Method for preparing conductive single-layer graphite sheet modified by ionic liquid cation group

A technology of single-layer graphite and ionic liquid, which is applied in the field of preparation of single-layer graphite flakes, can solve the problems of high molecular polymer miscibility, long time, environmental pollution, etc., and achieve good conductivity, fast reaction speed, and environmental friendliness Effect

Inactive Publication Date: 2010-02-03
NORTHEAST NORMAL UNIVERSITY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the only known way to prepare single-layer graphite flakes is the oxide of exfoliated carbon, but the single-layer graphite flakes made of oxides of exfoliated carbon are due to the presence of hydroxyl and epoxy compounds on the flakes. In addition, carbonyl and carboxyl groups appear on the edge of the sheet, so there are many defects: first, it is hydrophilic, not lipophilic, so it cannot be miscible with polymers; second, it is insulating, so it is in the preparation of conductive composites. There are also many limitations in the application
However, it takes a long time to add chemical modifiers and reducing agents, and Stankovich et al. use a large amount of methanol in the process of coagulating the composite material, thus causing environmental pollution and waste of time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing conductive single-layer graphite sheet modified by ionic liquid cation group
  • Method for preparing conductive single-layer graphite sheet modified by ionic liquid cation group
  • Method for preparing conductive single-layer graphite sheet modified by ionic liquid cation group

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Use 1-octyl-3-methylimidazolium hexafluorophosphate and water with a volume ratio of 1:1 as the electrolyte, graphite rods as electrodes, and a constant-voltage and stable-current power supply to provide 15 volts for 10 hours of electrolysis. After the reaction is complete, Wash the exfoliated single-layer graphite sheet with absolute ethanol, and dry it in a drying oven at 55°C for 6 hours to obtain a conductive single-layer graphite sheet modified with 1-octyl-3-methylimidazole Graphite flakes;

Embodiment 2

[0016] Use 1-octyl-3-methylimidazolium tetrafluoroborate and water with a volume ratio of 1:1 as the electrolyte, graphite rods as electrodes, and a constant voltage and constant current power supply to provide 15 volts, electrolysis for 8 hours, and the reaction is complete Finally, the exfoliated single-layer graphite flakes obtained were washed with absolute ethanol, and dried in a drying oven at 55° C. for 6 hours to obtain a single-layer graphite sheet with conductivity modified by 1-octyl-3-methylimidazole. layers of graphite flakes;

Embodiment 3

[0018] Use 1-octyl-3-methylimidazole chloride and water with a volume ratio of 1:5 as the electrolyte, graphite rods as electrodes, and a constant voltage and current power supply to provide 10 volts for 6 hours of electrolysis. After the reaction is complete, you will get The exfoliated single-layer graphite flakes were washed with absolute ethanol and dried in a drying oven at 55°C for 6 hours to obtain conductive single-layer graphite flakes modified with 1-octyl-3-methylimidazole ;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a process for preparing a single layer graphite flake with electrical conductivity and modification of ionic liquid cationic groups. Ionic liquid and water are used as electrolytic solution, a graphite rod is used as electrodes, cationic organic groups of the ionic liquid in reaction can be connected to graphite flakes and cause exfoliation of the graphite, obtained single layer graphite flakes have organic groups and are not oxygenized, thereby having good oil solubility to be mutually-soluble with the high molecular polymer, good electrical conductivity and the singlelayer graphite flakes can be used for preparing conductive composite materials with good performance.

Description

technical field [0001] The invention relates to a preparation method of a self-conducting single-layer graphite sheet modified with an ionic liquid cationic group, which does not require reduction. Background technique [0002] Carbon-based composite materials are being widely concerned by scientists due to their light weight, high strength, and good electronic conductivity. For example, they can be used in aerospace and military fields. (Kotov, A.N.Carbon sheet solutions. Nature 442, 254-255(2006).) At present, carbon-based composites are mostly filled with single-walled carbon nanotubes, but single-walled carbon nanotubes are easy to agglomerate; Carbon nanotubes formed by sheet curling are difficult to control in diameter and expensive. (Price, B.K., Hudson, J.L., Tour, J.M.Green Chemical Functionalization of Single-Walled Carbon Nanotubes in Ionic Liquids.J.Am.Chem.Soc.127, 14867-14870(2005).) For the above reasons, scientists have Turned his attention to single-layer ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B31/04
Inventor 罗芳刘娜
Owner NORTHEAST NORMAL UNIVERSITY