A kind of glass, glass product and manufacturing method thereof

A technology of glass and weight percentage, which is applied in the field of glass products and its manufacturing, can solve the problem of low impact, achieve high Young's modulus, reduce possibility, and excellent mechanical properties

Active Publication Date: 2022-04-15
CDGM OPTICAL GLASS
View PDF28 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, in the application of solar cell panel protection, the glass needs to keep the surface clean under long-term sand and dust impacts and wiped by wipers, but the possibility of impact is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of glass, glass product and manufacturing method thereof
  • A kind of glass, glass product and manufacturing method thereof
  • A kind of glass, glass product and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0110] In order to further clearly illustrate and illustrate the technical solution of the present invention, the following non-limiting examples are provided.

[0111]

[0112] The present invention adopts the manufacturing method of the above-mentioned glass to obtain the glass having the composition shown in Table 1-Table 3. In addition, the characteristics of each glass were measured by the test method described in the present invention, and the test results are shown in Tables 1 to 3.

[0113] Table 1.

[0114]

[0115]

[0116] Table 2.

[0117]

[0118]

[0119] table 3.

[0120]

[0121]

[0122]

[0123] Using the glasses shown in Tables 1 to 3, glass products were produced by the method for producing glass products, and the chemical strengthening process was shown in Tables 4 to 8. In addition, the characteristics of each glass product were measured by the test method described in the present invention, and the test results are shown in Table...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
refractive indexaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to View More

Abstract

The invention provides a kind of glass, the composition of the glass is represented by weight percentage, containing: SiO 2 : 41~65.5%; Al 2 o 3 : 17.5~31%; Li 2 O+Na 2 O: 5-14.5%; P 2 o 5 : 0.1~8%, of which Li 2 O / (Li 2 O+Na 2 O) is 0.1 to 0.4. Through reasonable component design, the glass obtained by the invention is suitable for chemical strengthening and secondary thermal processing, and also has a relatively high Young's modulus. The glass product obtained by the invention has high micro-Vickers hardness and excellent mechanical properties.

Description

technical field [0001] The present invention relates to a kind of glass, especially relates to a kind of glass suitable for chemical strengthening, and the glass article made from it and its manufacturing method. Background technique [0002] In the prior art, glass materials are widely used in fields such as panels, backplanes, and structural materials of various electronic devices (such as mobile phones, smart watches, etc.). In the above application fields, the primary consideration of glass materials is drop resistance and impact resistance. For example, CN110040982A, CN110627365A and CN106232541A all disclose glass with excellent drop resistance. [0003] The impact resistance and scratch resistance of glass materials are not the same performance. For example, building a two-phase composite structure can effectively improve the impact resistance of the material, and increasing the hardness can improve the scratch resistance of the material. In some applications, the s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C3/097C03C21/00
CPCC03C3/097C03C21/001C03C21/002
Inventor 马赫毛露路蔡冬雪
Owner CDGM OPTICAL GLASS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com