Ablative material of resin of phenolic cyanate

A technology of phenolic cyanate ester and ablation material, applied in the field of high temperature resistant ablation material, can solve the problems of high melt viscosity, high heteroatom content, low carbon content and the like

Inactive Publication Date: 2006-06-14
北京玻钢院复合材料有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The phenolic novolak cyanate resin system modified by fused ring phenol used as ablative resin has been described in US Patents 4,831,086 and 4,981,994. Esterification, and since it is necessary to use higher molecular weight novolac phenolic formaldehyde as the main structure to achieve a higher carbon residue rate, this will lead to a higher melt viscosity at 100 ° C, and although the novolac cyanate has a higher The glass transition temperature and thermal decomposition temperature, but the heteroatom content is high, the carbon content is low, and it has certain limitations in materials that need to obtain a high carbon residue rate.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ablative material of resin of phenolic cyanate
  • Ablative material of resin of phenolic cyanate
  • Ablative material of resin of phenolic cyanate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Example 1: Synthesis of novolac cyanate

[0027] The 37% aqueous solution of phenol and formaldehyde and the molar ratio of oxalic acid are 1:0.9:0.005, put into a three-necked flask equipped with a reflux condenser, react at 80~100℃ for 3~5 hours, wash with water and vacuum to obtain the softening point Novolac and novolac are dissolved in a mixed solvent of dichloromethane and ethyl acetate at 40~60℃, put into a four-neck flask with BrCN, dropwise add triethylamine, phenolic hydroxyl group, BrCN and triethylamine The molar ratio of is 1:1.05:1.10, the reaction is conducted at -15°C to -5°C for 5 hours, the salt and the solvent are separated, and the purification process is performed to obtain the novolac cyanate. In this case, n=2~5, m=0.

[0028] 1-2: Using the same method as 1-1, change the phenol to p-phenylphenol to obtain the novolac cyanate. In this case, n=2~5, m=0.

[0029] 1-3: Using the same method as 1-1, change the phenol to o-phenylphenol to obtain the novola...

Embodiment 2

[0030] 1-4: Reacting phenol and p-phenylphenol with benzaldehyde and p-toluenesulfonic acid at a molar ratio of 1:1:1.5:0.01, and then using the same method as 1-1 to obtain novolac cyanate. In this case, n=2~5, m=0. Example 2: Synthesis of linear fused ring phenol cyanate

[0031] 2-1: 1-Naphthol and formaldehyde 37% aqueous solution and oxalic acid molar ratio 1:0.80:0.005, put into a three-necked flask equipped with reflux condenser, in the presence of ketone solvent, at 60-100 ℃ React for 3 to 5 hours, wash with water, and vacuum to obtain a linear fused-ring phenol phenol with a softening point of 40-60°C. The linear fused-ring phenolic aldehyde is dissolved in dichloromethane solvent, put into a four-necked flask with BrCN, and triethylamine is added dropwise. The molar ratio of phenolic hydroxyl group to BrCN and triethylamine is 1:1.05:1.10, at -15℃~ React at -5°C for 5 hours, separate the salt and solvent, and perform purification treatment to obtain linear fused-ring phe...

Embodiment 3

[0034] Example 3: Synthesis of copolymerized phenolic cyanate

[0035] 3-1: A 37% aqueous solution of phenol, naphthol (molar ratio 1:1) and formaldehyde, and oxalic acid in a phenol, aldehyde, acid molar ratio of 1:0.9:0.005, put them into a three-necked flask equipped with a reflux condenser, React at 80~100℃ for 3~5 hours, wash with water and vacuum to obtain copolymerized phenolic aldehyde. The copolymerized phenolic aldehyde is dissolved in acetone solvent and put into a four-necked flask together with BrCN. Triethylamine, phenolic hydroxyl and BrCN are added dropwise. The molar ratio of the triethylamine is 1:1.05:1.10, and the reaction is carried out at -15°C to -5°C for 5 hours, the salt and the solvent are separated, and the purification treatment is performed to obtain the copolymerized phenol aldehyde cyanate. In this case, n:m=1:1.

[0036] 3-2: Change the molar ratio of phenol and naphthol to 1:2, and obtain the copolymerized phenol cyanate in the same way as benzalde...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a phenolic cyanate resin ablation material, which is composed of a blend obtained by blending a linear phenolic cyanate resin and a linear condensed ring phenolic cyanate resin and a reinforcing material. The blended phenolic cyanate can simultaneously meet the characteristics of high carbon residue rate (>60%), high heat resistance temperature (>350°C), low melt viscosity, low curing weight loss rate, long gel time, etc., and can meet Ablation performance requirements for high carbon residue rate and injection process requirements.

Description

[0001] This application is a division of the patent application with the filing date of July 8, 2003 and the application number of 03146583.8. Technical field [0002] The invention relates to a high-temperature ablation resistant material suitable for injection molding. The material is mixed with a reinforcing material that has a low melt viscosity, no small molecules released during curing, and a higher heat-resistant temperature and carbon residue rate. to make. Background of the invention [0003] At present, the only mature ablative resin is thermosetting phenolic resin, but because its curing system is a condensation polymerization system, a large amount of small molecules are released during curing, and because of its high viscosity, it must be dissolved in an inert solvent such as ethanol before it can be used. Therefore, the ablation resin of this system is suitable for the current mature molding and winding processes, and is not suitable for the injection molding process...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L61/14C08G8/28
Inventor 冯青平薛忠民陈淳胡平
Owner 北京玻钢院复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap