Preparation method of high-bearing low-temperature insensitive slow-rebound sponge

A slow-rebound sponge and high-load-bearing technology, which is applied in the field of preparation of high-load-bearing low-temperature insensitive slow-rebound sponge, can solve the problems of hard hand feeling and poor load-bearing performance of the sponge, and achieve soft hand feeling, excellent bearing capacity and reduced cost Effect

Active Publication Date: 2022-02-01
江苏钟山新材料有限公司
View PDF19 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The slow rebound sponge in the prior art generally has the problem of poor load

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-bearing low-temperature insensitive slow-rebound sponge

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Polyether polyol A: polyether polyol ZS-350G (purchased from Jiangsu Zhongshan New Material Co., Ltd.), polyoxypropylene oxide polyether triol, hydroxyl value: 30 (mgKOH / g), f( functionality)=3. Polyether polyol B: polyether polyol ZS-3160 (purchased from Jiangsu Zhongshan New Material Co., Ltd.), polyoxypropylene oxide polyether triol, hydroxyl value: 160 (mgKOH / g), f( functionality)=3. Polyether polyol C: polyether polyol C is ZS-8180 (purchased from Jiangsu Zhongshan New Material Co., Ltd.), polyoxypropylene oxide polyether tetraol, hydroxyl value: 180 (mgKOH / g), f = 4 (functionality). Polymer polyol D: Polymer polyol POP-720 (purchased from Jiangsu Zhongshan New Material Co., Ltd.), polyoxypropylene oxide polymer trihydric alcohol, hydroxyl value: 190 (mgKOH / g), solid content is 20%, f=3 (functionality).

[0018] A33 (commercially available) is a 33% triethylenediamine solution and is a tertiary amine catalyst. T12 (commercially available) is dibutyltin dilaura...

Embodiment 2

[0022] Add 45g polyether polyol A, 10g polyether polyol B, 40g polyether polyol C and 5g polyether polyol D into a 1L beaker, then add A33 (tertiary amine catalyst) 0.4g, T12 (organometallic Catalyst) 0.15g, LR-1085 (organic silicone oil) 0.35g and deionized water 3.5g, stirred for 30s and mixed evenly to obtain white material. Wherein polyether polyol A, polyether polyol B, polyether polyol C and polyether polyol D are the same as in Example 1.

[0023] Free foaming: Pour 40g of TDI (toluene diisocyanate) into the mixed white material, stir for 10 seconds under the mixer at a speed of 4000-5000r / min, pour the foamed liquid into the mold and fully foam until completely After aging (it takes 24 hours from foaming to full aging), it is cut to obtain a high-load low-temperature insensitive slow-rebound sponge. The rebound time of this high-load low-temperature insensitive slow-rebound sponge is about 5s, and it does not feel hard at a low temperature of -10°C to 10°C, that is, i...

Embodiment 3

[0025] Add 40g polyether polyol A, 10g polyether polyol B, 40g polyether polyol C and 10g polymer polyol D into a 1L beaker, then add A33 (tertiary amine catalyst) 0.3g, T12 (organometallic Catalyst) 0.1g, LR-1085 (organic silicone oil) 0.5g, deionized water 4g, stir for 30s and mix evenly to get white material. Wherein polyether polyol A, polyether polyol B, polyether polyol C and polyether polyol D are the same as in Example 1.

[0026] Free foaming: Pour 45g of TDI (toluene diisocyanate) into the mixed white material, stir for 10 seconds under the mixer at a speed of 4000-5000r / min, pour the foamed liquid into the mold and fully foam until completely After aging (it takes 24 hours from foaming to full aging), it is cut to obtain a high-load low-temperature insensitive slow-rebound sponge. The rebound time of this high-load low-temperature insensitive slow-rebound sponge is about 5s, and it does not feel hard at a low temperature of -10°C to 10°C, that is, it is not sensiti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of high-bearing low-temperature insensitive slow-rebound sponge, and belongs to the field of organic synthesis. The preparation method comprises the following steps: mixing polyether polyol A, polyether polyol B, polyether polyol C and polymer polyol D, adding a tertiary amine catalyst, an organic metal catalyst, organic silicone oil and water, and stirring to obtain a white material; pouring toluene diisocynate into the white material, stirring, foaming and curing to obtain the high-bearing low-temperature insensitive slow-rebound sponge. The hydroxyl value of the polyether polyol A is 25-40, and the functionality of the polyether polyol A is 2-4; the hydroxyl value of the polyether polyol B is 160 to 200, and the functionality of the polyether polyol B is 3 to 4.5; the hydroxyl value of the polyether polyol C is 140 to 180, and the functionality of the polyether polyol C is 2 to 4; and the hydroxyl value of the polymer polyol D is 170-200, and the functionality of the polymer polyol D is 2-4. The sponge prepared by the method disclosed by the invention has better bearing performance, and the hand feeling is not hardened under a low-temperature condition, namely, the sponge is insensitive to low temperature.

Description

technical field [0001] The invention relates to a preparation method of a high-load low-temperature insensitive slow-rebound sponge. Background technique [0002] Slow-rebound sponge is also called inert sponge, memory foam, low-rebound sponge, slow-rebound cotton, and zero-pressure sponge. Due to the unique pressure relief characteristics of slow-rebound sponge, slow-rebound pillows and mattresses can keep the body in a natural Get rest in a stress-free position. The slow-rebound sponge in the prior art generally has the problem of poor load-bearing performance, and the sponge feels hard under low temperature conditions. Contents of the invention [0003] The purpose of the present invention is to provide a preparation method of a high-load-bearing low-temperature insensitive slow-rebound sponge. The sponge prepared by the method has good load-bearing performance and does not feel hard under low temperature conditions, that is, it is not sensitive to low temperature. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G18/48C08G101/00
CPCC08G18/4837C08G18/4816C08G2101/00C08G2110/0083C08G2110/005
Inventor 张丽君宗红亮陆逸峰李月文吴亚清俞绿绿
Owner 江苏钟山新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap