Polyester fiber containing wormwood component and wormwood fragrance and preparation method of polyester fiber

A polyester fiber and wormwood technology, applied in the field of textile fibers, can solve the problems of odor, non-mosquito, bacteria breeding, etc., and achieve the effect of not easy to survive, enhance antibacterial ability, and enrich functions

Inactive Publication Date: 2021-12-31
郑杰
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a polyester fiber containing wormwood components and wormwood fragrance and a preparation method thereof, which solves the problems of peculiar smell, lack of protection against mosquitoes and breeding of bacteria and mites

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The embodiment of the present invention provides a kind of polyester fiber containing wormwood component and wormwood fragrance, including the following materials in parts by weight: 8 parts of japonicus root, 6 parts of clove, 6 parts of dandelion, 8 parts of rhubarb, 6 parts of gardenia, 2 parts of coptis, 30 parts of wormwood, 5 parts of cellulase, 50 parts of polyester, 15 parts of lignan, 16 parts of nano-scale titanium dioxide and 25 parts of fiber-forming polymer.

[0030] A preparation method of polyester fibers containing wormwood ingredients and wormwood fragrance, comprising the following steps:

[0031] S1. Auxiliary material handling

[0032] ①. Spray and clean the root of the root, clove, dandelion, rhubarb, gardenia, coptis and half of the wormwood, and then put it in the heat preservation and drying room, and dry it in the environment with the temperature set at 65 ℃ Drying treatment for 2 hours, then lower the temperature to 35°C for 2 hours, then set ...

Embodiment 2

[0046] The embodiment of the present invention provides a kind of polyester fiber containing wormwood component and wormwood fragrance, including the following materials in parts by weight: 11 parts of japonicus root, 9 parts of clove, 9 parts of dandelion, 11 parts of rhubarb, 9 parts of gardenia, 3 parts of coptis, 35 parts of wormwood, 7 parts of cellulase, 55 parts of polyester, 18 parts of lignan, 19 parts of nano-scale titanium dioxide and 28 parts of fiber-forming polymer.

[0047] A preparation method of polyester fibers containing wormwood ingredients and wormwood fragrance, comprising the following steps:

[0048] S1. Auxiliary material handling

[0049] ①. Spray and clean the root of the root, clove, dandelion, rhubarb, gardenia, coptis and half of the wormwood, and then put it in the heat preservation and drying room, and dry it in the environment with the temperature set at 75 ℃ Dry for 3 hours, then lower the temperature to 40°C for 3 hours, then set the tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides polyester fiber containing a wormwood component and wormwood fragrance and a preparation method of the polyester fiber, and relates to the technical field of textile fibers. The polyester fiber containing the wormwood component and the wormwood fragrance is prepared from the following materials in parts by weight of 8 to 11 parts of radix stemonae, 6 to 9 parts of flos caryophylli, 6 to 9 parts of herba taraxaci, 8 to 11 parts of radix et rhizoma rhei, 6 to 9 parts of flos gardeniae, 2 to 3 parts of rhizoma coptidis, 30 to 35 parts of wormwood, 5 to 7 parts of cellulase, 50 to 55 parts of polyester, 15 to 18 parts of lignans, 16 to 19 parts of nanoscale titanium dioxide and 25 to 28 parts of fiber-forming polymer. By adding a wormwood powder mixture and a wormwood extract, the taste of an industrial additive is effectively removed, meanwhile, the wormwood has the mosquito-repelling and insect-preventing effects, and secondly, the fragrance generated by the wormwood acts on nasal mucosa, so that the content of immune globulin S (SlGA) secreted by antibodies on the nasal mucosa is increased; and the increase of the content enables virus not to survive easily on the nasal mucosa and the respiratory mucosa.

Description

technical field [0001] The invention relates to the technical field of textile fibers, in particular to a polyester fiber containing wormwood components and wormwood fragrance and a preparation method thereof. Background technique [0002] Polyester fiber, commonly known as "polyester", is a synthetic fiber obtained by spinning polyester obtained by polycondensation of organic dibasic acid and dibasic alcohol, referred to as PET fiber, which belongs to polymer compounds. It was invented in 1941 and is the current synthetic The largest variety of fiber, the biggest advantage of polyester fiber is that it has good wrinkle resistance and shape retention, high strength and elastic recovery ability, and it is durable, wrinkle-resistant, non-ironing, and non-sticky. [0003] Polyester fiber is deeply loved by consumers because of its strong and durable performance. However, among the existing polyester fibers at this stage, there is a problem of odor caused by the use of process a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/92D01F1/10
CPCD01F6/92D01F1/10D01F1/103
Inventor 郑建国郑杰
Owner 郑杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com