Method for regulating and promoting growth of desulfurized gypsum crystals by using carbide slag-based desulfurizer
A technology for desulfurization gypsum and desulfurizer, which is applied in the field of resource recycling technology, can solve the problems of insufficient quality control of desulfurization gypsum, complicated process methods, gypsum crystal structure and particle size, moisture content and the influence of the back-end utilization process, etc. The number of nuclear particles, the effect of reducing the agglomeration of small particles
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] A method for regulating and promoting the growth of gypsum crystals by a calcium carbide slag-based desulfurizer, comprising the following steps:
[0027] (1) Preparation of desulfurizer from carbide slag:
[0028] Carbide slag is pretreated to obtain a desulfurizer. After pretreatment, the calcium carbide slag product has a particle size of <105 μm, a particle ratio of 94.15%, a dry basis calcium oxide content of 72.05%, a Mg content of 0.3%, and a Si content of 0.8%;
[0029] (2) wet desulfurization:
[0030] The desulfurization slurry is prepared with a mass ratio of desulfurizer to water of 1:4, and the flue gas SO at the inlet of the desulfurization system 2 Concentration of 3500ppm, actual measurement of tail gas SO for 24 hours 2 The concentration is always lower than 20ppm, and polyethylene glycol with a desulfurizing agent mass of 0.005% is added to the desulfurization slurry. The appearance of the desulfurization gypsum is long rod, the particle size range i...
Embodiment 2
[0032] A method for regulating and promoting the growth of gypsum crystals by a calcium carbide slag-based desulfurizer, comprising the following steps:
[0033] (1) Preparation of desulfurizer from carbide slag:
[0034] Carbide slag is pretreated to obtain a desulfurizer. After pretreatment, the calcium carbide slag product has a particle size of <105 μm, a particle ratio of 91.08%, a dry basis calcium oxide content of 73.80%, a Mg content of 0.1%, and an Fe content of 0.5%;
[0035] (2) wet desulfurization:
[0036] The desulfurization slurry is prepared with a mass ratio of desulfurizer to water of 1:4, and the flue gas SO at the inlet of the desulfurization system 2 The concentration is 2600ppm, and the measured exhaust gas SO for 24 hours 2 The concentration is always lower than 15ppm, and 0.5% polyvinyl alcohol of the desulfurizing agent mass is added to the desulfurization slurry. The appearance of the desulfurization gypsum is thick and short rod, the particle size ...
Embodiment 3
[0038] A method for regulating and promoting the growth of gypsum crystals by a calcium carbide slag-based desulfurizer, comprising the following steps:
[0039] (1) Preparation of desulfurizer from carbide slag:
[0040] Carbide slag is pretreated to obtain a desulfurizer. After pretreatment, the calcium carbide slag product has a particle size of <105 μm, a particle ratio of 93.14%, a dry basis calcium oxide content of 74.32%, a Mg content of 0.4%, a Si content of 0.5%, and an Fe content of 0.1%;
[0041] (2) wet desulfurization:
[0042] The desulfurization slurry is prepared with a mass ratio of desulfurizer to water of 1:3, and the flue gas SO at the inlet of the desulfurization system 2 Concentration of 5000ppm, actual measurement of tail gas SO for 24 hours 2 The concentration is always lower than 25ppm. During the desulfurization process, 3.0% sodium polyacrylate is added as a desulfurizer. The appearance of the desulfurized gypsum is whisker-like, the particle size...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction