Burned drill processing technique

A processing technology and process technology, applied in the field of crystal jewelry processing technology, can solve the problems of high cost, unenvironmental protection, many processes, etc., and achieve the effect of high processing efficiency

Inactive Publication Date: 2008-03-05
盖虎英
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of its technology are: 1. There are many processes and high cost; 2. Asphalt is used in the process, which is not environmentally friendly; 3. The efficiency is low. Taking No. 10 as an example, generally only 20 kg can be processed a day

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Burned drill processing technique

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Embodiment 1: The processing technology of this hot drilling mainly includes the following steps:

[0014] (1.1) Put the hot drill 1 into the small drum 2, the loading amount is more than 85% of the volume of the small drum, so that the small drum 2 revolves along the big drum 3 in addition to its rotation, and rotates for 10-30 minutes at a speed of 20 -40 rpm; the rotation direction of the small drum 2 and the large drum 3 are opposite. The small drum 3 and the large drum 3 are driven by a motor driven by a deceleration device, as shown in Figure 2.

[0015] (1.2). Take out the hot drill from the small drum, mix the hot drill and emery and vibrate the treatment. The hot drill and emery are mixed in a volume ratio of 1-100:1-10. The specific volume ratio is based on the size of the hot drill and the size of the burr It depends, the larger the hot diamond, the larger the burrs, the larger the ratio of emery, generally 4:1.

[0016] (1.3) Separate the hot diamond from the em...

Embodiment 2

[0018] Example 2: For hot drills with large burrs, mix the hot drills and polishing stones at a volume ratio of 1-100:1-10 and then put them into a small drum (the specific volume ratio is determined by the size of the hot drill and the size of the burrs , Generally 1:1), after processing according to step (1.1), separate the hot drill from the polishing stone, and then proceed to the subsequent steps (1.2) and (1.3).

Embodiment 3

[0019] Example 3: For hot drills that need to be processed for recess 1-2, the hot drills and emery are mixed in a volume ratio of 1-100:1-10 and then loaded into a small drum (generally 4:1), and added with After the water with the same volume of the mixture is processed according to step (1.1), the hot diamond is separated from the emery, and then the subsequent steps (1.2) and (1.3) are carried out.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to crystal ornament processing technique, and is especially hotfix rhinestone treating process. The hotfix rhinestone treating process includes the following steps: 1. loading hotfix rhinestones into small drum to fill 85 % of its volume, and rotating the small drum and revolving the small drum around one large drum simultaneously for 10-30 min; 2. taking out the hotfix rhinestones, mixing with emery and vibrating the mixture; and 3. separating the hotfix rhinestones from emery and washing. The hotfix rhinestone treating process can eliminate burrs of hotfix rhinestones with less damage to the edges, and is environment friendly and high in treating efficiency.

Description

Technical field [0001] The invention relates to a processing technology of crystal ornaments, and is mainly a processing technology of hot drilling. Background technique [0002] The original hot drill has many burrs after coming out of the mold. The burr treatment process steps are as follows: 1. Bead processing, which is to screen the front and back of the hot drill into one surface; 2. Perform asphalt printing; 3. Perform Coarse and fine grinding treatment; 4. Use hot water to scald the hot drill; 5. Clean the hot drill. The disadvantages of the process are: 1. There are many processes and the cost is high; 2. Asphalt is used in the process, which is not environmentally friendly; 3. The efficiency is low. Taking No. 10 as an example, it can only process 20 kg a day. Summary of the invention [0003] The present invention aims to solve the above-mentioned existing shortcomings and provide a hot drilling process. [0004] The technical solution adopted by the present invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B24B31/02
Inventor 盖虎英
Owner 盖虎英
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com