Ink paint

A coating and ink technology, applied in the coating field, can solve the problems of poor adhesion of the printing carrier, transfer printing, scratch resistance, poor cooking resistance, etc., and achieve the effects of good adhesion, high transfer rate and wide adaptability

Inactive Publication Date: 2005-04-27
张迪
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The ink coating of the carbon ribbons currently on the market cannot be completely transferred to the printing carrier after being scalded at an appropriate temperature. The ink layer has poor adhesion to the printing carrier, and its scratch resistance and cooking resistance are relatively poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 2

[0007] Example 2: The polyamide resin of this embodiment selects the P-1155 of Lauter Company, the modified rosin resin can adopt 210 of Suichuan resin, the polyethylene wax can select BASF's LumaxAL3 for use, and the filler can select superfine calcium carbonate and lithopone for use , Pigment is carbon black and selects Cabot company Cabet800, and dispersant selects BYK K-163 for use, and leveling agent selects the product of Dow Corning Company for use, code 5T, and solvent is xylene 60% by weight percentage, isopropanol 40%. Prepare materials according to the following formula, first heat and dissolve the resin in the solvent, then add other components in sequence, and use a grinder to disperse the system evenly, and the particle size should be below 10 μm.

[0008] polyamide resin

[0009] polyamide resin

Embodiment 4

[0010] Embodiment 4: the polyamide resin of this embodiment selects the P-1155 of Lauter Company, the modified rosin resin can adopt the 210 of Suichuan resin, the polyethylene wax can select BASF's LumaxAL3 for use, and the filler can select superfine calcium carbonate and Lide for use Powder, pigment is carbon black and selects Cabot Company Cabet800 for use, dispersant selects BYK K-163 for use, leveling agent selects the product of Dow Corning Company for use, code 5T, and solvent is xylene 70% by weight percentage, isopropanol 30% . According to the following formula, heat and dissolve the resin in the solvent first, then add other components in order, and use a grinder to disperse the system evenly, and the particle size should be below 10 μm.

[0011] polyamide resin

[0012] polyamide resin

[0013] polyamide resin

[0014] polyamide resin

[0015] polyamide resin

Embodiment 9

[0016] Embodiment 9: the polyamide resin of this embodiment selects the P-1155 of Lauter Company, the modified rosin resin can adopt the 210 of Suichuan resin, the polyethylene wax can select BASF's LumaxAL3, and the filler can select superfine calcium carbonate and Lide The powder and pigment, i.e. carbon black, are selected from Cabot Company Cabet800, the dispersant is selected from BYK K-163, the leveling agent is selected from the product of Dow Corning Company, code 5T, and the solvent is 60% xylene and 40% isopropanol by weight. Prepare materials according to the following formula, first heat and dissolve the resin in the solvent, then add other components in sequence, and use a grinder to disperse the system evenly, and the particle size should be below 10 μm. According to the following formula, heat and dissolve the resin in the solvent first, then add other components in order, and use a grinder to disperse the system evenly, and the particle size should be below 10 μ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to view more

Abstract

The present invention discloses one kind of ink paint, which, when heated, may be transferred to the print carrier completely, and has wide print carrier adaptability, great attachment, high scrape and boiling resistance, and no adhesion. The ink paint consists of polyamide resin, modified rosin resin, polyethylene wax, stuffing, pigment, dispersant, leveling agent and solvent. The present invention is used mainly in producing mark belt.

Description

technical field [0001] The invention relates to a coating, more specifically to a coating for marking carbon ribbons. Background technique [0002] The ink coating of the carbon ribbons currently on the market cannot be completely transferred to the printing carrier after being scalded at an appropriate temperature. The ink layer has poor adhesion to the printing carrier, and its scratch resistance and cooking resistance are relatively poor. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies in the prior art, and provide an ink layer with good hot stamping performance, high transfer rate, wide temperature adaptability, suitable for substrates such as PP, PE, PVC, aluminum foil, paper chemical fiber, etc. It has good adhesion, abrasion resistance, cooking resistance, and has a good combination with the auxiliary coating for the marking carbon ribbon coating. [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/102
Inventor 张迪
Owner 张迪
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap