Antibacterial and high-temperature-resistant hydrocolloid and preparation method thereof

A hydrocolloid, high-temperature-resistant technology, applied in medical science, bandages, absorbent pads, etc., can solve problems such as hydrocolloid adhesion, overflow glue, and lack of antibacterial and anti-inflammatory properties, and achieve simple operation, prevention of wound inflammation, and easy-to-control technology Effect

Inactive Publication Date: 2020-11-27
丁淞
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the low softening point of rosin resin, it is easy to soften at room temperature and cause hydrocolloid to stick to other objects. Usually, there will be different degrees of g...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial and high-temperature-resistant hydrocolloid and preparation method thereof
  • Antibacterial and high-temperature-resistant hydrocolloid and preparation method thereof
  • Antibacterial and high-temperature-resistant hydrocolloid and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The present embodiment provides a kind of antibacterial, the preparation method of high temperature resistant hydrocolloid, comprises the following steps:

[0035] (1) Mix 150g of SBS, 100g of naphthenic oil and 10g of dibutyl hydroxytoluene, heat and melt at 120°C, and homogenize at a stirring speed of 20r / min for 0.5h to obtain mixture a;

[0036] (2) Maintain the temperature at 120°C, add 180g HIKOREZT-1080 to the mixture a obtained in step (1), and homogenize at a stirring speed of 20r / min for 0.5h to obtain mixture b;

[0037] (3) Maintain a temperature of 120°C, add 180 g of sodium carboxymethylcellulose to the mixture b obtained in step (2), and homogenize at a stirring speed of 20 r / min for 0.3 h at the same time to obtain a mixture c;

[0038] (4) Maintain the temperature of 120°C, add 10g of Manuka honey to the mixture c obtained in step (3), and homogenize at a stirring speed of 20r / min for 0.5h to obtain the mixture d; extrude the mixture d and heat it at 90...

Embodiment 2

[0040] The present embodiment provides a kind of antibacterial, the preparation method of high temperature resistant hydrocolloid, comprises the following steps:

[0041] (1) Mix 480g SIS, 250g naphthenic oil and 80g dibutyl hydroxytoluene, heat up to 190°C for melting, and homogenize at a stirring speed of 80r / min for 3 hours to obtain mixture a;

[0042] (2) Maintain the temperature at 190°C, add 390g HIKOREZT-1080 to the mixture a obtained in step (1), and homogenize at a stirring speed of 60r / min for 3 hours to obtain mixture b;

[0043] (3) Maintain a temperature of 190°C, add 390 g of sodium carboxymethylcellulose to the mixture b obtained in step (2), and homogenize at a stirring speed of 60 r / min for 2 hours to obtain a mixture c;

[0044] (4) Maintain the temperature at 190°C, add 150g of Manuka honey to the mixture c obtained in step (3), and homogenize at a stirring speed of 60r / min for 1 hour to obtain the mixture d; extrude the mixture d and carry out at 150°C Co...

Embodiment 3

[0046] The present embodiment provides a kind of antibacterial, the preparation method of high temperature resistant hydrocolloid, comprises the following steps:

[0047] (1) Mix 310g SEBS, 170g naphthenic oil and 40g dibutyl hydroxytoluene, heat up to 150°C for melting, and homogenize at a stirring speed of 50r / min for 1.5h to obtain mixture a;

[0048] (2) Maintain the temperature at 150°C, add 280g HIKOREZT-1080 to the mixture a obtained in step (1), and homogenize at a stirring speed of 40r / min for 1.5h to obtain mixture b;

[0049] (3) Maintain a temperature of 150°C, add 280 g of sodium carboxymethylcellulose to the mixture b obtained in step (2), and homogenize at a stirring speed of 40 r / min for 1 hour to obtain a mixture c;

[0050] (4) Maintain the temperature of 150°C, add 80g of Manuka honey to the mixture c obtained in step (3), and homogenize at a stirring speed of 40r / min for 0.7h to obtain the mixture d; extrude the mixture d and heat it at 150°C Coating, the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to antibacterial and high-temperature-resistant hydrocolloid and a preparation method thereof. The antibacterial and high-temperature-resistant hydrocolloid comprises raw materials in parts by weight as follows: 15-48 parts of thermoplastic elastomer, 1-8 parts of an antioxidant, 10-25 parts of a plasticizer, 18-39 parts of a tackifier, 18-39 parts of a thickening agent and 1-15 parts of honey. According to the antibacterial and high-temperature-resistant hydrocolloid, by means of optimization of related formula components, the hydrocolloid is prevented from overflowing in a long-term high temperature environment, can continuously keep good viscosity and can realize antibacterial and anti-inflammation effects in a using process, thereby solving troubles caused by hydrocolloid overflow in a daily using process of a user and being capable of preventing wound inflammation. The preparation method is simple to operate, the process is easy to control, and large-scale production is facilitated.

Description

technical field [0001] The invention belongs to the field of nursing after medical ostomy, and in particular relates to an antibacterial, high temperature resistant hydrocolloid and a preparation method thereof. Background technique [0002] At present, most hydrocolloids use rosin resin as a tackifier. However, due to the low softening point of rosin resin, it is easy to soften at room temperature and cause hydrocolloid to stick to other objects. Usually, there will be different degrees of glue overflow at room temperature or even in an environment of 40°C; at the same time, it does not have antibacterial and anti-inflammatory functions during use. Can not meet the current market demand. [0003] Therefore based on this, propose technical scheme of the present invention. Contents of the invention [0004] In order to solve the problems in the prior art, the invention provides an antibacterial, high temperature resistant hydrocolloid and a preparation method thereof. Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L15/28A61L15/24A61L15/40A61L15/46
CPCA61L15/24A61L15/28A61L15/40A61L15/46C08L1/286C08L25/10
Inventor 丁淞
Owner 丁淞
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap