Molandy green zirconia ceramic and preparation method thereof
A zirconia ceramic, Morandi's technology, applied in the field of ceramics, can solve problems such as zirconia ceramics that are difficult to meet, and achieve the effects of excellent mechanical properties, high production efficiency, and uniform color distribution
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0024] The invention provides a method for preparing Morandi green zirconia ceramics, comprising the following steps:
[0025] 1) ball milling zirconia, nickel titanate, neodymium zirconate and ball milling media to obtain ball milling slurry;
[0026] 2) Drying, grinding, sieving and molding the ball mill slurry in sequence to obtain a ceramic green body;
[0027] 3) Sintering the ceramic green body to obtain Morandi green zirconia ceramics.
[0028] In the present invention, the zirconia in step 1) is yttria-stabilized zirconia powder, and the molar ratio of yttrium oxide to yttria-stabilized zirconia powder is 2.5 to 3.5:100, preferably 3:100; The purity of zirconium powder is 90-99.9%, preferably 93-99.9%, more preferably 95-99.9%.
[0029] In the present invention, the mass ratio of zirconium oxide, nickel titanate and neodymium zirconate in step 1) is 950~990:5~40:5~40, preferably 960~980:10~35:10~35, further Preferably it is 965-975: 20-25: 20-25, and more preferably...
Embodiment 1
[0041] Mix 950g of yttria-stabilized zirconia powder with a purity of 92% and 3mol% yttrium oxide, 10g of nickel titanate, 40g of neodymium zirconate and 1000g of absolute ethanol, and use zirconia balls as grinding balls in a planetary ball mill. The material ratio was 1.6:1, ball milled for 28 hours under the condition of rotating speed of 400r / min, and a slurry with a particle size of 160μm was obtained.
[0042] The slurry was dried at 80°C for 12 hours, then ground through an 80-mesh standard sieve, dry-pressed under a pressure of 4 MPa for 60 s, and then cold isostatically pressed under a pressure of 200 MPa for 80 s to obtain a ceramic body.
[0043] The ceramic body was sintered at 1450°C for 2 hours to obtain Morandi green zirconia ceramics.
Embodiment 2
[0045] Mix 950g of yttria-stabilized zirconia powder with a purity of 90% and 2.5mol% yttrium oxide, 40g of nickel titanate, 10g of neodymium zirconate and 2000g of absolute ethanol, and use zirconia balls as grinding balls in a planetary ball mill. The ball-to-material ratio was 2.4:1, and ball milling was performed for 26 hours at a rotational speed of 420 r / min to obtain a slurry with a particle size of 175 μm.
[0046] The slurry was dried at 85°C for 10 h, then ground through an 80-mesh standard sieve, dry-pressed at 12 MPa for 50 s, and then cold isostatically pressed at 240 MPa for 50 s to obtain a ceramic body.
[0047] The ceramic body was sintered at 1480°C for 3 hours to obtain Morandi green zirconia ceramics.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
luminance | aaaaa | aaaaa |
hardness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap