Non-halogen flame resistant base material and carpet for vehicle or airplane use

A base material, non-halogen technology, applied in the direction of vehicle exterior cleaning devices, etc., can solve the problem of reduced processing adaptability, and achieve the effect of good heat resistance and excellent stability over time

Inactive Publication Date: 2008-10-22
ETEC
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, in order to obtain sufficient flame retardancy, these non-halogen-based flame retardants must be added in large amounts relative to the polymers used in existing base materials. If the amount necessary to achieve flame retardancy is added, processing Decreased adaptability, causing problems in the stability of the base material over time, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-halogen flame resistant base material and carpet for vehicle or airplane use
  • Non-halogen flame resistant base material and carpet for vehicle or airplane use
  • Non-halogen flame resistant base material and carpet for vehicle or airplane use

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0100] Embodiment 1, comparative example 1

[0101] 150 parts by weight of aluminum hydroxide (Showa Denko Hijilite H21, average particle diameter 25 μm ), 3 parts by weight of foaming agent as other additives (surfactant, anionic), 1.0 parts by weight of dispersant (polyphosphate, sodium tripolyphosphate), 2 parts by weight of thickener [CMC (carboxymethyl fiber prime)], the base material was prepared by mixing in a stand mixer.

[0102] These base materials were foamed by a continuous mechanical foamer, and the amounts shown below were applied with a doctor blade on the inner surface of the nonwoven fabric shown below. After coating, it was dried at 160° C. for 10 minutes, and the resulting carpet was evaluated for flame retardancy test, heat resistance, processing suitability, and stability over time of the base material as described above. It should be noted that the solid content of the base material was adjusted to 50% by weight and the viscosity was adjusted to 5,000 ...

Embodiment 2

[0115] Embodiment 2, comparative example 2

[0116] In addition to using 100 parts by weight of latex A2 (Tg: 30° C.) in Example 1 as latex, and adding 100 parts by weight of flame retardants B1 to B4 and b1 to b2 shown below as flame retardants, the rest according to and Carpets were obtained in the same manner as in Example 1, and evaluated by flame retardancy tests. Furthermore, the stability and processing suitability of the base material were also evaluated. In addition, the solid content of the base material was adjusted to 50% by weight with the thickener and water, and the viscosity was adjusted to 5,000 mPa·s. (Measurement was performed with rotor No. 3).

[0117] The results are shown in Table 2.

[0118] The base materials of Examples 2-3 and 2-4 were poor in stability, but excellent in flame retardancy and processing suitability, thereby achieving the first object of the present invention.

[0119] Flame retardant B1: Aluminum hydroxide (the same as used in Exa...

Embodiment 3

[0129]In addition to using 100 parts by weight of latex A2 in Example 1 as latex, add 100 parts by weight of aluminum hydroxide used in Example 1, or add 100 parts by weight of ammonium polyphosphate B2-1 to B2-5 shown below (Average particle diameter: 25 μm) Except for the flame retardant, a carpet was obtained in the same manner as in Example 1, and the same evaluation as in Example 1 was performed. In addition, a water-soluble component means what disperse|distributes in water at 20 degreeC 2weight%. Both the solid content of the base material was adjusted to 50% by weight and the viscosity was adjusted to 5,000 mPa·s with the thickener and water. (Measurement was performed with rotor No. 3).

[0130] The results are shown in Table 3.

[0131] The ammonium polyphosphate used in Examples 3-1 to 3-3 has a water-soluble content of 0.2% by weight or less, is excellent in flame retardancy, processing suitability, and base material stability, and satisfies the first requirement...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a non-halogenic flame-retardant backing material having flame retardancy, although a halogenic flame retarder is not used therefor, excellent in processability and heat resistance, and further excellent in stability with the elapse of time. This non-halogenic flame-retardant backing material contains (A) an aqueous emulsion of a vinyl cyanide-acrylic copolymer in an amount of 100 pts.wt. (converted into a solid content) and (B) (B-1) at least one kind of non-halogenic phsphorous flame retarder selected from a group comprising polyphosphoric acid ammonium salts, a phosphoric acid ester, and water-soluble ammonium phosphate in an amount of 20-500 pts.wt. and / or (B-2) a non-halogenic metal hydrate in an amount of 20-500 pts.wt. [provided that, the components (B-1) and (B-2) are used in an amount of 20-500 pts.wt. in total, when the components are together used]. A carpet for a vehicle or an airplane is obtained by coating a back surface of the carpet with the backing material and drying the material.

Description

technical field [0001] The present invention relates to a non-halogen flame-retardant base material which does not generate halogen gas when burned, and carpets for vehicles (automobiles, railway vehicles) and airplanes using the base material. Background technique [0002] Currently, halogen-based flame-retardant base materials such as chlorine and bromine are used in fiber interior materials such as carpets of vehicles (automobiles and railway vehicles) and aircraft to comply with flame-retardant regulations. This base material corrodes the incinerator when waste is incinerated, and generates harmful dioxins when a fire occurs, which has the disadvantage of being environmentally unfavorable. [0003] On the other hand, as non-halogen flame retardants, non-halogen flame retardants such as ammonium polyphosphate, water-soluble ammonium phosphate and phosphoric acid ester, and non-halogen flame retardants such as aluminum hydroxide and magnesium hydroxide are known. Metalloi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L33/04C08K5/521C08K3/32B60S3/06
Inventor 宗秀二郎中井照雄林直树
Owner ETEC