A super wear-resistant technology for soles, applied in soles, applications, footwear, etc., to solve problems such as sole wear, loss of elasticity, slippage, etc.

Active Publication Date: 2008-05-28
ANTA CHINA
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Due to its special purpose, sports shoes require that the rubber used for the sole should be wear-resistant, wet-slip resistant, and also have good impact resistance. However, in the current rubber techn

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The formula of super wear-resistant rubber for sports shoe soles and the optimal weight combination in a batch of materials are shown in Table 1:

[0016] Raw material name

parts by mass

Weight (kg)

polybutadiene rubber

80

30.5

Natural rubber STR-5L

20

7.5

uniform tackifying resin

1

0.4

Silica

45-48

18

softening oil

3.5

1.3

coupling agent

3-3.2

1.2

active agent DEG

1.4-1.6

0.5

active agent PEG

2.4-2.6

1

active agent ZNO

1.4-1.6

0.6

Zinc stearate

1

0.4

Anti-fog agent

1

0.4

sulfur

1.9-2.1

0.74

accelerator DM

1.2-1.5

0.5

Accelerator M

0.3

0.12

Accelerator TS

0.15

0.06

[0017] After implementing above-mentioned formula, the detection result of rubber for sports shoes is a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a superwear-resisting rubber formulation of sport sole, and is characterized in that the formulation according to parts by weight comprises 80 parts of polybutadiene rubber, 20 parts of natural gum STR-5L, 1 part of uniform tackiness resin, 45-48 parts of white carbon black, 3.5 parts of softening oil, 3-3.2 parts of coupler, 5.2-5.8 parts of activator, 1 part of zinc stearate, 1 part of antifog agent, 1.9-2.1 parts of sulphur, and 1.65-1.95 part of accelerating agent, an ideal raw material functional combination can be obtained after applying the rubber formulation for sports shoes, which makes the sport shoe rubber sole having superwear resistance which is superior to ordinary rubber sole, and has a plurality of excellent properties such as wet-skid resistance, impact resistance and the like.

Description

technical field [0001] The invention relates to a rubber formula, in particular to a rubber formula for sports shoe soles. Background technique [0002] Due to its special purpose, sports shoes require that the rubber used for the sole should be wear-resistant, wet-slip resistant, and also have good impact resistance. However, in the current rubber technology for sports shoes, due to the irrationality of the formula, many Disadvantages: In the process of repeated bouncing and running, the soles of sports shoes wear out quickly, lose their elasticity, and slip. Contents of the invention [0003] In view of the above shortcomings, the present invention provides a super wear-resistant rubber formula for sports shoe soles with excellent wear resistance, wet skid resistance and good impact resistance. [0004] To achieve the above object, the technical solution of the present invention is: [0005] The formula of super wear-resistant rubber for sports shoe soles is characteri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L7/00C08K5/09A43B13/04C08K3/06
Inventor 丁世忠
Owner ANTA CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap