Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

Method for measuring deuteration rate of single crystal of potassium dideuterium phosphate

A technology of potassium dideuterium phosphate single crystal and deuteration rate, applied in the direction of removing certain components and weighing, can solve the problems of difficult to determine whether the crystal decomposition is complete, the deuteration rate is inaccurate, the method is cumbersome, etc. The effect of easy promotion and use, economic promotion and use, and simple method

Inactive Publication Date: 2006-02-01
FUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But this method is very cumbersome, and the test crystal sample must have two smooth crystal planes parallel to each other
Yu Shuqin and others reported on the 1986 Volume 15, No. 2 issue of "Journal of Synthetic Crystals" that the deuteration rate of DKDP crystals was determined by gravimetric method. 4 grams of DKDP bulk crystals in a platinum crucible are kept at 400°C for half an hour. It is difficult to determine whether the crystals are completely decomposed, and the residual KPO after heating and decomposition 3 Because it is easy to absorb moisture, it is difficult to weigh the weight on the electronic balance to a constant weight, and the measured deuteration rate is inaccurate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for measuring deuteration rate of single crystal of potassium dideuterium phosphate
  • Method for measuring deuteration rate of single crystal of potassium dideuterium phosphate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0013] Example: Put a pair of covered platinum crucibles on a NETZSCH STA449C thermogravimetric analyzer, close the covers, weigh until constant weight, and reset to zero. Put the DKDP crystal sample in the front platinum crucible, close the cover and weigh to constant weight, the reading is 23.9672mg, and then perform the measurement parameters (measurement type, operator, sample number, name, sample quality, heating program, temperature correction , sensitivity correction, etc.) setting, the temperature rise program is that the initial temperature is 30°C, slowly heated to 260°C at a rate of 5°C / min, and then kept at a constant temperature for 1 hour, then slowly heated at a rate of 5°C / min to 450°C, and then kept at a constant temperature for 1 hour Hour. Click "Initialize Working Conditions" to initialize the experimental temperature program first, and then click "Start" to conduct experimental measurements. The real-time curve during the experimental measurement process ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method for measuring single crystal deuterating rate of dideuteropotassium phosphate includes applying NETZSCHSTA 449 c thermogravimeter ; setting temperature up rising program as staring from 30 deg.c , heating up to 260 deg.c with speed rate of 5 deg.c / min and holding constant temperature for one hour , then heating up to 450 deg.c with speed rate of 5 deg.c / min and holding constant temperature for one hour to obtain a thermogravimetric curve ; calculating out weight loss rate from said curve and substituting it into formula of x ( % ) = [ ( x / 1 ¿C x ) x 58.648 ¿C 8.948 ] x 100 for deriving out deuterating rate of DKDP crystal sample .

Description

technical field [0001] The present invention relates to diduterium potassium phosphate (K(D X h 1-X ) 2 PO 4 , referred to as DKDP) simple method of measuring the deuteration rate of single crystal. Background technique [0002] The tetragonal potassium dihydrogen phosphate crystal with high deuteration rate is a kind of electro-optic modulation crystal widely used in laser technology. The electro-optic and nonlinear optical properties of DKDP crystals are directly proportional to its deuteration rate, so accurate measurement of the deuteration rate of tetragonal DKDP crystals plays a decisive role in DKDP crystals as optical modulators, optical frequency converters and other optical devices. role. [0003] It is well known that the deuteration rate of DKDP crystals is usually lower than that in its growth solution, so it cannot be equated to the deuteration rate of DKDP single crystal simply by measuring the deuteration rate in the growth solution, but it should be mea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N5/04
Inventor 李国辉苏根博庄欣欣李征东贺友平
Owner FUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More