Aluminium-scandium alloy standard spectrum sample and preparation method thereof

A technology of spectral standard samples and alloys, which is applied in the preparation of test samples, measurement of color/spectral characteristics, etc., and can solve problems such as inability to prepare

Inactive Publication Date: 2006-09-27
SOUTHWEST ALUMINUM GRP
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The object of the present invention is to provide a standard sample of aluminum-scandium alloy spectrum to solve the analysis and control problems in the production of 5A70 and 5A71 series aluminum alloy products
[0

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminium-scandium alloy standard spectrum sample and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The aluminum-scandium alloy spectral standard sample with the standard sample number E5101 contains all elements in the following weight percentages in pure aluminum: Si 0.25, Fe 0.35, Cu 0.01, Mn 1.10, Mg 4.8, Cr 0.24, Ni 0.011, Zn0. 10. Sc 0.04, Ti 0.01, Zr 0.03, Be 0.0001, B 0.001.

Embodiment 2

[0028] The aluminum-scandium alloy spectral standard sample with the standard sample number E5102 contains all elements in the following weight percentages in pure aluminum: Si 0.20, Fe 0.25, Cu 0.05, Mn 0.90, Mg 6.0, Cr 0.10, Ni 0.015, Zn0. 03. Sc 0.10, Ti 0.05, Zr 0.15, Be 0.001, B 0.002.

Embodiment 3

[0030] The aluminum scandium alloy spectral standard sample with the standard number E5103 contains all elements in the following weight percentages in pure aluminum: Si 0.015, Fe 0.20, Cu 0.03, Mn 0.45, Mg 5.5, Cr 0.02, Ni 0.009, Zn 0.05 , Sc 0.16, Ti 0.03, Zr 0.10, Be 0.003, B 0.004.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

This invention relates to a aluminium-scandium alloy standard spectrum sample and preparation method, <0}wherein, the sample comprises: Si 0.045~0.27%, Fe 0.07~0.37%, Cu 0~0.11%, Mn 0.13~1.2%, Mg 4.3~7.8%, Cr 0~0.27%, Ni 0~0.11%, Zn 0~0.17%, Sc 0.03~0.54%, Ti 0~0.18%, Zr 0.025~0.22%, Be 0.00005~0.0035% and B 0.0005~0.010%. The preparation relates to smelting, casting, homogenizing, lathing surface, and extruding. This invention meets practical demand, and provides foundation for production of 5A70 and 5A71 series Al-alloy.

Description

technical field [0001] The invention relates to an alloy standard sample and a preparation method thereof, in particular to an aluminum-scandium alloy spectral standard sample. Background technique [0002] The 5A70 and 5A71 series aluminum alloys are new alloys developed and registered by Southwest Aluminum (Group) Co., Ltd. in recent years, which belong to a series of aluminum scandium alloys (Al-Mg-Sc). After the alloy is alloyed with a trace amount of scandium (0.07%-0.35%), compared with similar alloys without scandium, the aluminum-scandium alloy has high strength, good plastic toughness, excellent corrosion resistance and welding performance, and is the next generation aluminum-lithium alloy. A new generation of lightweight structural materials for aerospace, aviation, and ships. 5A70 / 5A71 series aluminum alloys contain Mg, Mn, Zr, Ti, Sc, Zn, Ni, Cu, Fe, Si, B, Be, Cr13 elements. [0003] As we all know, the development of new alloys is inseparable from the analysi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N21/25G01N1/28
Inventor 朱学纯尹晓辉吴洪军陈瑜陈渝韦志宏胡永利彭速中彭斌钟玲
Owner SOUTHWEST ALUMINUM GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap