Ethylene-based polymers and processes to make the same

a technology applied in the field of ethylene-based polymers and processes to make the same, can solve the problems of reducing reducing the optics and toughness properties of high-melt strength resins, and polymerizing the balance of high-melt strength, so as to improve the maximum output of blown films and improve the effect of blown film quality

Active Publication Date: 2020-08-20
DOW GLOBAL TECH LLC
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

This patent describes a type of plastic made from ethylene-based polymers that have certain properties. The plastic has a specific ratio of two measurements, and it also has a specific value for a specific index. The technical effect of this composition is that it has specific physical properties that make it useful in various applications.

Problems solved by technology

Blown film production lines are typically limited in output by bubble stability.
High melt strength resins also typically have reduced optics and toughness properties.
However, such polymers do not provide an optimized balance of high melt strength, improved blown film maximum output, and excellent film properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ethylene-based polymers and processes to make the same
  • Ethylene-based polymers and processes to make the same
  • Ethylene-based polymers and processes to make the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007]Novel ethylene-based polymers, such as LDPEs, were developed with an optimized balance of high melt strength, improved blown film maximum output, and excellent film properties. The high melt strength allows an increase in the processability and output of the inventive polymers and blends containing the same.

[0008]As discussed above, the invention provides a composition comprising an ethylene-based polymer, which comprises the following properties:[0009]a) a Mw(abs) / Mw(conv)≥2.60; and[0010]b) a CDFIR (at MW ≤10,000 g / mole)≥0.145.

[0011]The composition may comprise a combination of two or more embodiments as described herein. The ethylene-based polymer may comprise a combination of two or more embodiments as described herein.

[0012]In one embodiment, the ethylene-based polymer has a CDFIR (at MW≤10,000 g / mole)≥0.140, or ≥0.142, or ≥0.145, or ≥0.148, or ≥0.150, or ≥0.153, or ≥0.155, or ≥0.160, or ≥0.165. In a further embodiment, the ethylene-based polymer is a LDPE. A LDPE is known...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Temperatureaaaaaaaaaa
Forceaaaaaaaaaa
Forceaaaaaaaaaa
Login to View More

Abstract

The invention provides a composition comprising an ethylene-based polymer, wherein the ethylene-based polymer comprises the following properties: a) a Mw(abs) / Mw(conv)>2.60; and b) a CDFRIR (at Mw<10,000 g / mole)>0.145.

Description

REFERENCE TO RELATED APPLICATIONS[0001]The present application claims the benefit of U.S. Provisional Application 62 / 298741, filed Feb. 23, 2016.BACKGROUND OF THE INVENTION[0002]Blown film production lines are typically limited in output by bubble stability. Blending Linear Low Density Polyethylene (LLDPE) with 0.5 wt %-90 wt % of Low Density Polyethylene (LDPE) increases bubble stability, in part due to the higher melt strength of the LDPE. The increase in melt strength, in part, provides for an increase in film output. High melt strength resins also typically have reduced optics and toughness properties. Thus, there is a need for new ethylene-based polymers, such as LDPEs, that have an optimized balance of melt strength and film properties, such as shrink, for blown film applications. LDPE polymers are disclosed in the following references: WO 2010 / 042390, WO 2010 / 144784, WO 2011 / 019563, WO 2012 / 082393, WO 2006 / 049783, WO 2009 / 114661, WO 2014 / 190039, WO 2014 / 190041, WO 2014 / 190036...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/06
CPCC08F2500/12C08L23/06C08F110/02C08L2207/066C08F10/02C08L23/04C08L2203/16C08L2205/025C08F2/00C08F2500/08
Inventor KARJALA, TERESA P.KARDOS, LORI L.BROWN, HAYLEY A.GILLESPIE, DAVID T.POLK, ZACHARY L.ORTEGA, JOSE
Owner DOW GLOBAL TECH LLC