High-thermal-conductivity silicone rubber cable material as well as preparation method and application thereof

A silicone rubber, high thermal conductivity technology, applied in rubber insulators, organic insulators, etc., can solve the problem of the thermal conductivity of cable materials needs to be improved, to improve flame retardant properties and mechanical properties, improve thermal conductivity, and reduce cable damage. Effect

Pending Publication Date: 2022-03-22
JIANGSU DASHENG POLYMER
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although the above-mentioned materials have obtained cable materials with excellent performance, they still cannot meet the double-sta

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-thermal-conductivity silicone rubber cable material as well as preparation method and application thereof
  • High-thermal-conductivity silicone rubber cable material as well as preparation method and application thereof
  • High-thermal-conductivity silicone rubber cable material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0052] Example 1

[0053] A high thermal conductivity silicone rubber cable material, which comprises the following components according to parts by weight:

[0054]

[0055] Its preparation method comprises the following steps:

[0056] (1) methyl vinyl silicone rubber, magnesium hydroxide, aluminum hydroxide, polydopamine-modified graphene (mix dopamine and graphene with a mass ratio of 1:1 in deionized water at 50° C. for 2 hours to obtain the Polydopamine modified graphene), boron nitride, compatibilizer, stabilizer, silicone masterbatch, silane coupling agent and antioxidant were mixed at 160°C for 25min, and then pelletized by a single-screw extruder. The single-screw extruder includes the first zone, the second zone, the third zone, the fourth zone, the fifth zone, the sixth zone and the seventh zone. The material passes through each zone in sequence, and the working temperature of the first zone is set as 110℃, the working temperature of the second zone is 115℃, t...

Example Embodiment

[0058] Example 2

[0059] A high thermal conductivity silicone rubber cable material, which comprises the following components according to parts by weight:

[0060]

[0061]

[0062] The preparation method of the high thermal conductivity silicone rubber cable material provided in this embodiment is the same as that of the high thermal conductivity silicone rubber cable material provided in Example 1.

Example Embodiment

[0063] Example 3

[0064] A high thermal conductivity silicone rubber cable material, which comprises the following components according to parts by weight:

[0065]

[0066] The preparation method of the high thermal conductivity silicone rubber cable material provided in this embodiment is the same as that of the high thermal conductivity silicone rubber cable material provided in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Thermal conductivityaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-thermal-conductivity silicone rubber cable material and a preparation method and application thereof, and the high-thermal-conductivity silicone rubber cable material comprises specific parts of silicone rubber, a flame retardant, polydopamine modified graphene, boron nitride, silicone master batch and a silane coupling agent. According to the high-thermal-conductivity silicone rubber cable material, a combination of specific parts of boron nitride and polydopamine modified graphene is selected as a thermal conductive filler, and the boron nitride and the polydopamine modified graphene are matched in a silicone rubber matrix to form a complete thermal conductive network, so that the obtained cable material has excellent thermal conductivity; meanwhile, specific parts of the flame retardant and the silane coupling agent are also added, so that the flame retardant property and the mechanical property of the cable material are effectively improved, and the high-thermal-conductivity silicone rubber cable material meeting the dual standards of IEC62930 and UL4703 is finally obtained.

Description

technical field [0001] The invention belongs to the technical field of cable materials, and in particular relates to a high thermal conductivity silicon rubber cable material and a preparation method and application thereof. Background technique [0002] In recent years, with the development of society, the application occasions of wires and cables have become more and more extensive. At the same time, the requirements for flame retardancy, mechanical properties, electrical properties and environmental protection of wires and cables have also gradually increased. As a substitute for halogen-containing flame-retardant cable materials, low-smoke halogen-free cable materials have a wider range of applications and are more environmentally friendly, but their flame-retardant and mechanical properties face greater challenges. In the use of general low-smoke halogen-free polyolefin cable materials, due to the low melting point of polyolefins, wires and cables cannot be used at high...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/07C08K3/38C08K9/04C08K3/04C08K3/22C08K5/544H01B3/28
CPCC08L83/04H01B3/28C08L2203/202C08L2201/08C08L2201/02C08K2003/385C08K2003/2227C08K2003/2224C08K3/38C08K9/08C08K3/042C08K3/22C08K5/544
Inventor 潘卫东范魏魏郑建
Owner JIANGSU DASHENG POLYMER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap