Multi-scale particle modified Al-Mg alloy welding wire and preparation method thereof

An alloy welding wire, multi-scale technology, applied in welding equipment, metal processing equipment, welding medium, etc., can solve problems such as welding hot cracks and insufficient weld strength

Pending Publication Date: 2021-09-14
JIANGXI UNIV OF SCI & TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of this program is to provide a multi-scale particle modified Al-Mg alloy welding wire and its preparation method to solve the problems of welding hot cracks and insufficient weld strength when welding high-strength and ultra-high-strength aluminum alloys

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multi-scale particle modified Al-Mg alloy welding wire and preparation method thereof
  • Multi-scale particle modified Al-Mg alloy welding wire and preparation method thereof
  • Multi-scale particle modified Al-Mg alloy welding wire and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1: Its preparation method of the Al-Mg alloy welding wire of a kind of multi-scale particle modification, comprises the following steps:

[0033] Step 1: Select material: Mg: 5.5%; Mn: 1.0%; Cr: 0.05%; Cu: 1.0%; TiB 2 : 0.5%; TiC: 3.5%; the rest is Al and unavoidable impurity elements;

[0034] Step 2: Preparation of TiB containing submicron 2 Aluminum master alloys of particles and nanoscale TiC particles;

[0035] Step 3: Add submicron TiB 2 Aluminum master alloys of particles and nanoscale TiC particles, Al-Cr, Al-Cu and other master alloys are smelted in a melting furnace with a temperature controlled at 800-820°C and protected by an inert gas. After complete melting, add Mg and stir well uniform, and then carry out the melt purification process of refining degassing and slag removal;

[0036] Step 4: The controlled alloy melt after melt purification is introduced into the tundish for heat preservation at 800-820°C, and injected into the continuous se...

Embodiment 2

[0038] Embodiment 2: Its preparation method of the Al-Mg alloy welding wire of a kind of multi-scale particle modification, comprises the following steps:

[0039] Step 1: Select material: Mg: 7.5%; Mn: 0.1%; Cr: 0.05%; Cu: 0; TiB 2 : 3.5%; TiC: 0.5%; the rest is Al and unavoidable impurity elements;

[0040] Step 2: Preparation of TiB containing submicron 2 Aluminum master alloys of particles and nanoscale TiC particles;

[0041] Step 3: Add submicron TiB 2 Aluminum master alloys and Al-Cr master alloys with particles and nanoscale TiC particles are melted in a melting furnace with a temperature controlled at 780°C and protected by an inert gas. After complete melting, Mg is added, fully stirred evenly, and then refined to remove Melt purification process for gas deslagging;

[0042] Step 4: The controlled alloy melt after melt purification is introduced into the tundish for heat preservation at 760-800°C, and injected into the continuous semi-solid rheological extruder a...

Embodiment 3

[0044] Embodiment 3: Its preparation method of the Al-Mg alloy welding wire of a kind of multi-scale particle modification, comprises the following steps:

[0045] Step 1: Select material: Mg: 6.5%; Mn: 0.3%; Cr: 0.1%; Cu: 0.5%; TiB 2 : 1%; TiC: 2.5%; the rest is Al and unavoidable impurity elements;

[0046] Step 2: Preparation of TiB containing submicron 2 Aluminum master alloys of particles and nanoscale TiC particles;

[0047] Step 3: Add submicron TiB 2 Aluminum master alloys of particles and nanoscale TiC particles, Al-Cr, Al-Cu and other master alloys are smelted in a melting furnace with a temperature controlled at 760-820°C and protected by an inert gas. After complete melting, add Mg and stir well uniform, and then carry out the melt purification process of refining degassing and slag removal;

[0048] Step 4: The controlled alloy melt after melt purification is introduced into the tundish for heat preservation at 780-820°C, and injected into the continuous semi-so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of metal material preparation, and particularly relates to a multi-scale particle modified Al-Mg alloy welding wire and a preparation method thereof. The multi-scale particle modified Al-Mg alloy welding wire comprises an alloy welding wire body, and the alloy welding wire body selects the following main element chemical components according to the particle content percentage: 5.5 to 7.5 percent of Mg, 0.05 to 0.5 percent of Mn, 0.05 to 0.2 percent of Cr, 0 to 1.0 percent of Cu, 0.5 to 3.5 percent of TiB2, 0.5 to 3.5 percent of TiC and the balance of Al and inevitable impurity elements. The Al-Mg alloy welding wire containing submicron TiB2 particles and nanoscale TiC particles prepared according to the method provided by the invention has the advantages that after the welding, a welding seam with a fine equiaxed grain structure and high welding seam strength can be obtained after welding; meanwhile, the extremely low welding crack sensitivity is achieved; and the Al-Mg alloy welding wire can be used for the welding of high-strength and ultrahigh-strength aluminum alloy structural parts.

Description

technical field [0001] The invention relates to the technical field of metal material preparation, in particular to an Al-Mg alloy welding wire modified by multi-scale particles and a preparation method thereof. Background technique [0002] Aluminum alloy has good electrical and thermal conductivity, high strength-to-mass ratio, corrosion resistance and damage resistance, and is widely used in aerospace, rail transit, automobiles, ships, pressure vessels, electronic appliances, furniture and many other fields , is one of the most widely used metal materials in industry. Inert gas shielded fusion welding (MIG welding and TIG welding) is a basic way to realize the connection of aluminum alloy structural materials, and it is also the most common connection method used in industrial aluminum alloy materials today. [0003] Ultra-high-strength aluminum alloys are copper-containing 7000-series aluminum alloys (Al-Zn-Mg-Cu alloys), which are one of the main structural materials i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K35/28B23K35/40C22C1/00C22C1/10C22C21/06C22C32/00
CPCB23K35/286B23K35/40C22C21/06C22C32/0047C22C1/1036C22C1/1073C22C1/12
Inventor 陈继强周子翔钟世标韩双文锋管仁国齐亮
Owner JIANGXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com