Antibacterial purification biological-effective-element composite polyvinyl chloride new material

A compound polyvinyl chloride and new material technology, applied in the field of environmental protection additives, can solve problems such as carcinogenicity, achieve the effects of reducing chlorine toxicity, improving aroma, and protecting human health

Pending Publication Date: 2020-12-18
陈坤
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the traditional polyvinyl chloride (PVC) is used in various industries such as facial masks, building materials, packaging, and medical applications in the world. In 1995, the annual production of PVC in Europe was about 5 million tons. PVC contains (Chlorine), this is toxic vinyl chloride monomer with high content will volatilize a lot of chlorine gas, causing carcinogenic effect on human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial purification biological-effective-element composite polyvinyl chloride new material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] This antibacterial and purifying biological effect compound polyvinyl chloride new material is made of the following raw material proportions by weight: 30 parts of silicon-aluminum compound, 1 part of antibacterial agent Xingjiangzi essential oil, and 2 parts of polymer polycouple material , 2 parts of photosynthetic peptide white powder, 3 parts of calcite, 1 part of nano-scale dioxide peptide, 2 parts of dispersing lubricant, 1 part of coupling agent, 2 parts of charcoal, 5 parts of refined tea powder, in which the silicon-aluminum compound is made of silicon The mixture of ore superfine powder, aluminum ore superfine powder and calcium ore superfine powder, the mass ratio of silicon ore superfine powder, aluminum ore superfine powder and calcium ore superfine powder is 1:1:1.

[0029] Furthermore, the silicon-aluminum composite is comprehensively ultra-fine and calcined, and then becomes multi-mineral after thermal cracking.

[0030] Further, the calcite is fissione...

Embodiment 2

[0035] This antibacterial and purifying biological effect compound polyvinyl chloride new material is made of the following raw material proportions by weight: 40 parts of silicon-aluminum compound, 12 parts of antibacterial agent Xingjiangzi essential oil, and 11 parts of polymer polycouple material , 8 parts of photosynthetic peptide white powder, 10 parts of calcite, 8 parts of nano-scale dioxide peptide, 5 parts of dispersing lubricant, 7 parts of coupling agent, 16 parts of charcoal, 15 parts of refined tea powder, in which the silicon-aluminum compound is made of silicon The mixture of ore superfine powder, aluminum ore superfine powder and calcium ore superfine powder, the mass ratio of silicon ore superfine powder, aluminum ore superfine powder and calcium ore superfine powder is 1:1:1.

[0036] Furthermore, the silicon-aluminum composite is comprehensively ultra-fine and calcined, and then becomes multi-mineral after thermal cracking.

[0037] Further, the calcite is ...

Embodiment 3

[0042] This antibacterial and purifying biological effect compound polyvinyl chloride new material is made of the following raw material ratios in parts by weight: 50 parts of silicon-aluminum compound, 15 parts of antibacterial agent Xingjiangzi essential oil, and 15 parts of polymer polycouple material , 15 parts of photosynthetic peptide white powder, 20 parts of calcite, 10 parts of nano-scale dioxide peptide, 8 parts of dispersing lubricant, 10 parts of coupling agent, 20 parts of charcoal, 25 parts of refined tea powder, wherein the silicon-aluminum compound is made of silicon The mixture of ore superfine powder, aluminum ore superfine powder and calcium ore superfine powder, the mass ratio of silicon ore superfine powder, aluminum ore superfine powder and calcium ore superfine powder is 1:1:1.

[0043] Furthermore, the silicon-aluminum composite is comprehensively ultra-fine and calcined, and then becomes multi-mineral after thermal cracking.

[0044] Further, the calci...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an antibacterial purification biological-effective-element composite polyvinyl chloride new material, which comprises silica-alumina, an antibacterial agent pungent litse fruit essential oil, a polymer polycoupling material, Photosynthetic titanium dioxide, calcite, nano-scale peptide dioxide, a dispersion lubricant, a coupling agent, carbon and refined tea leaf powder. The antibacterial purification biological-effective-element composite polyvinyl chloride new material has the beneficial effects that the antibacterial purification biological-effective-element composite polyvinyl chloride new material is added into an ethylene raw material to be polymerized into modified polyvinyl chloride, chlorine toxicity in the manufacturing process is neutralized and reduced,damage to a human body is avoided, the health of the human body is protected, after a product is formed, and the sterilization and purification function effects are obvious; the sterilization effect is as follows: the mould resistance and killing efficiency reaches 100%, and bacteria, germs, staphylococcus aureus and the like in other gases are resisted and killed; the purifying function is as follows: harmful particle gases such as formaldehyde, methylbenzene, TVOC organic volatile matter and PM2.5 are removed, the using effect is good, and popularization is facilitated.

Description

technical field [0001] The invention relates to the technical field of environmental protection additives, in particular to a new antibacterial and purifying biological effect compound polyvinyl chloride material. Background technique [0002] At present, the traditional polyvinyl chloride (PVC) is used in various industries such as facial masks, building materials, packaging, and medical applications in the world. In 1995, the annual production of PVC in Europe was about 5 million tons. PVC contains (Chlorine), this is toxic vinyl chloride monomer high content will volatilize a lot of chlorine gas, causing carcinogenic effects on the human body. Especially for the disorder of human endocrine hormones, it will cause great harm. Contents of the invention [0003] The present invention aims to solve the problems existing in the above-mentioned prior art, and provides a new compound polyvinyl chloride material with antibacterial and purifying bioeffects, which is added to et...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L23/02C08K13/06C08K9/00C08K3/34C08K3/22C08K3/26C08K3/04C08K5/00
CPCC08L27/06C08K2201/014C08K2201/011C08K2003/2241C08K2003/265C08L23/02C08K13/06C08K9/00C08K3/34C08K3/22C08K3/26C08K3/04C08K5/0058
Inventor 林实俄林雪青陈坤
Owner 陈坤
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com