Multimodal polyethylene composition obtainable with high activity catalyst

A composition and polyethylene technology, applied in the production of bulk chemicals, etc., can solve problems such as adverse effects of polymer properties and ideal reactions, and achieve the effects of improved appearance, beneficial purity, and improved impact strength

Active Publication Date: 2007-10-17
ボレアリステクノロジーオイ
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the addition of small amounts of comonomer may not drive the desired level of reaction and / or adversely affect the properties of the polymer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0168] 1. Definitions and Measurement Methods

[0169] a) molecular weight

[0170] Weight average molecular weight M w and molecular weight distribution (MWD=M w / M n , where M n is the number average molecular weight, and M w is the weight average molecular weight) was measured by a method based on ISO 16014-4:2003. A Waters 150CV plus instrument was used with a column 3 x HT&E styragel (divinylbenzene) from Waters and trichlorobenzene (TCB) as solvent at 140°C. Use the common narrow MWD PS standard (for PS, the Mark-Howwink constant K: 9.54*10 -5 and a: 0.725; and for PE, K: 3.92*10 -4 and a: 0.725) to calibrate the column setting. m w with M n The ratio of is a measure of the width of the distribution, since each is affected by opposite ends of the "population".

[0171] b) Density

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The present invention concerns a multimodal, preferably bimodal, polyethylene (PE) composition comprising a base resin which comprises (A) a first ethylene homo- or copolymer fraction, and (B) a second ethylene homo- or copolymer fraction, wherein (i) fraction (A) has a lower weight average molecular weight than fraction (B), (ii) the base resin has an MFR 5 of at least 0.01 g / 10 min and (iii) the base resin is obtainable by polymerising ethylene and optionally at least one comonomer in the presence of a catalyst having an overall activity of at least 30 kg polymer per g catalyst. Furthermore, the present invention relates to a process for the production of such a composition as well as to the use of such a composition for the production of articles.

Description

technical field [0001] The present invention relates to a multimodal, preferably bimodal polyethylene (PE) composition comprising two ethylene homopolymer or copolymer fractions with different molecular weights. Furthermore, the invention relates to a process for the preparation of such a composition and the use of this composition for the preparation of articles. Background technique [0002] In general, it is difficult to obtain a multimodal PE composition comprising at least one low molecular weight (LMW) fraction and one high molecular weight (HMW) fraction with a sufficient degree of homogeneity. However, in many end-use applications, the uniformity of the final composition is a key factor, for example, including injection molded articles (such as packaging articles, such as shipping packaging, houseware applications and caps / seals) and blow molded articles, In molded articles of pipes and films. [0003] Furthermore, in some applications, residues of polymerization c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08F10/02C08L23/04
CPCC08L23/04C08F110/02C08F210/16C08L23/06C08L23/0815C08L2205/02C08L2205/025C08L2308/00C08L2314/02Y02P20/52
Inventor 埃里克・范普雷特雷姆克・范玛丽昂比尔・古斯塔夫松西夫・弗雷德里克松马茨・贝克曼
Owner ボレアリステクノロジーオイ
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com