A kind of large diameter ductile iron pipe mold coating and its preparation method and application
A technology of ductile iron pipe and large diameter, which is applied in casting molding equipment, coating, casting mold, etc. It can solve the problems of high porosity, low refractive index, high melting point, etc., and achieve low air permeability, excellent surface quality and excellent performance Effect
Active Publication Date: 2021-12-10
广东新兴铸管有限公司
View PDF10 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
As we all know, diatomaceous earth is a water-resistant powder commonly used in casting coatings. It is mainly composed of the skeleton remains of a single-celled aquatic algae plant. It has high porosity, strong adsorption, small bulk density, high melting point, heat insulation, and absorption. Acoustic, low refractive index, stable chemical properties, etc., belong to non-renewable resources, and the cost is high
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
specific Embodiment
[0045] 1. Preparation of large diameter ductile iron pipe mold coating
[0046] The present invention provides a kind of preparation method of large diameter ductile iron pipe mold coating, comprises the following steps:
[0047] (1) Preparation of composite suspending agent
[0048] 1. In parts by weight, weigh 100 parts of rectorite and add it to 1000 parts of water, stir evenly, add 6 parts of amino-containing silane compound (KH550) after heating up to 80°C, react for 12 hours, and filter to obtain amino-modified retort stone;
[0049] 2. Add the amino-modified rectorite and succinic anhydride obtained in step 1 into the solvent according to the molar ratio of carboxyl and amino groups of 1:1, adjust the pH value to 4.0 and react for 6 hours, then filter and dry to prepare carboxylated rectorite ;
[0050] 3. The carboxylated rectorite obtained in step 2 is mixed with sodium bentonite and / or lithium bentonite according to the formulation amount in Table 1 to prepare a c...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| softening point | aaaaa | aaaaa |
| tensile strength | aaaaa | aaaaa |
Login to View More
Abstract
The present invention selects a variety of perlite and diatomite with different particle sizes as the mixed refractory aggregate, cooperates with a composite suspending agent composed of sodium bentonite and / or lithium bentonite and carboxylated rectorite, and adds hollow microspheres, A water-based centrifugal casting pipe mold coating for large-diameter ductile iron was prepared with commonly used binders, which has excellent suspension stability and high temperature crack resistance, as well as low gas generation, permeability and moisture absorption . At the same time, the present invention also adjusts and optimizes the specific spraying process to coat the large-diameter ductile iron pipe mold paint on the surface of the pipe mold, and the surface of the large-diameter ductile iron pipe prepared after centrifugal casting has no pores and sticky sand. , Shrinkage cavity and other surface defects, the surface quality is excellent.
Description
technical field [0001] The invention belongs to the technical field of refractory coatings, in particular to a large-diameter ductile iron pipe mold coating and a preparation method and application thereof. Background technique [0002] Centrifugal casting is a casting method of pouring and forming under a centrifugal force field, and is the main method for the production of large-diameter ductile iron pipe fittings. Among them, the pipe mold is a mold that works in a hot state in centrifugal casting. It is subjected to sharp thermal alternating loads in continuous production. When the accumulation of residual stress exceeds the ultimate strength of the material, a thermal crack grid will be generated. scrapped. Pipe molds are expensive. In order to reduce production costs, improve pipe mold production conditions, and prolong pipe mold life, there are currently two effective ways to protect pipe molds: coating casting paint and cloth resin sand. Due to the poor surface qua...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): B22C3/00B22D13/02
CPCB22C3/00B22D13/02
Inventor 暴延强梅燕娜王世锋杨京龙孔少华宋斌林雪川赵文亮董小宏于礼勇张胜平
Owner 广东新兴铸管有限公司