Production process of transparent glass mirror with stereo pattern

A production method and a pattern technology, which are applied in the fields of technology for producing decorative surface effects, decorative art, special decorative structures, etc., can solve the problems of losing the value of mirror plating, lack of three-dimensional sense and layering, and achieve strong three-dimensional sense, The effect of strong artistic value

Inactive Publication Date: 2004-12-29
上海恒昊玻璃技术有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, patterned glass mirrors are mainly plated with embossed glass, but its pattern and glass are all silvery white, without three-dimensional and layered effects. The glass-coated mirror also has a frosted effect on the mirror surface, no mirror reflection effect, and loses the value of the mirror-coated mirror.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The production method of mirror plated with light-transmitting three-dimensional pattern glass is to carry out according to the following method steps:

[0019] (1) Clean the transparent flat glass, and after drying, print the pattern on the glass with a pre-designed screen. The printing ink is anti-corrosion ink, and then dry it.

[0020] (2) Cover the back of the flat glass with the pattern printed on it after drying with an anti-corrosion material, and then emulsify on one side.

[0021] (3) After cleaning the flat glass processed in step (2) (retaining the ink pattern), put it into a corrosion box filled with corrosive liquid and soak for 10 minutes. The composition and weight ratio of the corrosive liquid are prepared, 65 parts of water, sulfuric acid 5 parts, 21 parts of hydrofluoric acid.

[0022] (4) Rinse the flat glass treated in step (3) with water to remove the ink and the covering material on the back of the glass.

[0023] (5) Rinse the flat glass treate...

Embodiment 2

[0029] The production method of light-transmitting three-dimensional pattern glass is to carry out according to the following method steps:

[0030] (1) Clean the transparent flat glass, and after drying, print the pattern on the glass with a pre-designed screen. The printing ink is anti-corrosion ink, and then dry it.

[0031] (2) After drying, the back of the plate glass with the printed pattern is covered with anti-corrosion material and then emulsified.

[0032] (3) After cleaning the flat glass processed in step 2 (retaining the ink pattern), put it into a corrosion box filled with corrosive solution and soak for 15 minutes. The composition and weight ratio of the corrosive solution are prepared, 67 parts of water, 8 parts of sulfuric acid, 25 parts of hydrofluoric acid.

[0033] (4) Rinse the flat glass treated in step 3 with water to remove the ink and anti-corrosion material on the back of the glass.

[0034] (5) Rinse the flat glass processed by step 4 with water, d...

Embodiment 3

[0040] The production method of light-transmitting three-dimensional pattern glass is to carry out according to the following steps:

[0041] (1) After cleaning the transparent flat glass and drying it, use a pre-designed screen to print the pattern on the glass. The printing ink is anti-corrosion ink, and then dry it.

[0042] (2) After drying, the back of the flat glass with the printed pattern is covered with anti-corrosion material and then emulsified on one side

[0043] (3) After cleaning the flat glass processed in step (2) (retaining the ink pattern), put it into a corrosion tank filled with corrosive liquid and soak for 20 minutes. The composition and weight ratio of the corrosive liquid are prepared: 72 parts of water, 10 parts of sulfuric acid , 26 parts of hydrofluoric acid.

[0044] (4) Rinse the flat glass treated in step (3) with water to remove the ink and anti-corrosion material on the back of the glass.

[0045] (5) Rinse the flat glass treated in step (4) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heightaaaaaaaaaa
Login to View More

Abstract

The production process of glass mirror with stereo pattern includes cleaning of glass plate, printing pattern on one side of the glass plate with anticorrosive ink and covering the other side with anticorrosive material, emulsifying the pattern side, soaking the glass plate in erosion liquid for 10-20 min, water washing, eliminating the ink and covering material to form transparent with stereo pattern, plating silver, aluminum or copper chemically to form mirror, drying, spraying with paint and washing to produce the mirror with stereo pattern. The product is novel and artistic and may be used in decorating built-in cupboard, furniture, sliding door, etc.

Description

Technical field: [0001] The invention belongs to the technical field of glass deep processing, and in particular relates to a production method for producing light-transmitting three-dimensional pattern glass by chemical acid etching and then mirror-coating. The produced glass patterns are silvery and dotted with each other. Background technique: [0002] At present, patterned glass mirrors are mainly plated with embossed glass, but its pattern and glass are all silvery white, without three-dimensional and layered effects. The glass-plated mirror also has a frosted effect on the mirror surface, without mirror reflection effect, and loses the value of the plated mirror. Invention content: [0003] The purpose of the present invention is to overcome the above-mentioned fly in the ointment, and provide a kind of screen pattern printing technology on white glass with strong corrosion-resistant ink as protection and then chemical etching to make light-transmitting three-dimensi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B44C1/22B44C5/08C03C15/00
Inventor 熊国祥李金钟
Owner 上海恒昊玻璃技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com