Plasticizing enhancement nylon 6 composite material with good apparent mass and preparation method thereof

A technology of appearance quality and composite materials, applied in the field of toughened and reinforced nylon 6 composite materials and its preparation, can solve the problems of loss of mechanical properties and thermal properties of materials, achieve changes in flow characteristics, solve parts warping, appearance good performance

Active Publication Date: 2011-07-06
CHONGQNG PRET NEW MATERIAL +2
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

They either put forward many special requirements for the raw materials for the preparation of these inorganic mineral reinforced nylon 6 composites, or they sacrifice the excellent mechanical and thermal properties of certain glass fiber reinforced materials as a price, although the corresponding good performance of the parts can be obtained from them. The apparent quality, but the mechanical properties and thermal properties of the material will inevitably suffer a large loss

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plasticizing enhancement nylon 6 composite material with good apparent mass and preparation method thereof
  • Plasticizing enhancement nylon 6 composite material with good apparent mass and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The weight ratio of PA6 resin is 57.3%, the weight ratio of MAPP is 2%, the weight ratio of toughened masterbatch A is 20%, the weight ratio of KH550 is 0.4%, and the weight ratio of 1010 / 168 is 0.1 / 0.2%. The above components are mixed at room temperature (the glass fiber with a weight ratio of 20% is added from the first exhaust port), and the TE-35 (L / D=48) twin-screw extruder produced by Nanjing Keya Company is used to produce , the processing temperatures (from the feed port to the die) are: 170 ° C, 200 ° C, 215 ° C, 220 ° C, 230 ° C, the host speed is 30 Hz, the test results are listed in Table 1.

Embodiment 2

[0044] The weight ratio of PA6 resin is 51.3%, the weight ratio of MAPP is 8%, the weight ratio of toughened masterbatch A is 20%, the weight ratio of KH550 is 0.4%, and the weight ratio of 1010 / 168 is 0.1 / 0.2%. The above components are mixed at room temperature (the glass fiber with a weight ratio of 20% is added from the first exhaust port), and the TE-35 (L / D=48) twin-screw extruder produced by Nanjing Keya Company is used to produce , the processing temperatures (from the feed port to the die) are: 170 ° C, 200 ° C, 215 ° C, 220 ° C, 230 ° C, the host speed is 30 Hz, the test results are listed in Table 1.

Embodiment 3

[0046] The weight ratio of PA6 resin is 59.3%, the weight ratio of MAPP is 5%, the weight ratio of toughened masterbatch A is 15%, the weight ratio of KH550 is 0.4%, and the weight ratio of 1010 / 168 is 0.1 / 0.2%. The above components are mixed at room temperature (the glass fiber with a weight ratio of 20% is added from the first exhaust port), and the TE-35 (L / D=48) twin-screw extruder produced by Nanjing Keya Company is used to produce , the processing temperatures (from the feed port to the die) are: 170 ° C, 200 ° C, 215 ° C, 220 ° C, 230 ° C, the host speed is 30 Hz, the test results are listed in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a nylon 6 composite material for appearance quality toughening and reinforcing and a preparation method thereof. The nylon 6 composite material comprises by weight percentage 20-75 percent of nylon 6 resin, 1-10 percent of compatilizer, 10-40 percent of glass fiber, 10-40 of toughening masterbatch and 0.5-3 percent of other additives. The specific steps are that: every material is weighed except the glass fiber and mixed in a mixer for 3-5 minutes; the well-mixed material is put in a twin-screw extruder, wherein, the glass fiber is added in a first exhaust port, and the temperature from a feeding port to an extrusion die head is respectively 160-180 DGE C, 190-220 DGE C, 210-240 DGE C, 220-250 DGE C, 210-240 DGE C; the rotating speed of a host is 20-50 Hz, and thena sample is prepared by an injection moulding machine. The nylon 6 composite is characterized by no exposure of glass fiber and warping, good heat resistance and easy processing.

Description

technical field [0001] The invention belongs to the field of polymer composite materials, and in particular relates to a toughened and reinforced nylon 6 composite material with good apparent quality and a preparation method thereof. Background technique [0002] Generally speaking, nylon 6 has excellent mechanical properties, thermal properties, impact resistance and chemical resistance, so it is widely used in automobile parts, electronic and electrical parts, household goods parts and other fields. Among them, inorganic mineral-reinforced nylon 6, especially glass fiber-reinforced nylon 6, is widely used in automobiles, machinery, home appliances, Aviation and military components and other fields. However, in the actual application process, some materials need better toughness and appearance quality, and at the same time, there are more cost-effective and more convenient products in terms of price and processing. Simply adding glass fibers to nylon 6 can greatly improve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L77/02C08K7/14B29C70/52B29C70/54B29C47/92C08K3/00B29C48/40B29C48/92
CPCB29C48/92B29C2948/92704B29C48/04B29C48/40B29C48/9185B29C2948/9259B29C2948/92885B29C2948/92895B29C2948/92904
Inventor 刘正军张祥福周文
Owner CHONGQNG PRET NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap