Forming die and forming method for special-shaped curved surface structural parts

A special-shaped surface, forming mold technology, applied in the field of precision sheet metal processing, can solve the problems of easy cracking, non-equal wall thickness products can not be formed at one time, large workload, etc., to ensure product quality, reduce wrinkling and Risk of cracking, effect of preventing stockpiling

Active Publication Date: 2022-03-04
BEIJING HANGXING MACHINERY MFG CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003]Cold stamping processing equipment and processing technology can only process products with equal wall thickness, and products with non-equal wall thickness cannot be formed at one time, and only tailor-welded after segmental forming can be used craft
[0004] There are the following disadvantages in adopting the process of segmented forming and then tailor welding: First, the process of segmented forming and then tailor welding requires manual repair, shape correction and grinding, and the workload is large , leading to extremely low product processing efficiency
Secondly, there are many welding seams, large welding seam deformation, and cracks are easy to occur in the shape correction, resulting in a low pass rate of the product at one time
Thirdly, the surface quality of the products processed by tailor welding process is poor
Finally, due to the presence of welds, the mechanical properties of the parts will inevitably be reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Forming die and forming method for special-shaped curved surface structural parts
  • Forming die and forming method for special-shaped curved surface structural parts
  • Forming die and forming method for special-shaped curved surface structural parts

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0072] A specific embodiment of the present invention discloses a forming device, which is used for one-time forming of structural parts with non-uniform wall thickness and special-shaped curved surfaces.

[0073] Non-equal wall thickness special-shaped curved surface structural parts include front section 8, shrinkage section 9 and tail section 10; the product material is: 1Cr18Ni9Ti stainless steel, the material thickness is 1mm and 2mm respectively, that is, the front section and shrinkage section are 1mm, the rear section is 2mm, and the product length × width × height is 1100mm × 130mm × 100mm, the product model after forming is as follows Figure 7 shown. The bottom surface of the formed special-shaped curved surface structure is inclined upward from the tail section to the front section, and the angle between the bottom surface and the horizontal plane is β, such as Figure 8 (a) and Figure 8 (b) shown.

[0074] According to the traditional design idea, in order to ...

Embodiment 2

[0100] Another specific embodiment of the present invention discloses a method for forming a structural member with non-uniform wall thickness and special-shaped curved surface. The forming die of Embodiment 1 is used for one-time forming of the structural member with non-uniform wall thickness and special-shaped curved surface.

[0101] Figure 8 (a) is a schematic diagram of the target product formed by a traditional mold, Figure 8 (b) is a schematic diagram of the target product formed by the forming die of the present invention. Figure 8 (a) and Figure 8 The products of (b) are identical, but superficially Figure 8 (a) The upper surface of the product is parallel to the horizontal plane, and the lower surface is inclined upward by an angle β; and Figure 8 (b) The lower surface of the product is parallel to the horizontal plane, and the upper surface is inclined downward at a certain angle.

[0102] The forming process of the product is described in detail below. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a forming mold and a forming method for a special-shaped curved surface structural part, which belongs to precision sheet metal processing, and solves the problems in the prior art that it is impossible to form products with non-uniform wall thickness special-shaped curved surfaces at one time, the surface quality of the product is poor, and the processing efficiency is low. . The forming mold includes an upper mold and a lower mold; the upper surface of the lower mold is provided with an opening, and the blank is in contact with the lower surface of the upper mold, and enters the cavity of the lower mold through the opening; the side of the upper mold is provided with steps, and the steps are connected with blanks of different thicknesses. Corresponding to the non-flat surface of . The forming method includes making a blank; welding the blank; placing the welded blank on a forming mold, and the welding seam corresponds to the steps of the upper mold; lowering the upper mold and the jacking cylinder to complete the one-time forming of the non-uniform wall thickness special-shaped curved surface structure. The invention realizes the one-time forming of the non-uniform wall-thickness special-shaped curved surface structural parts.

Description

technical field [0001] The invention relates to the technical field of precision sheet metal processing, in particular to a forming die and a forming method of a special-shaped curved surface structural part. Background technique [0002] Aerospace components are becoming more and more complex, and non-uniform wall thickness products are widely used in aerospace vehicles as a typical component. [0003] The cold stamping processing device and processing technology can only process products with equal wall thickness. For products with non-equal wall thickness, they cannot be formed at one time, and only the process of tailor welding after segmental forming can be used. [0004] The process of segmented forming and then tailor welding has the following disadvantages: First, the process of segmented forming and then tailor welding requires manual repair, shape correction, and grinding, and the workload is heavy, resulting in extremely low product processing efficiency. Secondl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21D37/10B21D22/06B21D45/02B21D43/00B21D37/12
CPCB21D37/10B21D22/06B21D45/02B21D43/003B21D37/12
Inventor 周蕾蕾刘奇李妍华李保永秦中环刘玉平韩维群
Owner BEIJING HANGXING MACHINERY MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap