Thick steel plate with great line energy and low welding crack sensitivity and its production process

A technology with low welding cracks and large input energy, which is applied in the field of welded structural steel and high-strength steel with high input energy and low welding crack sensitivity. It can solve the problems of low steel plate strength, achieve good performance, simple production process, and low welding Effect of Crack Sensitivity

Inactive Publication Date: 2008-06-25
ANGANG STEEL CO LTD
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The strength of this steel plate is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thick steel plate with great line energy and low welding crack sensitivity and its production process
  • Thick steel plate with great line energy and low welding crack sensitivity and its production process
  • Thick steel plate with great line energy and low welding crack sensitivity and its production process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0052] The chemical composition of the steel of the present invention is (by weight percentage), C: 0.6~0.10%, Si: 0.15~0.40%, Mn: 1.20~1.60%, P: ≤0.015%, S: ≤0.007%, Ni: 0.15~ 0.40%, Cr: ≤0.30%, Mo: 0.15-0.30%, V: 0.02-0.06%, and the balance is Fe and unavoidable impurities. In addition, the steel chemical composition of the present invention must also meet:

[0053] Pcm=C+Si / 30+Ni / 60+(Mn+Cr+Cu) / 20+Mo / 15+V / 10+5B≤0.20%;

[0054] In the specific implementation of the present invention, the content of the following elements is adjusted, C: 0.06% to 0.08%, Si: 0.15% to 0.30%, Mn: 1.40% to 1.55%, Ni: 0.20% to 0.30%, Mo: 0.20% to 0.30%, Als: 0.015% to 0.045%, Ti: 0.010% to 0.025%, Nb: 0.015% to 0.030%. The thickness of the finished steel plate produced is ≤20.0mm.

[0055] In the implementation of the present invention, the following element contents are adjusted, C: 0.08%~0.10%, Si: 0.15%~0.30%, Mn: 1.25%~1.45%, Ni: 0.25%~0.40%, Mo: 0.15%~ 0.25%, Als: 0.015% to 0.045%, Ti: 0.0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The present invention discloses one kind of thick steel plate with great line energy and low welding crack sensitivity and its production process. The chemical composition includes C 0.06-0.10 wt%, Si 0.15-0.40 wt%, Mn 1.20-1.60 wt%, P not more than 0.015 wt%, S not more than 0.007 wt%, Ni 0.15-0.40 wt%, Cr not more than 0.30 wt%, Mo 0.15-0.30 wt%, V 0.02-0.06 wt%, Al 0.015-0.045 wt%, Ti 0.010-0.034 wt%, except Fe and inevitable impurities; and meets Pcm not higher than 0.20 %. The production process includes pre-treatment of molten iron, smelting in converter, LF furnace plus VD furnace vacuum treatment, two stage controlled rolling, on-line laminar flow cooling, tempering at 600-680 deg.c and other steps. The produced steel plate has no need of quenching and tempering treatment.

Description

technical field [0001] The invention belongs to the field of low-alloy steel manufacturing, and relates to a steel for welding structure, in particular to a high-strength steel with a tensile strength of 610 MPa and low welding crack sensitivity with large input energy. Background technique [0002] Prior to the present invention, JP-A-49-37814 and JP-A-4-13406 have disclosed techniques for reducing the sensitivity of welding cracks, reducing C and adding Ti-B. Up to now, the high-strength steel plate with a tensile strength of 600MPa and low welding crack sensitivity basically adopts quenching and tempering production technology, almost all of which add B to ensure the hardenability of the steel, without considering the problem of large heat input welding. Using B to ensure the strength of the steel and increase the hardenability of the steel, the chemical composition and manufacturing conditions will change, which may lead to unstable properties of the base metal, especial...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/14C22C38/50C21D8/02B21B37/74
Inventor 张禄林郝森王丽慧徐烈山陈涛苏国阳高文涛信昕丛津功梁福鸿徐光刘曙光潘玲
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products