Efficient waterproof material for tunnels and preparation method thereof

A waterproof material and high-efficiency technology, applied in the field of waterproof materials, can solve problems such as poor fracture resistance and tensile performance, poor waterproof effect, etc.

Active Publication Date: 2021-08-31
CHINA FIRST HIGHWAY ENG
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing waterproof materials for tunnels have poor fracture resistance and tensile properties during construction and use, resulting in the waterproof layer formed by the waterproof material being pulled and broken during the construction process, resulting in poor waterproof effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Efficient waterproof material for tunnels and preparation method thereof
  • Efficient waterproof material for tunnels and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Weigh 90 grams of paraffin, 2 grams of polyethylene, 15 grams of emulsifier and 5 grams of polyamide resin in turn; heat the paraffin until it melts, add emulsifier to mix and emulsify; pour polyethylene and polyamide resin into the emulsified paraffin , to obtain modified paraffin after mixing reaction for 0.5h;

[0030] Sequentially weigh 90 grams of rubber particles, 1 gram of graphene oxide, 5 grams of monosilane, and 5 grams of anionic surfactant; soak the rubber particles in sodium hydroxide solution for 1 hour, take them out, wash and dry them, and heat the rubber particles After melting, add anionic surfactant and mix for 0.5h, add graphene oxide and monosilane and mix for 0.5h to obtain modified rubber;

[0031] Weigh 100 grams of bamboo charcoal fiber and put it into a 13% sodium hydroxide solution to soak for 1 hour, then take out the bamboo charcoal fiber, dry it, add 5 grams of silane coupling agent, and react for 0.5 hours to obtain a coupling modified bam...

Embodiment 2

[0034] Weigh 90 grams of paraffin, 4 grams of polyethylene, 30 grams of emulsifier and 10 grams of polyamide resin in turn; heat the paraffin until it melts, add emulsifier to mix and emulsify; pour polyethylene and polyamide resin into the emulsified paraffin , to obtain modified paraffin after mixing reaction for 1h;

[0035] Sequentially weigh 90 grams of rubber particles, 3 grams of graphene oxide, 10 grams of disilane, and 8 grams of anionic surfactant; soak the rubber particles in sodium hydroxide solution for 3 hours, take them out, wash and dry them, and heat the rubber particles After melting, add an anionic surfactant and mix for 1 hour, add graphene oxide and disilane and mix and react for 1 hour to obtain a modified rubber;

[0036] Weigh 100 grams of bamboo charcoal fiber and put it into a 20% sodium hydroxide solution to soak for 2 hours, then take out the bamboo charcoal fiber, dry it, add 15 grams of silane coupling agent, and react for 1 hour to obtain a coupl...

Embodiment 3

[0039] Take by weighing 90 grams of paraffin, 3 grams of polyethylene, 22 grams of emulsifier and 7 grams of polyamide resin; obtain modified paraffin with the preparation method of Example 2;

[0040] Take by weighing 90 grams of rubber particles, 2 grams of graphene oxide, 7 grams of disilane, and 6 grams of anionic surfactant; obtain modified rubber with the preparation method of Example 2;

[0041] Weigh 100 grams of bamboo charcoal fiber and put it into a 16% sodium hydroxide solution for soaking for 1.5 hours, then take out the bamboo charcoal fiber, dry it, add 10 grams of silane coupling agent, and react for 0.75 hours to obtain a coupling modification charcoal fibre;

[0042] Weigh 50 grams of quartz stone powder, 10 grams of modified paraffin, 45 grams of modified rubber, 20 grams of polyvinyl chloride, 0.35 grams of antioxidant, 0.55 grams of tackifier, 7 grams of coupling modified bamboo charcoal fiber, polyacrylonitrile fiber 7 grams; Obtain waterproof material w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of waterproof materials, and provides an efficient waterproof material for tunnels and a preparation method thereof in order to solve the problem that an existing waterproof material is poor in fracture resistance and tensile property during construction. The efficient waterproof material for tunnels is prepared from the following components: filler, modified paraffin, modified rubber, polyvinyl chloride, an antioxidant, a tackifier, coupling modified bamboo charcoal fibers and polyacrylonitrile fibers. Modified rubber is further added into the filler, the modified rubber is firstly put into a sodium hydroxide solution to be soaked and passivated, then the passivated rubber reacts with an anionic surfactant, the surface of the rubber is modified through the anionic surfactant, the rubber can be in full contact with graphene oxide and a silicon-hydrogen compound, and the graphene oxide and the silicon-hydrogen compound are grafted on the surface of the rubber, so that the ductility and the strength of the rubber are improved.

Description

technical field [0001] The invention relates to the technical field of waterproof materials, in particular to a high-efficiency waterproof material for tunnels and a preparation method thereof. Background technique [0002] Waterproof material is the building envelope to prevent rainwater, snowwater and groundwater from penetrating into the building. It is a building material commonly used in tunnel construction and maintenance. There are many kinds of waterproof materials, including: asphalt waterproof materials, rubber and plastic waterproof materials, cement waterproof materials, and metal waterproof materials. Existing waterproof materials for tunnels have poor fracture resistance and tensile properties during construction and use, resulting in the waterproof layer formed by the waterproof materials being pulled and broken during construction, resulting in poor waterproof effects. Contents of the invention [0003] The object of the present invention is to solve the s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L21/00C08L91/06C08L23/06C08L77/00C08L27/06C08L33/20C08K9/06C08K9/02C08K7/06C08K3/04
CPCC08L21/00C08L2205/16C08L91/06C08L23/06C08L77/00C08L27/06C08L33/20C08K9/06C08K9/02C08K7/06C08K3/042
Inventor 庄前兵徐创才王国靖邵中冯浩杨武超靳崇刚
Owner CHINA FIRST HIGHWAY ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap