure 1 shown. From figure 1 It can be seen that the electrolyte solution of Example 1 has a stable voltage window of 2.8...

Embodiment 2

[0063] NaClO 4 - Preparation of Methanol Electrolyte:

[0064] 1.7mol NaClO 4 Add to 6mol water, stir and mix to obtain NaClO with a mass molar concentration of 15.74mol / kg 4 aqueous solution; then 2 mol methanol was added to NaClO 4 In the aqueous solution, stirring and mixing to obtain NaClO with a mass molar concentration of 9.88mol / kg 4 base electrolyte.

[0065] Test the NaClO that embodiment 2 obtains according to the method for embodiment 1 4 The voltage window and conductivity of the base electrolyte, the electrolyte of Example 2 was measured to have a stable voltage window of 2.8V, and the conductivity was 140.61mS / cm.

[0066] According to the method for embodiment 1, embodiment 2 is obtained NaClO 4 -Methanol electrolyte is used in supercapacitors, and cyclic voltammetry tests are carried out on supercapacitors at room temperature, 0°C, -20°C, -40°C and -60°C, and the test results are as follows Figure 6 shown. From Figure 6 It can be seen that the supercap...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
freezing pointaaaaaaaaaa
electrical conductivityaaaaaaaaaa
freezing pointaaaaaaaaaa
Login to view more

Abstract

The invention provides a water-system high-voltage window antifreeze electrolyte and application thereof. The electrolyte solution provided by the present invention includes an inorganic salt electrolyte, water and an organic solvent; the freezing point of the organic solvent is -12 to -97°C, the organic solvent is soluble in water, and the inorganic salt electrolyte is contained in the organic solvent Soluble; the molar ratio of the inorganic salt electrolyte, water and organic solvent is 1.1-3.1:4.5-6:2-7. The electrolyte solution provided by the invention can avoid salting out of the electrolyte solution in a low temperature environment, can also widen the voltage window of the aqueous electrolyte solution, and can provide higher ion conductivity, so that the electrochemical energy storage device can operate equally well in a low temperature environment. Has excellent electrochemical performance.

Description

technical field [0001] The invention relates to the technical field of low-temperature electrochemical energy storage, in particular to a water-system high-voltage window antifreeze electrolyte and its application. Background technique [0002] Aqueous electrochemical energy storage devices have attracted widespread attention due to their high safety and low cost. Electrolyte plays a key role in the operation of electrochemical energy storage devices, but the high freezing point of water (0°C) limits the application of water-based electrochemical energy storage devices, and the decomposition voltage of water is 1.23V, which is for The realization of high energy density electrochemical energy storage devices is very unfavorable. [0003] At present, the voltage window of the patented aqueous electrolyte is generally below 1.2V (CN 105280397 B, CN 104505263 B). In recent years, there have been some patent applications to achieve a wide voltage window of aqueous electrolytes ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/0566H01M10/0568H01M10/0569H01G11/58H01G11/60H01G11/62
CPCH01G11/58H01G11/60H01G11/62H01M10/0566H01M10/0568H01M10/0569Y02E60/10
Inventor 阎兴斌孙英伦窦青云马亚兰赵攀马鹏军
Owner LANZHOU INST OF CHEM PHYSICS CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap