PU adhesive for single-component microfiber leather and preparation method thereof

A microfiber leather, one-component technology, applied in the direction of adhesive additives, non-polymer adhesive additives, adhesive types, etc., can solve the problems of resin without cohesion, poor adhesion, etc., and achieve physical properties Excellent, good hydrolysis resistance, huge market potential effect

Active Publication Date: 2022-01-25
YANGZHOU POLYTECHNIC INST
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Most PU adhesives on the market are mainly wet paste. Normal PU adhesives will have poor adhesion after being baked in an oven at 110°C for 3 minutes, or the resin will be completely dried without adhesion.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PU adhesive for single-component microfiber leather and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Example 1: 400 g of polyhexamethylene adipate diol (molecular weight: 2000) was weighed and added into a three-necked flask, and the reaction temperature was raised to 110° C. to melt it, and at the same time, water removal treatment was carried out. Then add 0.02g of antioxidant and 0.003g of phosphoric acid and stir well therein, then add 50g of molten isocyanate MDI (R value is set to 1). Stir at high speed to make it viscosifying reaction, the reaction temperature is about 110 ℃, add the organic solvent N,N-dimethylformamide to dilute during the viscosifying process. Another organic solvent, isopropanol, was added after the reaction was finished and the mixture was stirred for 1 h. The prepared PU adhesive has a solid content of 40% and a viscosity of 80,000-120,000 (cps / °C). Wherein, the mass ratio of the used solvent N,N-dimethylformamide to isopropanol is 4:1.

Embodiment 2

[0030] Example 2: 400 g of polybutylene adipate diol (molecular weight: 2000) was weighed and added into a three-neck flask, the reaction temperature was raised to 110° C. to melt, and water removal treatment was carried out at the same time. Then add 0.02g of antioxidant and 0.003g of phosphoric acid and stir well therein, then add 42g of molten isocyanate NDI (R value is set to 1). Stir at high speed to make it viscosifying reaction, the reaction temperature is about 110 ℃, add the organic solvent N,N-dimethylformamide to dilute during the viscosifying process. Add another organic solvent, acetone, to continue stirring for 1 h after the reaction is complete. The prepared PU adhesive has a solid content of 40% and a viscosity of 80,000-120,000 (cps / °C). Wherein, the mass ratio of the used solvent N,N-dimethylformamide to acetone is 4:1.

Embodiment 3

[0031] Example 3: Weigh 400 g of polyhexamethylene sebacate diol (molecular weight: 2000) and put it into a three-necked flask, and the reaction temperature is raised to 110° C. to melt it, and at the same time, water removal treatment is carried out. Then add 0.02g of antioxidant and 0.003g of phosphoric acid and stir well therein, then add 48.9g of molten isocyanate TMXDI (R value is set to 1). Stir at high speed to make it viscosifying reaction, the reaction temperature is about 110 ℃, add the organic solvent N,N-dimethylformamide to dilute during the viscosifying process. After the reaction, another organic solvent butanone was added to continue stirring for 1 h. The prepared PU adhesive has a solid content of 40% and a viscosity of 80,000-120,000 (cps / °C). Wherein, the mass ratio of the used solvent N,N-dimethylformamide to butanone is 4:1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

This case involves a one-component PU adhesive for microfiber leather and its preparation method. The preparation method includes: putting polyester polyol into a reaction bottle and heating it to melt, then adding antioxidant BHT and phosphoric acid, stirring evenly and then adding The molten isocyanate is reacted at 110°C. During the reaction, an organic solvent is added for dilution until the viscosity of the system reaches 8-120,000 cps / °C; another organic solvent is added to the reaction bottle to adjust the solid content of the system to 40%, and then continue to stir for 1h before wrapping. The single-component PU adhesive for microfiber leather prepared in this case has the advantages of simple process and convenient operation; the prepared PU adhesive has a low softening point, good hydrolysis resistance, heat resistance and mildew resistance, and is suitable for dry pasting. When this PU adhesive is used for superfiber veneer, there will be no fogging phenomenon.

Description

technical field [0001] The invention relates to the field of leather adhesives, in particular to a single-component microfiber leather PU adhesive and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, higher requirements are put forward for daily necessities. The hand feel and physical properties of common types of wet-dry PU synthetic leather have gradually failed to meet people's needs for high-quality life. At this time, polyurethane microfiber leather came into being. Compared with different types of polyurethane synthetic leather, microfiber leather has a fleshy and icy feeling that is closer to or even surpasses real leather. At the same time, because the microfiber leather presents a three-dimensional hole structure similar to that of genuine leather, the waterproof and breathable performance of the microfiber leather is better. The preparation method of microfiber leather is similar to that of ordinary P...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J175/06C09J11/06C08G18/42C08G18/76
CPCC09J175/06C09J11/06C08G18/4238C08G18/7671C08G18/7678C08G18/7642C08K5/13
Inventor 王元有贾生超王雯门育龙王元帅
Owner YANGZHOU POLYTECHNIC INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap