A kind of preparation method of composite plant fiber imitation porcelain bottle

A plant fiber and composite fiber technology, applied in the field of imitation porcelain materials, can solve the problems of low impact strength and poor water resistance, and achieve the effects of low cost, improved mechanical properties, and outstanding water and oil resistance.

Active Publication Date: 2022-08-02
安徽绿之态秸秆制品有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a preparation method of a composite plant fiber imitation porcelain bottle, which solves the defects of low impact strength and poor water resistance of traditional plant fiber imitation porcelain bottle materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of composite plant fiber imitation porcelain bottle
  • A kind of preparation method of composite plant fiber imitation porcelain bottle

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A preparation method of a composite plant fiber imitation porcelain bottle, the steps comprising:

[0026] Step 1: Select raw materials, the raw materials include by weight: 80 parts of composite fiber powder, 10 parts of food-grade calcium carbonate ultrafine powder, 2 parts of starch, 1 part of rosin resin, 1 part of carboxymethyl chitosan and 1 part of carboxymethyl chitosan. parts epoxy silane;

[0027] Among them, the composite fiber powder is obtained by mixing the fiber raw materials with 0.5wt% citric acid solution, then treating at 20°C and 1MPa for 12 hours, and finally drying and grinding, and the fiber raw materials are made by mixing straw fibers and wood fibers;

[0028] Wherein, food-grade calcium carbonate ultrafine powder is obtained by the following operations:

[0029] (1) one-time treatment: under the condition of stirring, the calcium carbonate slurry that the solid content is 20% is added to the stearic acid-ethanol solution (V 硬脂酸 :V 乙醇 = 2:1),...

Embodiment 2

[0033] A preparation method of a composite plant fiber imitation porcelain bottle, the steps comprising:

[0034] Step 1: Select raw materials, the raw materials include by weight: 90 parts of composite fiber powder, 20 parts of food-grade calcium carbonate ultrafine powder, 5 parts of starch, 3 parts of rosin resin, 3 parts of carboxymethyl chitosan and 2 parts of carboxymethyl chitosan. parts styrylsilane;

[0035] Among them, the composite fiber powder is obtained by mixing the fiber raw materials with 20wt% salicylic acid solution, then treating it at 70 ° C and 5MPa for 6 hours, and finally drying and grinding. The fiber raw materials are mixed with straw fibers, bagasse fibers and bamboo pulp fibers. to make;

[0036] Wherein, food-grade calcium carbonate ultrafine powder is obtained by the following operations:

[0037] (1) one-time treatment: under the condition of stirring, the calcium carbonate slurry that the solid content is 50% is added to the stearic acid-ethan...

Embodiment 3

[0041] A preparation method of a composite plant fiber imitation porcelain bottle, the steps comprising:

[0042] Step 1: Select raw materials, which include by weight: 100 parts of composite fiber powder, 30 parts of food-grade calcium carbonate ultrafine powder, 8 parts of starch, 5 parts of rosin resin, 5 parts of carboxymethyl chitosan and 3 parts of carboxymethyl chitosan. parts of methacryloyloxysilane;

[0043] Among them, the composite fiber powder is prepared by mixing the fiber raw materials with 70wt% salicylic acid solution, then treating at 120 ° C and 8MPa for 0.1 h, and finally drying and grinding. The fiber raw materials are prepared by mixing rice husk fiber and bagasse fiber;

[0044] Wherein, food-grade calcium carbonate ultrafine powder is obtained by the following operations:

[0045] (1) one-time treatment: under the condition of stirring, the calcium carbonate slurry that the solid content is 80% is added to the stearic acid-ethanol solution (V 硬脂酸 :V ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
elastic modulusaaaaaaaaaa
water contact angleaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a composite plant fiber imitation porcelain bottle. The steps include: step 1, selecting raw materials, and the raw materials include: 80-100 parts of composite fiber powder, 10-30 parts of food-grade calcium carbonate superfine powder, 2- 8 parts of starch, 1-5 parts of rosin resin, 1-5 parts of carboxymethyl chitosan and 1-3 parts of silane coupling agent; Step 2, take each raw material and mix well, preheat at 70-90 ℃ for 1 ‑5min, and then press molding for 0.5‑5min under the conditions of 140‑170℃ and 30‑40MPa, that is, it is obtained. The invention makes full use of the advantages of plant fiber materials, adds food-grade calcium carbonate ultrafine powder as filler, and cooperates with the use of other additives to improve the mechanical properties of the material, improve the impact strength, and effectively prevent moisture , The adhesion of oil on the surface of the material and the penetration of the fiber wall cavity make the obtained imitation porcelain bottle high in strength, not easy to crack, resistant to falling, high surface gloss, and outstanding in water and oil resistance; the raw materials used are widely sourced, low in cost, and environmentally friendly , non-toxic.

Description

technical field [0001] The invention relates to the technical field of imitation porcelain materials, in particular to a preparation method of a composite plant fiber imitation porcelain bottle. Background technique [0002] Plant fibers are derived from crop straws and fast-regenerating plants. They are inexhaustible renewable resources in nature. They have the advantages of high strength, natural and simple surface texture, bright colors and novel textures, and are suitable for multiple production. , Repeatedly used items can replace some plastic, glass, pottery, porcelain and other products, such as vases, perfume bottles, wine bottles, etc. that are common in life. [0003] However, in the pulping process of plant fibers, many micropores will be formed on the surface of the cell wall, resulting in poor mechanical properties of the fiber material, low impact strength, and excessive surface wettability, showing hydrophilicity and poor water resistance. For this reason, wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L97/02C08L3/02C08L93/04C08L5/08C08K9/04C08K3/26C08K5/5435C08K5/54C08K5/5425
CPCC08L97/02C08K2003/265C08L2205/035C08L2205/025C08L2205/16C08L3/02C08L93/04C08L5/08C08K9/04C08K9/08C08K3/26C08K5/5435C08K5/54C08K5/5425
Inventor 刘海林崔巍潘杨笠刘和文赵原
Owner 安徽绿之态秸秆制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More