Magnetic wood treatment process

A processing technology, magnetic wood technology, applied in wood treatment, wood treatment details, wood processing equipment, etc., can solve problems full of electromagnetic pollution, human injury, electronic product impact, etc., to achieve the effect of reducing impact and interference

Inactive Publication Date: 2020-11-03
安徽葵普科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies of the prior art, the present invention provides a magnetic wood treatment process, which has the advantage of making the wood material magnetic, and solves the problem that the current living area is full of electromagnetic pollution, causing harm to the human body, and affecting electronic products. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A magnetic wood treatment process, comprising a powder method, the powder method comprising the following steps:

[0032] A1: Prepare magnetic powder, wood powder and resin adhesive, and pour them into the stirring tank according to the ratio of 3:8:5 to mix and stir. The speed of the stirring tank is 2400 rpm, so that the magnetic powder, wood powder and resin adhesive The adhesive is evenly mixed;

[0033] A2: Import the mixture obtained in the step A1 into a mold, and apply high pressure to it, and press it into a block;

[0034] A3: Send the obtained massive magnetic wood material into a drying oven, and dry it at 80-90°C. After drying, keep it healthy for a week, and then put it into storage.

Embodiment 2

[0036] A magnetic wood treatment process, comprising a coating method, the coating method comprising the following steps:

[0037] B1: Prepare paint and magnetic additives, mix iron powder and paint in a ratio of 8:3 and pour into a stirring tank for mixing and stirring. The speed of the stirring tank is 3200 rpm, so that the paint and iron powder are evenly mixed to obtain a magnetic paint;

[0038] B2: Apply the magnetic paint obtained in step B2 evenly on the wooden product, and dry it naturally at 32-40°C for 3 hours after painting;

[0039] B3: Repeat step B2 three times, then keep the wooden material coated with magnetic paint for one week to obtain magnetic wood, and put it into storage.

Embodiment 3

[0041] A magnetic wood treatment process comprising a filling method comprising the steps of:

[0042] C1: Mix the dipping potion and magnetic substance powder in a stirring tank at a ratio of 7:3;

[0043] C2: Put the wood to be treated into the impregnation tank for vacuuming. After the vacuuming is completed, inject the impregnation solution prepared in step C1 through the pipeline;

[0044] C3: After the injection is completed, pressurize to about 0.5MPa, and release it after keeping the pressure for 5 hours;

[0045] C4: Take out the wood and dry it at 80-90°C for one day, and then keep it for one week.

[0046] The impregnation treatment can reduce the polar substances in the wood and reduce the hygroscopicity of the wood. On the other hand, the filling material can increase the volume of the cell wall, and after the immersion in the wood, the esterification reaction will be carried out and the solidification will stay.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of magnetic wood treatment, and discloses a magnetic wood treatment process. The magnetic wood treatment process comprises a powder method, and the powdermethod comprises the following steps of A1, preparing magnetic powder, wood powder and a resin adhesive, pouring the magnetic powder, the wood powder and the resin adhesive into a stirring kettle according to a ratio, and carrying out mixing and stirring to uniformly mix the magnetic powder, the wood powder and the resin adhesive; A2, guiding a mixture obtained in the step A1 into a mold, applyinghigh pressure to the mixture, and pressing the mixture into blocks; and A3, feeding an obtained blocky magnetic wood material into a drying box, conducting drying at the temperature of 80-90 DEG C, conducting preserving for one week after drying is finished, and immediately warehousing the material. According to the magnetic wood treatment process, the problems that a current living area is filled with electromagnetic pollution, harm is caused to a human body, and electronic products are affected can be solved.

Description

technical field [0001] The invention relates to the technical field of magnetic wood treatment, in particular to a magnetic wood treatment process. Background technique [0002] With the rapid increase of industrial, transportation, electric power and living facilities, people are in an increasingly complex electromagnetic environment, and the geomagnetic field has become more and more complex in the local area. Nowadays, electromagnetic radiation pollution is Recognized as an important source of pollution that endangers the ecological environment, the United Nations Environmental Conference has also listed it as an important object of pollution prevention and control. With the wide application of electromagnetic technology, people have begun to pay attention to the benefits it brings when they enjoy the benefits it brings. pollution problem. Contents of the invention [0003] (1) Solved technical problems [0004] Aiming at the deficiencies of the prior art, the present...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27N3/08B27N3/18B27K3/08B27K5/04C08L97/02C08L101/00C08K3/22A01G7/06B05D7/06B05D3/02
CPCA01G7/06B05D3/02B05D7/06B27K3/08B27K5/04B27N3/08B27N3/18C08K2003/2251C08K2003/2265C08K2003/2272C08K2003/2275C08K2201/01C08L97/02C08L101/00C08K3/22
Inventor 周煜周楠周洪杰于海龙孙兴平张振
Owner 安徽葵普科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com