Tea polyphenol-based deodorizing and bacteriostatic nursing pad and preparation method thereof
A tea polyphenol-based and tea polyphenol technology is applied in the field of tea polyphenol-based deodorant and antibacterial nursing pads and their preparation fields, and can solve the problem that the ideal antibacterial and deodorizing function cannot be achieved, the skin toxicity is unclear, and the use effect is large. Discount and other issues, to achieve the effect of significant deodorization effect, good product dispersion and good stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0034] (1) In 100 parts by mass of boiling water, put 2 parts by mass of green tea powder into the powder, stir and leach, after centrifugal sedimentation, carry out membrane separation and filtration to obtain green tea filtrate A;
[0035] (2) use ethyl acetate as extractant, take 1 mass part of filtrate A, put into 1 mass part of ethyl acetate, under normal temperature, ultrasonic extraction 40min, obtain extract B;
[0036] (3) Evaporate the extract B, and after drying, tea polyphenol C is obtained;
[0037] (4) Mix 100 parts by mass of tea polyphenol C with 5 parts by mass of nano titanium oxide, then use 3 parts by mass of sodium lauryl silicate to carry out surface treatment to obtain tea polyphenol-based deodorant antibacterial agent D;
[0038] (5) Add 2 parts by mass of tea polyphenol-based deodorant antibacterial agent D in 100 parts by mass of sodium polyacrylate superabsorbent resin, after mixing uniformly, mixture E is obtained;
[0039] (6) Press the mixture E ...
Embodiment 2
[0045] (1) In 100 parts by mass of boiling water, put 1 part by mass of green tea powder, stir and leach, after centrifugal sedimentation, carry out membrane separation and filtration to obtain green tea filtrate A;
[0046] (2) use ethyl acetate as extraction agent, take 1 mass part of filtrate A, put into 0.5 mass parts of ethyl acetate, under normal temperature, ultrasonic extraction 30min, obtain extract B;
[0047] (3) Evaporate the extract B, and after drying, tea polyphenol C is obtained;
[0048] (4) 100 parts by mass of tea polyphenol C are mixed with 2 parts by mass of nano-zinc carbonate, followed by surface treatment using 2 parts by mass of sodium dodecylbenzenesulfonate to obtain tea polyphenol-based deodorant bacteriostatic agent D;
[0049] (5) Add 1 mass part of tea polyphenol-based deodorant antibacterial agent D in 100 mass parts of sodium polyacrylate superabsorbent resin, after mixing uniformly, obtain mixture E;
[0050] (6) Press the mixture E with toil...
Embodiment 3
[0056] (1) in 100 mass parts of boiling water, put into 10 mass parts of green tea powder, stir and leach, after centrifugal sedimentation, carry out membrane separation and filtration, make green tea filtrate A;
[0057] (2) use ethyl acetate as extractant, take 1 mass part of filtrate A, put into 2 mass parts of ethyl acetate, under normal temperature, ultrasonic extraction 50min, obtain extract B;
[0058] (3) Evaporate the extract B, and after drying, tea polyphenol C is obtained;
[0059] (4) Mix 100 parts by mass of tea polyphenol C with 15 parts by mass of zinc oxide whiskers, then use 5 parts by mass of sodium dodecylbenzenesulfonate to carry out surface treatment to obtain tea polyphenol-based deodorant bacteriostatic agent D ;
[0060] (5) Add 3 parts by mass of tea polyphenol-based deodorant antibacterial agent D in 100 parts by mass of sodium polyacrylate superabsorbent resin, after mixing uniformly, obtain mixture E;
[0061] (6) Press the mixture E with toilet ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com