Production method of microcrystal antiskid ceramic tile

A production method and technology of microcrystals, which are applied in the field of production of microcrystal anti-skid tiles, can solve problems such as personnel falling and injury, and achieve the effects of increased friction coefficient and high practical value

Active Publication Date: 2020-07-31
FOSHAN SANSHUI NEW PEARL CONSTR CERAMICS IND +1
View PDF9 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention effectively solves the problem of people falling and hurting people due to wet water on the groun

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] A microcrystalline anti-slip ceramic tile and a production method thereof, comprising the following key steps.

[0023] (1) Formulate the formula of microcrystalline anti-skid glaze and prepare raw materials.

[0024] (2) The base glaze ingredients are pre-milled into a semi-finished glaze slurry.

[0025] (3) Add microcrystalline nuclei material and then ball mill to obtain microcrystalline non-slip glaze slurry.

[0026] (4) First pour a layer of bottom glaze, and then pour a layer of non-slip glaze slurry on the surface of the bottom glaze layer.

[0027] (5) A microcrystalline anti-slip layer is formed on the surface of the firing under specific temperature conditions, thereby obtaining a microcrystalline anti-slip tile.

[0028] In the above step (1), the formula composition of the microcrystalline anti-skid glaze slurry is as follows: 25% quartz, 18% limestone, 20% albite, 6% black mud, 4% aluminum oxide, Zinc 27%.

[0029] Among them, the microcrystalline cor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a production method of a microcrystal anti-skid ceramic tile. The production method comprises the following steps: (1) preparing a microcrystal anti-skid glaze to form a baseglaze ingredient; (2) pre-ball-milling the base glaze ingredient into a semi-finished glaze slip; (3) adding a microcrystalline core material, and carrying out ball milling to obtain a microcrystal antiskid glaze slip; (4) firstly spraying a layer of ground coat on a ground blank, and then spraying a microcrystalline antiskid glaze slip layer on the surface of the ground coat layer; and (5) firingthe surface under a specific temperature condition to form a microcrystal anti-skid layer so as to obtain the microcrystal anti-skid ceramic tile. The product produced by the invention effectively solves the problem of personnel falling injury caused by slippery ground becoming wet when encountering water, achieves perfect combination of an anti-skid function and soft surface texture, and has very high practical value.

Description

technical field [0001] The invention relates to a production method of building decoration materials, in particular to a production method of microcrystalline anti-skid tiles. Background technique [0002] The surface of traditional glazed tile products is a flat glass body, the surface is relatively smooth, and the anti-skid performance is poor; and through the dry particle anti-skid process, good anti-skid performance can be achieved, but the surface is too rough and the place of use is limited. Contents of the invention [0003] The technical problem solved by the present invention is to provide a kind of microcrystalline anti-slip ceramic tile. The principle is to add zinc oxide with very coarse particle size to the special base glaze to form a new formula system. Zinc and quartz will combine to form a fine crystal, and the microcrystal and glaze will be combined to form a microcrystal anti-slip layer on the glaze surface. When the water is in the water, the tiny groo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/04C03C10/00C04B41/89C04B41/86
CPCC03C8/04C03C10/0009C04B41/52C04B41/5023C04B41/89C04B41/86C04B41/504
Inventor 叶德林黄春林朱光耀韦前
Owner FOSHAN SANSHUI NEW PEARL CONSTR CERAMICS IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap