Nanogold antibacterial agent as well as preparation method and application thereof
A technology of antibacterial agent and nano gold, which is applied in the direction of nanotechnology, nanomedicine, nanotechnology, etc., can solve the problems of inability to have antibacterial effect against Gram-positive bacteria and Gram-negative bacteria at the same time, and poor antibacterial effect, and achieve Excellent antibacterial effect and simple preparation process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0077] A preparation method of nano gold antibacterial agent, comprising the steps of:
[0078] S1. In the chloroauric acid solution with a mass concentration of 12%, add a sodium borohydride solution with a mass concentration of 2% to obtain a mixed solution A, and feed nitrogen into it;
[0079] S2. Continue to add the ethylene glycol solution whose volume fraction is 6% to the above mixed solution A to obtain the mixed solution B;
[0080] S3. In mixed solution B, add the dimethyl diallyl ammonium chloride of 0.6% total solution fraction to obtain mixed solution C;
[0081] S4. Add 0.4% 4-mercaptobenzoic acid in the total volume fraction of the solution to the mixed solution C, under a nitrogen atmosphere, the reaction temperature is 2°C, the stirring rate is 50rpm / min, and the nitrogen rate is 35mL / min, and the reaction time is 3h to obtain nano Gold antimicrobial.
Embodiment 2
[0083] A preparation method of nano gold antibacterial agent, comprising the steps of:
[0084] S1. In the chloroauric acid solution with a mass concentration of 15%, add a sodium borohydride solution with a mass concentration of 4% to obtain a mixed solution A, and feed nitrogen into it;
[0085] S2. Continue to add the ethylene glycol solution whose volume fraction is 8% to the above mixed solution A to obtain the mixed solution B;
[0086] S3. In mixed solution B, add the dimethyl diallyl ammonium chloride of 1.2% total solution fraction to obtain mixed solution C;
[0087] S4. Add 1.5% of the total volume fraction of 3-mercapto-2-pentanone in the mixed solution C, under nitrogen atmosphere, the reaction temperature is 4°C, the stirring rate is 100rpm / min, the nitrogen rate is 35mL / min, and the reaction time is 5h , to obtain nano gold antibacterial agent.
Embodiment 3
[0089] A preparation method of nano gold antibacterial agent, comprising the steps of:
[0090] S1. In the chloroauric acid solution with a mass concentration of 20%, add a sodium borohydride solution with a mass concentration of 6% to obtain a mixed solution A, and feed nitrogen into it;
[0091] S2. Continue to add the ethylene glycol solution whose volume fraction is 10% to the above mixed solution A to obtain the mixed solution B;
[0092] S3. In the mixed solution B, add 1.7% cetyltrimethylammonium bromide of the total solution fraction to obtain the mixed solution C;
[0093] S4. Add 1.2% 3-mercaptopropionic acid in the total volume fraction of the solution to the mixed solution C, under a nitrogen atmosphere, the reaction temperature is 8°C, the stirring rate is 200rpm / min, and the nitrogen rate is 35mL / min, and the reaction time is 6h to obtain nano Gold antimicrobial.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap