Fluorocopolymer and its applications
A technology of copolymer and tetrafluoroethylene, applied in coating, layered products, transportation and packaging, etc., can solve problems such as insufficient copolymerization ability, and achieve good interlayer adhesion performance, good heat resistance, and good fuel shielding performance effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0066] Example 1
[0067] Remove the air in a 1.2-liter polymerization autoclave equipped with a stirrer, and then add 1131 g of 1,3-dichloro-1,1,2,2,3-pentafluoropropane (manufactured by Asahi Glass Co., Ltd., below Called AK225cb) and 120.1 grams of CF 2 =CFO(CF 2 ) 3 F. Then the inside of the polymerization autoclave was heated to 50°C, 73 g of TFE was added, and the pressure was increased to 0.43 MPa / G. One cubic centimeter of AK225cb solution containing 0.1% by mass (perfluorobutyryl) peroxide was added as a polymerization initiator solution to initiate polymerization, and thereafter 1 cubic centimeter of this polymerization initiator solution was added every 10 minutes. In addition, TFE was continuously added to maintain the pressure at 0.43 MPa / G during the polymerization process. In addition, the AK225cb solution containing 0.3% by mass of NAH was continuously added in an amount equal to 0.1 mol% of the molar amount of TFE added during the polymerization process. Five hour...
Example Embodiment
[0071] Example 2
[0072] The air in the polymerization autoclave used in Example 1 was removed, and then 500AK225cb, 600 g of HFP and 50 g of TFE were added, and the inside of the polymerization autoclave was heated to 50°C. The pressure becomes 0.98 MPa / G. One cubic centimeter of AK225cb solution containing 0.25% by mass of bis(perfluorobutyryl) peroxide was added as a polymerization initiator solution to initiate polymerization, and thereafter 1 cubic centimeter of this polymerization initiator solution was added every 10 minutes. In addition, TFE was continuously added to maintain the pressure at 0.98 MPa / G during the polymerization process. In addition, the AK225cb solution containing 0.3% by mass of NAH was continuously added, and the addition amount was equal to 0.1 mol% of the continuously added TFE molar amount. 4 hours and 20 minutes after the initiation of the polymerization, 50 g of TFE had been added at this time, the temperature in the polymerization autoclave was lo...
Example Embodiment
[0076] Example 3
[0077] Remove the air in the polymerization autoclave used in Example 1, and then add 500AK225cb, 600g HFP, 25g CF 2 =CFO(CF 2 ) 3 F and 50 g of TFE, and heated the inside of the polymerization autoclave to 50°C. The pressure becomes 0.96 MPa / G. One cubic centimeter of AK225cb solution containing 0.25% by mass of bis(perfluorobutyryl) peroxide was added as a polymerization initiator solution to initiate polymerization, and thereafter 1 cubic centimeter of this polymerization initiator solution was added every 10 minutes. The TFE is continuously added to maintain the pressure at 0.96 MPa / G during the polymerization process. In addition, the AK225cb solution containing 0.3% by mass of NAH was continuously added, and the addition amount was equal to 0.1 mol% of the continuously added TFE molar amount. 4 hours and 40 minutes after the initiation of the polymerization, 50 g of TFE had been added at this time, the temperature in the polymerization autoclave was lowere...
PUM
Property | Measurement | Unit |
---|---|---|
Melting point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap