Method for making thin type elastic PU synthetic leather
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A production method and synthetic leather technology, applied in textiles and papermaking, etc., can solve the problems of narrowing the width of the door, difficulty in guaranteeing product quality, inability to produce high-quality thin synthetic leather products, etc., and achieve the effect of improving processing performance
Active Publication Date: 2008-05-14
ZHEJIANG HEXIN NEW MATERIAL CO LTD +1
View PDF0 Cites 7 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
This kind of thin and elastic base fabric will become narrow and difficult to control after wet processing and drying, and curling and shrinkage will also occur, making it difficult to guarantee product quality
In order to reduce the phenomenon of narrowing, curling and shrinkage of the door width during processing due to the influence of tensi
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0011] Base fabric: thin warp-knitted polyester fleece, thickness 0.35mm;
[0030] Wet peel strength of composite cloth: 0.10kg / 3cm;
[0031] Dry peel strength of composite cloth: 0.48kg / 3cm;
[0032] The thickness of the synthetic leather obtained: 0.52mm;
[0033] Other qualities of the prepared synthetic leather: qualified, low wet peeling, easy to peel.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
Thickness
aaaaa
aaaaa
Thickness
aaaaa
aaaaa
Thickness
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to a manufacturing method of thin elastic PU synthesized leather. One side of a thin elastic base cloth is attached with a layer of machine woven cloth, and the other side of the base cloth is compounded with a PU layer via wet processing of synthesized leather, then the base cloth is dried and molded, and the machine woven cloth is peeled during a coiling process; wherein, the base cloth and the machine woven cloth are fuzzed in a single surface, the fuzzed surface of the machine woven cloth is attached to the non-fuzzed surface of the base cloth by low concentration hydrophilic adhesive, and the PU layer is compounded to the fuzzed surface of the base cloth. The invention adopts the method of compounding a machine woven cloth to the rear surface of the base cloth, leads the machine woven cloth to bear the tension during the conveying process so as to prevent the thin elastic base cloth from distorting during the conveying process, thus enhancing the fabricating performance of the base cloth; the woven cloth is peeled during the coiling process, so high quality product can be obtained. The adhesive for the fuzzed surface of the machine woven cloth is attached to the non-fuzzed surface of the base cloth, and the dried adhesive is adhered and remained on the fuzzed surface of the machine woven cloth during the peeling process, which does not influence the performance of the PU synthesized leather.
Description
technical field [0001] The invention relates to a method for manufacturing thin and elastic PU synthetic leather, a method for manufacturing thin elastic leather made of elastic cloth such as thin warp knitting and knitting as a base cloth, and belongs to the field of synthetic leather production technology. Background technique [0002] PU (polyurethane) synthetic leather is made by coating polyurethane resin on the base fabric. Among them, PU synthetic leather (used for golf gloves, hemmed shoe leather, clothing leather, etc.) etc.), the thickness of the base cloth is less than 0.3mm, and the tanning process usually adopts the traditional wet process. In the wet process, the base fabric needs to have a certain tension along the conveying direction during the conveying process of unwinding, scraping, solidification, washing and drying. This type of thin, elastic base fabric will become narrow and difficult to control after wet processing and drying, and curling and shrinka...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more