A kind of preparation method of natural denim effect leather
A technology of denim effect, applied in the field of preparation of natural denim effect leather, can solve the problems of cumbersome process and poor bonding, and achieve the effects of simplifying the process, promoting absorption and combination, and promoting penetration and combination
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0032] Wet blue leather squeezed, shaved, and weighed: Take 2 pieces of wet blue leather with the same origin, size, thickness and grade, squeeze water, shaved, and weigh the weight of the shaved wet blue leather as 12kg. The weight determines the parts by weight of the reagent used in the subsequent treatment process steps;
[0033]Pretreatment: Add 24kg of water at 40-50°C and 0.24kg of silane coupling agent (weak cationic silane coupling agent KT-3636 from Kite Silicone New Materials Co., Ltd.) into the drum, and rotate for 40 minutes; add 0.36kg of modified Non-toxic silica gel (cationic polyurethane silica gel KT-4301 from Kite Silicone New Materials Co., Ltd.), rotate for 90 minutes; finally add 0.36kg neutralizer (conventional industrial baking soda), rotate for 90 minutes, adjust the pH of the bath solution to 6.6-6.8, drain, wash;
[0034] Retanning filling: add 12kg of water at 30-40°C, 0.24kg of organic carboxylic acid polymer (MCS from United Chemical Company) in ...
Embodiment 2
[0039] Wet blue leather squeezed, shaved, and weighed: Take 3 pieces of wet blue leather with the same origin, size, thickness and grade, squeeze water, shaved, and weigh the weight of the shaved wet blue leather as 16kg. The weight determines the parts by weight of the reagent used in the subsequent treatment process steps;
[0040] Pretreatment: Add 30kg of water at 40-50°C, 0.24kg of silane coupling agent (weak cationic silane coupling agent KT-3636 from Kite Silicone New Materials Co., Ltd.) into the drum, and rotate for 30 minutes; add 0.64kg of modified Non-reactive silica gel (cationic polyurethane silica gel KT-43010.16kg, amphoteric acrylic silica gel KT-20340.48kg from Kate Silicone New Materials Co., Ltd.), rotate for 120min; finally add 0.32kg neutralizer (conventional industrial baking soda), rotate for 120min, adjust the bath liquid pH to 6.4-6.6, drain and wash with water;
[0041] Retanning filling: Add 16kg of water at 30-40°C, 0.32kg of organic carboxylic ac...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com